Production method of vermiculite flame retardant medium density fiberboard

A production method and fiberboard technology, applied in the field of wood-based panel manufacturing, can solve problems affecting the physical and mechanical properties of slabs, achieve the effects of delaying fire time, saving costs, and solving environmental problems

Inactive Publication Date: 2011-11-30
NANJING FORESTRY UNIV
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese Patent No. ZL200720042049.9 once disclosed a practical technology of "cotton stalk flame-retardant medium density fiberboard". The main raw materials of the composite board are three-layer structure made of foamed vermiculite, adhesive, and cotton stalk fiber according to a certain formula. Flame-retardant medium-density fiberboard (surface foamed vermiculite, core layer of cotton stalk fiber), the flame-retardant medium-density fiberboard made according to this formula, its main disadvantage is that the foamed vermiculite is not glued but directly paved, vermiculite The addition of stone will affect the physical and mechanical properties of the slab

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of vermiculite flame retardant medium density fiberboard
  • Production method of vermiculite flame retardant medium density fiberboard

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 1. Select raw materials, vermiculite, wood fiber, and urea-formaldehyde resin as adhesives, among which the vermiculite is crushed and sieved through 60 mesh, the moisture content of wood fiber is less than 8%, and the preset density of the slab is 0.75g / cm 3 ;

[0019] Second, the surface layer, the bottom layer,

[0020] 1) The amount of vermiculite added is 30% of the dry fiber weight; the sizing amount of urea-formaldehyde resin to vermiculite is 6% of the dry fiber weight, and the curing agent NH is added to the urea-formaldehyde resin 4 Cl, curing agent NH 4 Cl amount is 1% of urea-formaldehyde resin weight;

[0021] 2) Combine urea-formaldehyde resin with curing agent NH 4 Cl mixed and stirred, mixed and stirred evenly, mixed with vermiculite and stirred evenly;

[0022] 3) Mix urea-formaldehyde resin, curing agent NH 4 The mixed material of Cl and vermiculite is divided into two parts, which are respectively used as surface layer and bottom layer material; ...

Embodiment 2

[0028] 1. Select raw materials, vermiculite, wood fiber, and urea-formaldehyde resin as adhesives, among which the vermiculite is crushed and sieved through 60 mesh, the moisture content of wood fiber is less than 8%, and the preset density of the slab is 0.85g / cm 3

[0029] Second, the surface layer, the bottom layer,

[0030] 1) The amount of vermiculite added is 70% of the dry fiber weight; the sizing amount of urea-formaldehyde resin to vermiculite is 9% of the dry fiber weight, and the curing agent NH is added to the urea-formaldehyde resin 4 Cl, curing agent NH 4 Cl amount is 1% of urea-formaldehyde resin weight;

[0031] 2) Combine urea-formaldehyde resin with curing agent NH 4 Cl mixed and stirred, mixed and stirred evenly, mixed with vermiculite and stirred evenly;

[0032] 3) Mix urea-formaldehyde resin, curing agent NH 4 The mixed material of Cl and vermiculite is divided into two parts, which are respectively used as surface layer and bottom layer material;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The present invention is a production method of vermiculite flame retardant medium density fiberboard, which includes selection of raw materials, preparation of surface layer, bottom layer and core layer, paving, pre-pressing, hot pressing, cooling, stacking, edge cutting, physical mechanics and combustion performance tests, etc. process steps. Advantages: due to the separate sizing of the surface layer, bottom layer and core layer materials, the amount of vermiculite added is based on the percentage of absolute dry fiber weight, the mechanical properties of the medium density fiberboard made by the present invention are better than the existing flame retardant and wood fiber Mechanical properties of medium density fiberboard made with mixed sizing. The results of the combustion performance test show that due to the addition of vermiculite accounting for 30-70% of the dry fiber weight in wood fibers, the heat release rate, total heat release, total smoke release, smoke yield and Mass loss rate, delayed ignition time. Tests have proved that with the increase of the amount of vermiculite added, the flame retardant performance of the product will increase. This product solves the problems of flammability and environmental protection, has low cost, and has both practical significance and promotion value.

Description

technical field [0001] The invention relates to a production method of a vermiculite flame-retardant medium-density fiberboard using inorganic vermiculite as a flame retardant, and belongs to the technical field of wood-based panel production. Background technique [0002] Medium-density fiberboard is a high-grade wood-based panel, which is widely used in furniture manufacturing, interior decoration, vehicle and ship manufacturing, and audio and musical instrument manufacturing. At present, the most commonly used inorganic flame retardants for flame-retardant wood-based panels are compounds containing P, N, B, Al and halogens, etc., which can be roughly divided into phosphorus-nitrogen series based on ammonium phosphate, and boron series mainly based on borides. , Halogen-containing halogen compounds and metal oxides or hydroxides containing Mg, Al, etc. The flame retardant treatment of medium density fiberboard is generally divided into two types: finished board treatment ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/06
Inventor 黄润州石晶李慧媛卫佩行周定国
Owner NANJING FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com