Wax removing water for cleaning wax scale on surface of polished workpiece and preparation method thereof

A technology for removing wax on the surface of workpieces, applied in the field of cleaning and preparing wax removing water, and can solve problems such as foaming, peeling, and unsatisfactory wax removal effects

Inactive Publication Date: 2011-10-12
HUBEI DE MEI TECH
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Various alloy materials (copper alloy, aluminum alloy, zinc alloy) and iron and steel materials will be mechanically polished after processing, and solid particles such as polishing paste will remain on the polishing surface. Adverse effects such as blistering and peeling
However, the current organic solvent dissolution or degreasing liquid technology is difficult to remove, and there are defects such as slow wax removal speed and unsatisfactory wax removal effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wax removing water for cleaning wax scale on surface of polished workpiece and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0009] Example 1: 1. Use a container to heat 350L of pure water to 60-70°C and add it to the stirring tank. 2. Turn on the stirring tank at a rotating speed of 60r / min, respectively mix 0.5 kg of linear alkylbenzene sulfonate sodium, 5 kg of secondary alkyl sulfonate, 5 kg of alkanolamide, 30 kg of fatty alcohol polyoxyethylene ether sulfate, and trimerize Add 100kg of sodium phosphate and 10kg of EDTA into the stirring tank and stir to dissolve. 3. Add pure water to the required volume of 1000L and stir well.

[0010] Each component and preparation method of example 2 to example 5 are as follows:

[0011]

[0012] The appearance of the dewaxing water provided by the invention is milky white liquid. When using the wax removal water to clean and polish the wax scale on the surface of the workpiece, ultrasonic method or immersion method can be used, specifically:

[0013] Ultrasonic method: Prepare wax removal water as an aqueous solution of 3-4% by weight, heat to 60-80°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses wax removing water for cleaning wax scale on the surface of a polished workpiece and a preparation method thereof. The wax removing water comprises the following components: 3 to 5 g / L of linear alkylbenzene sodium sulfonate, 5 to 10 g / L of secondary alkyl sulfate, 5 to 10 g / L of alkanolamide, 30 to 40 g / L of fatty alcohol polyoxyethylene ether sulfate, 100 to 150 g / L of sodium tripolyphosphate, and 3 to 5 g / L of ethylene diamine tetraacetic acid (EDTA). The wax removing water has good emulsifying effect and very strong solubilizing and dispersion effects, and can thoroughly clean the wax scale on the surface of the polished workpiece.

Description

technical field [0001] The invention relates to a cleaning and wax-removing water used for removing wax scales produced on various alloy parts and steel parts after mechanical processing and mechanical polishing, and a preparation method thereof. Background technique [0002] Various alloy materials (copper alloy, aluminum alloy, zinc alloy) and iron and steel materials will be mechanically polished after processing, and solid particles such as polishing paste will remain on the polishing surface. Adverse effects such as blistering and peeling. However, the organic solvent dissolution or degreasing liquid technology currently used is difficult to remove, and there are defects such as slow wax removal speed and unsatisfactory wax removal effect. Contents of the invention [0003] In order to solve the above problems, the present invention provides a kind of wax removal water, which can completely remove the wax scale on the surface of the workpiece through alkaline degreas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G5/06
Inventor 瞿德勤
Owner HUBEI DE MEI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com