High-resistance electrothermal alloy material and preparation method thereof

An electrothermal alloy and high resistance technology, which is applied in the field of high resistivity electrothermal alloy materials, electrothermal alloy materials, and Cr20Ni80Y materials, can solve the problem that the mechanical performance requirements of industrial electric heating elements cannot be met, and the service life can only reach 2000 hours, which affects the use of finished products Life and other issues, to achieve the effect of reasonable component design, small thermal expansion coefficient, and ensure safety and reliability

Active Publication Date: 2012-11-21
JIANGSU XINHUA ALLOY ELECTRIC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the widely used nickel-chromium alloy Cr20Ni80 has the advantages of high melting point, small thermal expansion coefficient and good oxidation resistance, it still has the disadvantages of poor high-temperature strength and short service life. 0 C, its anti-oxidation performance is significantly reduced, and its service life can only reach 2000 hours
In addition, in the process of producing Cr20Ni80, due to the unreasonable design of the preparation process, sometimes the ingot breaks and cracks during the forging process, which seriously affects the service life of the finished product and is far from meeting the mechanical properties of industrial heating elements. Require

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-resistance electrothermal alloy material and preparation method thereof
  • High-resistance electrothermal alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0052] The present invention is further described and understood by non-limiting examples below.

[0053] Five sets of examples have been prepared for the high-resistance electrothermal alloy material of the present invention, and the furnace numbers are: 105-2768, 2769, 2770, 2771, and 2772. Embodiment 1-5 groups of high-resistance electrothermal alloy materials, calculated by weight percentage, contain the following components:

[0054] The first group: furnace number: 105-2768, C: 0.025%; Si: 1.35%; Mn: 0.30%; P: 0.005%; S: 0.003%; Cr: 22.5%; Al: 0.22%; Fe: 0.25% ; Y: 0.6%; Ni: 73.5%; Miscellaneous rare earths: 0.25%.

[0055] The second group: furnace number: 105-2769, C: 0.05%; Si: 1.4%; Mn: 0.20%; P: 0.008%; S: 0.006%; Cr: 21.0%; Al: 0.3%; Fe: 0.36% ; Y: 0.5%; Ni: 75.5%;

[0056] Miscellaneous rare earths: 0.20%.

[0057] The third group: furnace number: 105-2770, C: 0.04%; Si: 1.25%; Mn: 0.15%; P: 0.008%; S: 0.006%; Cr: 21.5%; Al: 0.25%; Fe: 0.45% ; Y: 0.45%; Ni: 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-resistance electrothermal alloy material, which comprises the following components in percentage by weight: 0.02 to 0.08 percent of C, 0.75 to 1.6 percent of Si, 0.1 to 0.5 percent of Mn, less than or equal to 0.02 percent of P, less than or equal to 0.015 percent of S, 20 to 23 percent of Cr, 0.1 to 0.5 percent of Al, 0.2 to 0.8 percent of Y, 0.2 to 1.0 percent of Fe, and the balance of Ni and inevitable impurities. The preparation method for the high-resistance electrothermal alloy material comprises the following steps of: smelting; forging; coiling; annealing; rinsing; mold drawing, and the like. Compared with Cr20Ni80, the high-resistance electrothermal alloy material has higher antioxidation performance, and is an electrothermal alloy material with small thermal expansion coefficient, high high-temperature strength and processability, long service life and high resistivity.

Description

technical field [0001] The invention relates to a high-resistivity electrothermal alloy material in the technical field of metal materials, in particular to a [0002] High-resistance electrothermal alloy material and its preparation method. It specifically relates to a Cr20Ni80Y material, which is mainly used as an electrothermal alloy material for household appliances, industrial electric furnaces and heating elements. Background technique [0003] Electrothermal alloy is a functional material that converts electrical energy into heat energy. Its maximum service temperature can reach 1400 ° C. It is used to manufacture various electric heating elements in the fields of metallurgy, machinery, petrochemical, electrical, construction, military industry, and household appliances. At present, electrothermal alloy materials have become an important engineering alloy material and occupy an important position in the national economy. With the development of the household applian...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/05C22C1/02C22F1/10C21D1/26C22B9/04C22B9/18
Inventor 华大凤王树平
Owner JIANGSU XINHUA ALLOY ELECTRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com