High-precision aluminum alloy rectangular tube forming method

A technology of aluminum alloy and rectangular tube, applied in the direction of wire drawing die, etc., can solve the problems of tube billet breaking and corner transverse cracks, etc., and achieve the effect of eliminating transverse cracks, dense structure and good surface quality.

Inactive Publication Date: 2013-04-03
CHONGQING UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the deficiencies of the above-mentioned prior art, and provide a forming method of aluminum alloy rectangular pipe, which can effectively improve the dimensional accuracy and surface quality of the finished pipe, improve the service performance and life of the product, and solve the During the process, the tube billet is broken, and there are obvious transverse cracks at the corners

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-precision aluminum alloy rectangular tube forming method
  • High-precision aluminum alloy rectangular tube forming method
  • High-precision aluminum alloy rectangular tube forming method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0034] In this embodiment, taking an aluminum alloy tube with a ratio of height H to width B of 1:2.0, a dimension of 90.12mm×45.16mm×2.06mm, and an inner surface roughness of Ra1.0 as an example, a method for manufacturing this type of rectangular tube is proposed. The forming process method, the specific implementation steps are as follows:

[0035] a) Equally heat the prepared aluminum alloy ingot of brand 6061 to 415±5°C for 1-2h. The purpose of the ingot homogenization treatment is to eliminate the residual stress formed inside the metal ingot, improve the plastic processing ability of the metal ingot, improve the structure and mechanical properties of the product, and prepare for the subsequent further processing. In actual production, most aluminum alloy ingots must be subjected to a necessary heat treatment before pressure processing.

[0036] b) First, preheat the extrusion splitter mold to 400°C, then put the aluminum alloy ingot with a heating temperature of 450°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-precision aluminum alloy rectangular tube forming method which comprises the following steps: a) heating the prepared No.6061 aluminum alloy ingot over uniform fire to 415+ / -5 DEG C, and keeping for 1-2 hours; b) performing hot extrusion on an extrusion shunting mould with a preheating temperature of 400 DEG C to obtain an initial tube blank; c) performing annealingtreatment in salt bath; d) performing cold rolling on the tube blank obtained in the step c) to obtain a round tube; e) soaking the round tube obtained in the step d) in a 38# cylinder oil for 24 hours; f) performing non-mandrel drawing on the tube blank obtained in the step e) to obtain an approximately rectangular tube; g) performing mandrel drawing on the approximately rectangular tube obtained in the step f) through a rectangular correction mould to obtain a rectangular tube; and h) performing mandrel drawing of the rectangular tube obtained in the step g) to obtain the finished tube. Through the invention, the size precision and surface quality of the finished tube are improved, the problems that the tube blank is drawn apart in the drawing process and obvious transverse cracks appear at the corner are solved, and the operational performance and service life of the product are remarkably improved.

Description

technical field [0001] The invention belongs to the technical field of metal material processing, and in particular relates to a forming method of a high-precision aluminum alloy rectangular tube. Background technique [0002] As an important component of radio microwave communication and navigation equipment, the high-precision aluminum alloy rectangular tube is widely used in important scientific and technological fields such as aviation, aerospace, radar, telemetry and long-distance communication. Due to the particularity of the work and use environment, stricter requirements are imposed on the dimensional accuracy and inner surface quality of this type of rectangular tube. At present, in actual production, the preparation of this type of pipe mainly adopts the drawing forming scheme of initial circular tube billet-transitional ellipse-finished rectangle. However, due to the unreasonable deformation of the tube blank material, the consistency and uniformity of the flow o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C37/15B21C3/02
Inventor 徐戊矫王凯庆周杰王鹏程杨小兵朱若岭
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com