Fire-retardant insulating polyvinyl chloride material and electrical sleeve

A polyvinyl chloride, flame retardant masterbatch technology, applied in insulators, electrical components and other directions, to meet the needs of insulation and flame retardant, excellent flame retardant performance and insulation performance

Inactive Publication Date: 2011-06-15
KANGTAI PLASTIC SCI & TECH GRP
View PDF3 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At this stage, the ingredients of flame retardants are mostly halogen-based, phosphorus-based, etc., and once burned, certain toxic components will still be released.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fire-retardant insulating polyvinyl chloride material and electrical sleeve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Ingredient parts by weight

[0058] 120 parts of polyvinyl chloride;

[0059] 60 parts of flame retardant masterbatch;

[0060] 5 parts of chlorinated polyethylene;

[0061] 0.5 part of calcium zinc stabilizer;

[0062] 0.5 parts of polyethylene wax;

[0063] 1 part paraffin;

[0064] ACR401 2 copies;

[0065] 20 copies of MBS;

[0066] 10 parts of calcium carbonate;

[0067] 2.5 parts of rutile titanium dioxide.

Embodiment 2

[0069] Ingredient parts by weight

[0070] 150 parts of polyvinyl chloride;

[0071] 50 parts of flame retardant masterbatch;

[0072] 3 parts of chlorinated polyethylene;

[0073] 0.2 part of calcium zinc stabilizer;

[0074] 0.3 parts of polyethylene wax;

[0075] 0.5 parts of paraffin;

[0076] ACR401 1 copy;

[0077] 15 copies of MBS;

[0078] 10 parts of calcium carbonate;

[0079] 2 parts of rutile titanium dioxide.

Embodiment 3

[0081] Ingredient parts by weight

[0082] 100 parts of polyvinyl chloride;

[0083] 20 parts of flame retardant masterbatch;

[0084] 2 parts of chlorinated polyethylene;

[0085] 0.2 part of calcium zinc stabilizer;

[0086] 0.3 parts of polyethylene wax;

[0087] 0.5 parts of paraffin;

[0088] ACR401 1 copy;

[0089] 10 copies of MBS;

[0090] 8 parts of calcium carbonate;

[0091] 1.8 parts of rutile titanium dioxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fire-retardant insulating polyvinyl chloride material and an electrical sleeve made from the material. The fire-retardant insulating polyvinyl chloride material comprises the following raw materials in part by weight: 100 to 150 parts of polyvinyl chloride, 0.2 to 5 parts of heat stabilizer, 5 to 20 parts of compatibilizer, 20 to 60 parts of fire retardant master batch, 0.3 to 1 part of lubricant, 1 to 3 parts of titanium white powder, 10 to 20 parts of impact modifier, 2 to 4 parts of processing aid and 5 to 20 parts of calcium carbonate. The fire-retardant insulating polyvinyl chloride material provided by the invention has excellent flame retardant property and insulating property; the oxygen index can be over 33.4; the test is up to V-0 level according to the measurement standard of GB / T2048-2008 plastic combustibility; and the resistivity can be up to 1.1*1,011 Omega.m. Therefore, the material can meet the requirement on insulation and fire retardance of a low-voltage wire cable.

Description

technical field [0001] The invention relates to a flame-retardant insulating material, in particular to a flame-retardant insulating polyvinyl chloride material. In addition, the present invention also relates to a bushing, especially an electrical bushing. Background technique [0002] Polyvinyl chloride plastic has good physical, mechanical and electrical properties, and is suitable for insulation and sheathing materials for low-voltage wires and cables. In special occasions, there will be higher flame retardant requirements for wires and cables. The oxygen index is used to evaluate the flame retardant performance of materials. The higher the oxygen index, the better the flame retardant performance. [0003] Polymer materials are mostly composed of carbon, hydrogen, oxygen and other elements, so they are flammable and combustible materials, and even produce a lot of smoke and toxic gases when burning, causing great harm to the environment and a huge threat to people's lif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/28C08L51/00C08L23/08C08L51/06C08L77/02C08K13/06C08K9/10C08K3/34C08K3/32C08K5/053C08K3/22C08K3/26H02G3/04H01B17/58
Inventor 林云青张文霖郝洪波
Owner KANGTAI PLASTIC SCI & TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com