Bark powder phenolic-resin adhesive and preparation method thereof
A technology of phenolic resin and bark powder, applied in adhesives, aldehyde/ketone condensation polymer adhesives, adhesive types, etc., can solve the problems of high equipment corrosion, high equipment requirements, and low replacement rate. Achieve the effect of low production conditions, low price and good quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028] Bark powder phenolic resin adhesive formula and process:
[0029] Formula: 100 parts of phenol (solid), 125 parts of larch bark powder (solid), 70 parts of sodium hydroxide (solid), 5 parts of calcium sulfite (solid), 8 parts of anhydrous sodium sulfite (solid), formaldehyde (37% ) 275 parts, 236 parts of water.
[0030] Note: 70 parts of sodium hydroxide (solid) is prepared with 105 parts of water to make a 40% sodium hydroxide solution.
[0031] Process: start the reactor mixer, add 131g water, add 117g sodium hydroxide solution (40%), add bark powder 125g, add anhydrous sodium sulfite 8g, add calcium sulfite 5g, add 100g phenol, pass into steam and heat up to 110°C, keep warm for 2.5-3.0 hours. During the activation treatment stage of larch bark powder, the reaction kettle is required to be airtight to prevent the loss of moisture and phenol volatilization.
[0032] Turn off the steam valve to stop heating, and pass cold water to cool the feed liquid to 55°C, then...
Embodiment 2
[0035] Bark powder phenolic resin adhesive formula and process:
[0036] Formula: 100 parts of phenol (solid), 45 parts of larch bark powder (solid), 48 parts of sodium hydroxide (solid), 2 parts of calcium sulfite (solid), 4 parts of anhydrous sodium sulfite (solid), formaldehyde (37% ) 210 parts, 144 parts of water.
[0037] Note: 48 parts of sodium hydroxide (solid) is prepared with 72 parts of water to make a 40% sodium hydroxide solution.
[0038] Process: Start the reactor mixer, add 72g of water, add 80g of sodium hydroxide solution (40%), add 45g of larch bark powder, add 4g of anhydrous sodium sulfite, add 2g of calcium sulfite, add 100g of phenol, and feed steam to heat up To 110°C, keep warm for 2.5-3.0 hours. During the activation treatment stage of larch bark powder, the reaction kettle is required to be airtight to prevent the loss of moisture and phenol volatilization.
[0039] Turn off the steam valve to stop heating, and pass cold water to cool the feed liq...
Embodiment 3
[0042] The effects of using calcium sulfite and not using calcium sulfite on the curing rate and water-resistant bonding strength of larch bark powder phenolic resin adhesive were compared.
[0043] Formula and process:
[0044] Recipe and technology are except not using calcium sulfite, other are identical with embodiment 1. In order to verify the use of calcium sulfite on the curing rate and water-resistant bond strength. The testing of curing rate and water-resistant bonding strength is carried out according to the method specified in the national standard GB / T14074-2006.
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com