A method of manufacturing an intermediate frequency low loss mnzn ferrite core

A technology of a ferrite core and a manufacturing method, which is applied in the manufacture of inductors/transformers/magnets, inorganic material magnetism, electrical components, etc., can solve the problems that nano-additives are not easy to disperse uniformly, nano-materials are easy to agglomerate, and energy consumption is high. The effect of high saturation magnetic flux density, good powder activity and low loss

Active Publication Date: 2012-02-15
江门江益磁材有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the manganese-zinc ferrite core of the invention has excellent performances of high frequency, high saturation magnetic flux density and low loss, its production cost is high due to the use of nano-scale oxides as additives, and because nano-materials are easy to agglomerate , the nano-additives are not easy to disperse evenly during the production process
[0006] Therefore, it can be seen that the existing MnZn power ferrite materials, such as the manufacturing method of MnZn ferrite cores, have the disadvantages of high sintering temperature and high energy consumption, which lead to high manufacturing costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of manufacturing an intermediate frequency low loss mnzn ferrite core
  • A method of manufacturing an intermediate frequency low loss mnzn ferrite core
  • A method of manufacturing an intermediate frequency low loss mnzn ferrite core

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Weigh the main component: 67wt% Fe with a purity of 99.3% or more 2 o 3 , 24wt% Mn 3 o 4 (Mn content is 71.1%), the purity of 9wt% is ZnO more than 99.7%, takes by weighing low-temperature flux simultaneously: CuO based on the CuO of 0.2wt% of main component gross weight; Add 80wt% water of the total weight of the powder to the material, stir and grind to mix evenly; after spray drying, pre-calcine at 800°C for 2 hours; based on the total weight of the pre-calcined powder, add additives: 0.04wt% CaCO 3 , 0.003wt% SiO 2 , 0.02wt% Nb 2 o 5 , 0.01wt% ZrO 2 And then add low temperature flux: 0.06wt% TiO 2, then add 60wt% of deionized water, 1wt% of dispersant, and 1wt% of defoamer for secondary grinding until the average particle size is 1.0±0.2μm; after drying, based on the total amount of ground powder Weight, in this powder, add the aqueous solution granulation of the polyvinyl alcohol of 8wt% (above each material can be purchased from the market); Green sample...

Embodiment 2

[0040] Weigh the main component: 70wt% Fe with a purity of 99.3% or more 2 o 3 , 23wt% Mn 3 o 4 (Mn content is 71.1%), the purity of 7wt% is 99.7% ZnO, weighs low-temperature flux simultaneously: based on the SnO of 0.25wt% of main component gross weight 2 and 0.25wt% TiO 2 ; In the sand mill, add 90wt% water of the total weight of the powder to the powder weighed above, stir and grind and mix evenly; after spray drying, pre-calcine at 780 ° C for 3 hours; based on the pre-calcined The total weight of the powder, adding additives: 0.05wt% CaCO 3 , 0.004wt% SiO 2 , 0.03wt% Nb 2 o 5 , 0.02wt% ZrO 2 And then add low temperature flux: 0.09wt% SnO 2 , and then add 70wt% deionized water, 1wt% dispersant, and 1wt% defoamer for secondary grinding, until the average particle size is 1.0±0.2μm; after drying, based on the total amount of ground powder Weight, in this powder, add the aqueous solution granulation of the polyvinyl alcohol of 8wt% (above each material can be purcha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method for manufacturing an intermediate frequency low-loss MnZn ferrite core, the method is composed of the following steps: A, batching; B, grinding and mixing; C, pre-burning; D, secondary grinding; E, granulation ; F, molding; G, sintering. The invention promotes the solid-phase reaction by adding low-temperature flux, thereby reducing the pre-burning temperature, and can greatly save energy on the basis of achieving the same solid-phase reaction effect. In addition, because the pre-calcination temperature is low, the activity of the powder is better, so the reaction can occur at a lower temperature, thereby reducing the sintering temperature of the present invention and saving energy. At the same time, the MnZn ferrite core manufactured by the invention has lower loss and higher saturation magnetic flux density.

Description

technical field [0001] The invention relates to a method for manufacturing a MnZn ferrite core, in particular to a method for manufacturing an intermediate frequency low-loss MnZn ferrite core. Background technique [0002] Since the advent of power ferrite (LPL) materials, MnZn ferrite core materials have been receiving attention and have been widely used in the field of switching power supply transformers. With the continuous improvement of the manufacturing process, the development trend of ferrite materials, especially its high frequency and low loss, is very rapid. For example, Japan's TDK company has developed a loss-free ferrite with a working frequency of 100kHz-500kHz by using a spray roasting powder making process. PC40 (H7C4) and PC44 materials have dropped sharply, and Philips has launched 3F4 with a working frequency of 2MHz, and even 3F5 materials with a working frequency of 4MHz. Although the high-frequency development of MnZn ferrite materials is very rapid,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/34H01F41/02B22F9/04B22F3/12C04B35/26C04B35/645
Inventor 汪南东谭福清黄爱萍豆小明王家永冯则坤
Owner 江门江益磁材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com