A technology of anchoring agent and firecrackers, which is applied in the field of new anchoring agents, can solve problems such as unfavorable firecrackers processing and production, affecting firecrackers, and mismatching completion time, so as to realize large-scale firecrackers processing and production, reduce production costs, and reduce preparation costs. cost effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0009] Example 1, the novel firecracker fixing agent is uniformly mixed from three raw materials of Portland cement, powdered stone and hardener, and the weight percentage of the three raw materials is: Portland cement 25% wt, powdered stone 75%wt, the powdered stone is 50-100 mesh, Portland cement and powdered stone are mixed first to obtain a mixture, and then 4% chlorine by weight of Portland cement is added to the mixture Calcium, and then evenly stirred to obtain firecrackers anchoring agent. The firecracker anchoring agent of gained is used on the firecracker solidification and sealing process, sprays into appropriate amount of water (water mist) in anchoring agent during use, quickly fills in the anchoring agent after the water spray wetting by hand or machinery Insert the firecrackers into the firecracker barrel, thereby fixing the firecracker lead wire and sealing the firecracker barrel, and the firecrackers are all cured in about 7 hours. After completing the firecra...
Embodiment 2
[0010] Embodiment 2, the novel firecracker fixing agent is formed by uniform mixing of three raw materials of Portland cement, powdery stone and hardener, and the weight percentages of the three raw material components are: Portland cement 20%wt, 80% wt of powdery stone, the powdery stone is 100-150 mesh, first mix Portland cement and powdery stone to obtain a mixture, then add triethanolamine with 3% weight of Portland cement to the mixture, Stir and mix evenly to obtain the firecracker fixing agent. Then complete the curing and sealing process according to the usage method of the anchoring agent described in Example 1. The firecrackers are all solidified in about 10 hours, and enter the next firecracker processing process after completing the firecracker curing and sealing process.
Embodiment 3
[0011] Example 3, the novel firecracker fixing agent is uniformly mixed from three raw materials of Portland cement, powdered stone and hardener, and the weight percentage of the three raw material components is: Portland cement 30% wt, powdery stone 70%wt, the powdery stone is 50-100 mesh, Portland cement and powdery stone are mixed first to obtain a mixture, and then add Portland cement weight 5% speed in the mixture A coagulant, the quick-setting agent is a mixture of alumina clinker, calcium carbonate and quicklime in a weight ratio of 1:1:0.5, and then uniformly stirred and mixed to obtain a firecracker anchoring agent. Then complete the curing and sealing process according to the usage method of the anchoring agent described in Example 1. The firecracker fixing agent is completely cured in 11.5 hours, and after completing the firecracker curing and sealing process, it enters the next firecracker processing process.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com