Two-component split type composite FDY fiber and preparation method thereof

A composite fiber and two-component technology, applied in the field of fiber spinning, can solve the problems of poor dyeability and harsh dyeing conditions of PET

Inactive Publication Date: 2010-09-29
XIAMEN HONGXIN SPECIAL FIBER CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing split-type FDY fibers are polyester / nylon split-type composite FDY fibers, that is, polyethylene terephthalate (PET) / polyamide (PA6) split-type composite FDY fibers, but due to poor dyeability of PET, Therefore, the dyeing conditions required for dyeing the fabric made of this nylon / polyester composite FDY fiber through fiber opening are relatively harsh, and dyeing can only be achieved under high pressure and high temperature conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-component split type composite FDY fiber and preparation method thereof
  • Two-component split type composite FDY fiber and preparation method thereof
  • Two-component split type composite FDY fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] 1. Preparation of double-group lobed FDY fibers

[0043] Take 78 parts of polytrimethylene terephthalate chips and dry them at 140°C, put them into a polyester spinning screw extruder and melt them at 275°C; take 22 parts of polycaprolactam chips, dry them at 90°C and put them into polyamide spinning The screw extruder melts at 270°C;

[0044] The melt of the two screw extruders was passed through as figure 2 The 8-split spinneret is extruded to obtain as-spun fibers. The following examples all use this spinneret to extrude to obtain 8-split as-spun fibers. The lobes between the fiber skeletons are composed of polycaprolactam, and the fiber lobes are polytrimethylene terephthalate;

[0045] Then, the as-spun fiber is cooled and shaped by ring blowing through a cooling blowing device, the cooling temperature is 23° C., and then oiled by an oil tanker on both sides. The oil agent is 10wt% siloxane emulsion, and the oil content of the fiber after oiling is 1.1 %, then ...

Embodiment 2 to Embodiment 4

[0049] 1. Preparation of double-group split-sheet FDY fibers

[0050] The concrete process parameter of this part operation among above-mentioned three embodiments sees Table 2:

[0051] Measure the performance of two-group split-sheet FDY fibers prepared in Examples 2 to 5, which are listed in Table 1.

[0052] 2. Preparation of two-component microfiber fabric

[0053] The process of this part of the above-mentioned three embodiments is all the same as that of Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a two-component split type composite FDY fiber which is characterized in that he two components in the two-component composite DTY fiber are a polyester component and a polyamide component, wherein the polyester component is selected from one or more of polytrimethylene terephthalate, polybutylene terephthalate and cation normal-pressure dyeable polyester. The invention also provides a preparation method for preparing the split type composite FDY fiber, which comprises the following steps: respectively melting the polyester component and the polyamide component, then carrying out extrusion molding through a spinneret plate, cooling, applying oil, drafting and winding to obtain the two-component split type composite FDY fiber. The composite FDY fiber and the two-component superfine fiber fabric which are prepared by the method have the characteristics of good dyeing property and soft texture.

Description

technical field [0001] The invention relates to the field of fiber spinning, in particular to a double-group split-sheet type composite FDY fiber and a preparation method thereof. Background technique [0002] Composite fiber refers to a chemical fiber made of two polymers, two or more polymers, or the same polymer with different properties through composite spinning, and contains two or more immiscible components in the cross section of the fiber. point. According to the structure, common composite fibers include side-by-side type, sheath-core type, island-in-the-sea type, split type, etc. [0003] The same single fiber cross-section of the two-group split-type composite fiber is divided into several partitions, and the two components are arranged alternately. According to the different arrangement methods, the split-type composite fiber can be divided into orange-shaped, rice-shaped, and gear type etc. The split-type composite fiber splits the two components from each o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/14D01F8/12D01D5/088D01D5/096D01D5/098D01D5/28
Inventor 张飞跃蔡世镇李森
Owner XIAMEN HONGXIN SPECIAL FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products