Anti-bonding bleed-out continuous casting covering slag

A technology of continuous casting mold slag and mold slag, which is applied in the field of protective powder, can solve the problems of destroying the performance of slag, achieve the effect of improving production efficiency and avoiding bonding breakouts

Active Publication Date: 2012-04-25
BAOSHAN IRON & STEEL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

MnO, Fe 2 o 3 There are too many oxidizing components such as CoO, etc., which are easy to react with reducing elements in molten steel, thus destroying the properties of slag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Mold flux composition: CaO: 33%, SiO 2 : 42%, Al 2 o 3 : 2%, F: 5%, Na 2 O: 7.6%, Li 2 O: 3.7%, B 2 o 3 : 2.2%, C: 2.8%, and the rest are impurities brought in by raw materials. The mold flux has a basicity of 0.78, a viscosity of 0.21 Pa.s at 1300°C, and a solidification temperature of 970°C.

Embodiment 2

[0025] Mold flux composition is: CaO: 28.2%, SiO 2 : 43.5%, Al 2 o 3 : 4%, F: 6.7%, Na 2 O: 5%, B 2 o 3 : 9%, C: 1.2%, and the rest are impurities brought in by raw materials. The mold flux has a basicity of 0.65, a viscosity of 0.35 Pa.s at 1300°C, and a solidification temperature of 935°C.

Embodiment 3

[0027] Mold flux composition: CaO: 22%, SiO 2 : 43%, Al 2 o 3 : 8%, F: 2.3%, Na 2 O: 4%, Li 2 O: 3%, B 2 o3 : 14.5%, C: 0.72%, and the rest are impurities brought in by raw materials. The mold flux has a basicity of 0.51, a viscosity of 0.48 Pa.s at 1300°C, and a solidification temperature of 950°C.

[0028] The mold slag consumption in the above three embodiments is between 0.4-0.5kg / t steel during use, and the liquid slag layer is kept within the range of 10-16mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a covering powder material, in particular to an anti-bonding bleed-out continuous casting covering slag. The components of the anti-bonding bleed-out continuous casting covering slag in weight percent are as follow: 2-8% of Al2O3, 2-7% of F, 4-8% of Na2O, less than 4% of Li2O, 2-15% of B2O3, 0.7-3% of C, less than 3% of impurities carried in by raw materials, and balance of CaO and SiO2 with the weight ratio of CaO / SiO2 being 0.5-0.8. The properties of the covering slag are as follows: solidification temperature is less then 980 DEG C, viscosity at 1300 DEG C is 0.2-0.5Pa.s, and no crystal is precipitated during solidification. The usabilities of the covering slag are as follows: consumption rate is larger than or equal to 0.4kg / t steel, and the thickness of melt slag layer is 10-16mm. The anti-bonding bleed-out continuous casting covering slag in the invention can prevent the phenomenon of bonding bleed-out, improve operation rate of continuous casting machine, and reduce cost and accidents.

Description

technical field [0001] The invention relates to a protective powder used in metal continuous casting, in particular to anti-bonding breakout continuous casting protective powder for steelmaking. Background technique [0002] Continuous casting mold flux is a powdery or small granular steelmaking auxiliary material used to cover the surface of molten steel in the mold of a continuous casting machine. It has many functions such as thermal insulation, preventing oxidation of molten steel, absorbing inclusions, lubricating and controlling heat transfer, etc., and plays an important role in the quality of casting slabs. [0003] When mold slag covers the surface of molten steel, a certain thickness of liquid slag layer must be formed between molten steel and solid mold slag, so as to effectively prevent the entry of air and accommodate more foreign inclusions, and provide a gap between the billet and the copper plate of the water-cooled crystallizer. Sufficient liquid slag is pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/108
Inventor 张晨蔡得祥宗震宇曹伟朱祖民胡暑名王洪亮潘永飞
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap