High-temperature resistant porcelain imitation material and production method thereof

A technology of imitating porcelain material and production method, applied in grain processing and other directions, can solve the problems of limiting the application range of melamine molding compound, small specific gravity, etc., and achieve the effect of making up for low temperature resistance and expanding application fields

Inactive Publication Date: 2010-02-24
KAIHUA RUIDA PLASTIC TECH
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional melamine molding compound is made of melamine-formaldehyde resin as the base material, wood pulp cellulose as the filler, and the powder molding compound is made by adding curing agent, lubricant and pigment. It is molded and pressed, and the product has a surface It is flat, non-toxic, tasteless, and drop-resistant, and is widely used in tableware, daily necessities, electrical appliances, etc.; but its specific gravity is small, without the heavy feeling of porcelain, and the temperature resistance is generally around 150 ° C, which limits the use of melamine. Applications of molding compounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Resin synthesis: Weigh 95kg of formaldehyde in the high-level metering tank and put it into a stainless steel reaction kettle, add sodium hydroxide solution to adjust the pH to 8.5-9.5, then add 80kg of melamine while stirring and heat at the same time, when the temperature rises to 60°C , stop heating, wait for the temperature to rise naturally to 80-85°C, keep warm, measure the water number (4°C), when the reaction is complete, add triethanolamine, and cool.

[0022] 2. Mixing of raw materials: Cool the melamine formaldehyde resin to below 60°C under stirring, add 26kg of glass fiber, 126kg of talcum powder, 60g of benzoic acid, 300g of zinc stearate, and 3.2kg of titanium dioxide, and heat to keep the temperature of the material at 60°C , and stirred for 60 minutes.

[0023] 3. Wet material drying: Open the condenser cooling water valve, vacuum pump, jacket steam valve, and reactor vent valve slowly. Under the condition of -0.05Mpa, when the material temperature r...

Embodiment 2

[0026] 1. Resin synthesis: Weigh 95kg of formaldehyde in the high-level metering tank and put it into a stainless steel reaction kettle, add sodium hydroxide solution to adjust the pH to 8.5-9.5, then add 80kg of melamine while stirring and heat at the same time, when the temperature rises to 60°C , stop heating, wait for the temperature to rise naturally to 80-85°C, keep warm, measure the water number (4°C), when the reaction is complete, add triethanolamine, and cool.

[0027] 2. Mixing of raw materials: Cool the melamine formaldehyde resin to below 60°C under stirring, add 32kg of whisker silicon, 120kg of talcum powder, 60g of benzoic acid, 300g of zinc stearate, and 320g of phthalocyanine blue, and heat to keep the temperature of the material at 60°C °C and stirred for 60 minutes.

[0028] 3. Wet material drying: Open the condenser cooling water valve, vacuum pump, jacket steam valve, and reactor vent valve slowly. Under the condition of -0.05Mpa, when the material temper...

Embodiment 3

[0031] 1. Resin synthesis: Weigh 95kg of formaldehyde in the high-level metering tank and put it into a stainless steel reaction kettle, add sodium hydroxide solution to adjust the pH to 8.5-9.5, then add 80kg of melamine while stirring and heat at the same time, when the temperature rises to 60°C , stop heating, wait for the temperature to rise naturally to 80-85°C, keep warm, measure the water number (4°C), when the reaction is complete, add triethanolamine, and cool.

[0032] 2. Mixing of raw materials: Cool the melamine formaldehyde resin to below 60°C under stirring, add 152kg of talcum powder, 60g of benzoic acid, 200g of zinc stearate, 120g of calcium stearate, and 3.2kg of titanium dioxide, and heat to keep the temperature of the material at 60°C, stirring for 60 minutes.

[0033] 3. Wet material drying: Open the condenser cooling water valve, vacuum pump, jacket steam valve, and reactor vent valve slowly. Under the condition of -0.05Mpa, when the material temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-temperature resistant porcelain imitation material and a production method thereof. The high-temperature resistant porcelain imitation material comprises the followingcomponents in percentage by weight: 30-35% of melamine formaldehyde resin, 0-10% of glass fiber, 55-65% of filler, 0-2% of coloring agent, 0.5-2% of curing agent and 0.5-3% of auxiliary agent. The production method of the high-temperature resistant porcelain imitation material comprises the steps of resin synthesizing, raw material mixing, wet material drying and dried material grinding and sieving. The porcelain imitation material which has vivid porcelain sensation and can resist the temperature of more than 220 DEG C is obtained by adjusting the formula of the molding material. The porcelain imitation material can be widely used for the industries of tableware, articles for daily use and the like, is especially suitable for products with higher high-temperature resistant requirements, such as electrothermal cookers and the like, makes up the defect of low temperature resistance of the original melamine molding material, and expands the application field of the melamine molding material.

Description

technical field [0001] The invention relates to a high-temperature-resistant porcelain-like material and a production method thereof, in particular to a high-temperature-resistant porcelain-like material of amino molding compound. Background technique [0002] The traditional melamine molding compound is made of melamine-formaldehyde resin as the base material, wood pulp cellulose as the filler, and the powder molding compound is made by adding curing agent, lubricant and pigment. It is molded and pressed, and the product has a surface It is flat, non-toxic, tasteless, and drop-resistant, and is widely used in tableware, daily necessities, electrical appliances, etc.; but its specific gravity is small, without the heavy feeling of porcelain, and the temperature resistance is generally around 150 ° C, which limits the use of melamine. Applications of molding compounds. Contents of the invention [0003] The purpose of the present invention is to provide a high-temperature-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L61/28C08K7/14C08K3/34C08K3/26B29B13/06B02C23/16
Inventor 杨国华
Owner KAIHUA RUIDA PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com