Preparation method of nano coating

A nano-coating and nano-powder technology, applied in the field of coatings, can solve the problems of lack of weather resistance, color retention, gloss retention and aging resistance, short service life, short service life, etc. Good construction performance

Active Publication Date: 2009-12-09
马秀荣
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The scrub resistance of nano-coatings depends on the surface effect of nano-materials, and it shows scrub resistance on the coating. For ordinary latex paints, the scrub resistance is very low, generally only 1000-2000 times. Therefore, use The number of years is short and cannot meet people's requirements
[0005] General paint coatings do not have strong weather resistance, color retention, gloss retention and aging resistance. Therefore, the service life of the coating is short. Nanomaterials have a strong shielding effect on ultraviolet rays, which can greatly slow down the sunlight on the coating. The destruction of the layer makes the coating have stronger weather resistance, color retention, gloss retention and aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nano coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0046] A kind of preparation method of nano coating is carried out according to the following steps:

[0047] The first step: prepare the nano-calcium carbonate slurry, take 75% of the water and add it to the container, add 25% of the calcium carbonate into the water, stir while adding, until it is uniform, and prepare the nano-calcium carbonate slurry for use;

[0048] Step 2: To prepare nano-composite slurry, first add 19.5% water to the reactor, start stirring, and then add ethylene glycol 14.7%, dispersant PK200 2.5%, dispersant SN5040 5%, wetting agent NP in order -10 0.3%, 4% nano-titanium dioxide and 4% nano-silicon dioxide, stir while adding until uniform, and finally add 50% nano-calcium carbonate slurry, stir for 5-10 minutes, and then use a high-speed shearing machine to react Cut in the kettle for 30 minutes to preliminarily disperse the powder, then send the slurry after the preliminary dispersion of the powder into a sand mill for 2-3 times of grinding, each time...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a nano coating. In the method, nano-composite size is adopted and added with fillers and various auxiliary agents; the mixture is mixed and reacts in a reaction kettle, sheared, emulsified, milled and dispersed in a sand mill, concocted in a paint mixing kettle and filtered in a filter so as to prepare the nano coating. The method comprises the following steps: step 1: concocting nano calcium carbonate size; step 2: preparing nano-composite size; step 3: employing the reaction kettle for mixing and reaction; step 4: employing a high-speed shear emulsifying machine for shearing and emulsifying for 30min; step 5: transferring the size to the sand mill for milling and dispersion for 2-3 times, with 30-50min per times; step 6: transferring the size to the paint mixing kettle to be stirred, adding phenylethylene-propyl ethylene acid ester emulsion, a film forming auxiliary agent and a defoamer while stirring and finally adding propylene glycol and a bactericide; step 7: adjusting the pH value to 8-9; step 8: adding a thickener to ensure the viscosity to be 3000-4000 MPa.S; step 9: adopting a coating filter for filtering and preparing the finished product after filtering. The coating is bactericidal, nontoxic, tasteless and resistant to 300000 times of washing.

Description

technical field [0001] The invention relates to a coating, in particular to a preparation method of a nano coating. Background technique [0002] At present, a large number of wall paints sold on the market in our country contain organic solvents. Although some powder materials are inorganic powders, the material components used contain certain toxic pigments and fillers, which produce certain harmful substances during production and use. Pollution affects human health. [0003] The reason why the paint coating is not resistant to stains, dust, and dirt is mainly determined by the surface structure of the paint and the characteristics of the material. The paints sold on the market are either hydrophobic or oleophobic. The former Good water resistance, but not oil resistance; the latter has good oil resistance, but not water resistance. For this reason, making the amphiphobic structure of the nano coating is very beneficial to people's living requirements. [0004] The scr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D5/14C09D7/12
Inventor 赵青山
Owner 马秀荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products