Novel environment-friendly composite material and application thereof

A composite material and environmentally friendly technology, applied in household containers, decorative arts, plates, etc., to achieve the effect of clear texture, hard texture and simple manufacturing process

Inactive Publication Date: 2012-01-11
高农
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a new type of environmentally friendly composite material and its application. In order to solve the above-mentioned defects of the existing single material or composite material, its raw material ratio is scientific and reasonable, the source is extensive and rich, green and energy-saving, low in price, and simple in production process , the prepared product has excellent performance, strong use and decoration effect and market competitiveness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] tea tray tea set

[0026] The components of the raw materials of the composite material include: in parts by mass:

[0027] Magnesium oxide 8 parts

[0028] Magnesium chloride 8 parts

[0029] Silicon dioxide and titanium dioxide (according to any mass ratio) 1 part

[0030] Sand or sawdust powder or bamboo powder 3 parts.

[0031] When stirring and mixing, add pigments according to the color of the product, add yellow, brown and green iron oxide pigments, and adjust the amount according to the required color, such as adjusting the color of the log.

[0032] The preparation process is:

[0033] First, make tea tray and tea set molds according to the products produced. The molds are carved with wood carving, stone carving or mud carving, or directly purchase products of various materials and appearances, or make molds with silica gel, gypsum or fiberglass, plastic, leather, iron or steel;

[0034] Before preparation, wax the mold or apply a release agent so that the...

Embodiment 2

[0036] Decorative sheet

[0037] The components of the raw materials of the composite material include: in parts by mass:

[0038] Magnesium oxide 10 parts

[0039] Magnesium chloride solution 10 parts

[0040] Silicon dioxide and titanium dioxide (according to any mass ratio) 3 parts

[0041] Sand or sawdust powder or bamboo powder 10 parts.

[0042] When stirring and mixing, add pigments of various colors. The pigments are commonly used pigments for decorative materials. The added colors and dosage can be adjusted according to the color requirements of the product.

[0043] When stirring and mixing, add glass fiber filaments, the addition amount of the glass fiber filaments is: 4 parts; adding glass fiber filaments increases the toughness of the product.

[0044] The preparation process is:

[0045] First of all, make decorative plate molds according to the products produced. The molds are carved with wood carving, stone carving or mud carving, or directly purchase prod...

Embodiment 3

[0048] relief

[0049] The components of the raw materials of the composite material include: in parts by mass:

[0050] Magnesium oxide 9 parts

[0051] 9 parts magnesium chloride solution

[0052] Silicon dioxide and titanium dioxide (according to any mass ratio) 2 parts

[0053] 5 parts of sand or sawdust powder or bamboo powder.

[0054] Pigments of various colors can also be added during stirring and mixing. This pigment is a commonly used pigment for decorative materials. The added color and dosage can be adjusted according to the color of the product.

[0055]The raw materials in the composite material also include glass fiber filaments, which are added during stirring and mixing. The amount of the glass fiber filaments added is: 2-3 parts; adding glass fiber filaments increases the toughness of the product.

[0056] The preparation process is:

[0057] First, make relief molds according to the reliefs made. The molds are carved with wood carving, stone carving or ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
wear resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a novel environment-friendly composite material and application thereof, and belongs to the technical field of material preparation. The composite material comprises raw materials of magnesium oxide and magnesium chloride taken as substrates, sawdust powder or sand or bamboo flour taken as a filler, and silicon dioxide and titanium dioxide added as active agents. The methodfor preparing the composite material comprises the following steps: dissolving the magnesium chloride into water 12 hours earlier in a ratio of 1:1-2; then, mixing the solution with other raw materials evenly; pouring the mixture into a mould for natural solidification or heating solidification; and obtaining the formed composite material after mould stripping. The novel environment-friendly composite material can be used for preparing tea trays, tea sets, rilievo and various decorating boards with carving effect. The novel environment-friendly composite material overcomes the defects of the prior single material and composite material, has the advantages of scientific and reasonable raw material matching, broad and rich raw material sources, environmental protection and energy conservation, low price, simple manufacture process, and excellent performance of prepared products, and has strong use and decoration effects and strong market competitive force.

Description

technical field [0001] The invention belongs to the technical field of material preparation, and more specifically relates to a novel environment-friendly composite material and its application. Background technique [0002] Tea trays, tea sets, reliefs or various decorative panels with engraving effects on the market are mostly made of a single wooden material, which is expensive, and excessive harvesting of wood will also bring harm to the environment. There are also stone and jade materials, but there are disadvantages such as expensive raw materials, inconvenient processing, time-consuming and labor-intensive manufacturing process, and high cost. There are also various decorative composite materials on the market, but due to the difference in raw materials and production, there are many shortcomings such as poor performance, high cost, and inconvenient production. Contents of the invention [0003] The purpose of the present invention is to provide a new type of envir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/32B28B1/14B28B11/00B44C3/04A47G19/02A47G19/16A47G19/22C04B14/42C04B14/06C04B18/26
CPCC04B2103/0014C04B2111/00965C04B2103/0019C04B28/32C04B2111/00017Y02W30/91C04B14/06C04B14/42C04B18/26C04B2103/10C04B2103/54C04B18/248C04B22/06
Inventor 高农
Owner 高农
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com