Maleimide modified polymethacrylimide foam and preparation method thereof

A technology of polymethacrylimide and maleimide, which is applied in the field of maleimide-modified polymethacrylimide foam and its preparation, can solve the problem of poor temperature resistance and low mechanical strength of foam , large foam deformation and other problems, to achieve the effect of improving heat resistance, high heat resistance, and increasing imide structure

Active Publication Date: 2009-10-07
AEROSPACE RES INST OF MATERIAL & PROCESSING TECH
View PDF1 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two methods are prone to phase separation, large foam deformation, poor foam temperature resistance, and low mechanical strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Maleimide-modified polymethacrylimide foam of the present invention, it obtains by following component mixing reaction:

[0044] Monomer: methacrylic acid (MAA), its weight ratio is 35;

[0045] Monomer: methacrylonitrile (MAN), its weight ratio is 65;

[0046] Maleimide modifier: tribromophenylmaleimide, its weight ratio is 10;

[0047] Initiator: azobisisobutyronitrile AIBN, its weight ratio is 0.1;

[0048] Foaming agent: Virahol, its weight ratio is 10;

[0049] Nucleating agent: magnesium oxide, its weight ratio is 1;

[0050] Crosslinking agent: triallyl cyanurate, its weight ratio is 0.1.

[0051] The preparation method of above-mentioned maleimide modified polymethacrylimide foam, it adopts following steps to carry out successively:

[0052] (1) monomer methacrylic acid and methacrylonitrile, maleimide modifier, initiator, foaming agent, nucleating agent, crosslinking agent are weighed according to metering, uniformly mixed to form a reaction solution;

[...

Embodiment 2

[0057] Maleimide-modified polymethacrylimide foam of the present invention, it obtains by following component mixing reaction:

[0058] Monomer: methacrylic acid (MAA), its weight ratio is 45;

[0059] Monomer: methacrylonitrile (MAN), its weight ratio is 55;

[0060] Maleimide modifier: phenylmaleimide, its weight ratio is 1;

[0061] Initiator: azobisisovallonitrile, its weight ratio is 2.0;

[0062] Foaming agent: urea, its weight ratio is 20;

[0063] Nucleating agent: calcium oxide, its weight ratio is 8.

[0064] The preparation method of above-mentioned maleimide modified polymethacrylimide foam, it adopts following steps to carry out successively:

[0065] (1) monomer methacrylic acid and methacrylonitrile, maleimide modifier, initiator, foaming agent, nucleating agent are weighed according to metering, uniformly mixed to form a reaction solution;

[0066] (2) Put the reaction solution into a sealed mold consisting of two glass plates and rubber strips (rubber str...

Embodiment 3

[0070] Maleimide-modified polymethacrylimide foam of the present invention, it obtains by following component mixing reaction:

[0071] Monomer: methacrylic acid (MAA), its weight ratio is 55;

[0072] Monomer: methacrylonitrile (MAN), its weight ratio is 45;

[0073] Maleimide modifier: butylmaleimide, its weight ratio is 0.1;

[0074] Initiator: azobisisobutyronitrile (AIBN) and dibenzoyl peroxide mixture, its weight ratio is 1.0;

[0075] Foaming agent: tert-butyl alcohol, its weight ratio is 1.0;

[0076] Nucleating agent: urea, its weight ratio is 4.

[0077] The preparation method of above-mentioned maleimide modified polymethacrylimide foam, it adopts following steps to carry out successively:

[0078] (1) monomer methacrylic acid and methacrylonitrile, maleimide modifier, initiator, foaming agent, nucleating agent are weighed according to metering, uniformly mixed to form a reaction solution;

[0079] (2) Put the reaction solution into a sealed mold consisting of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
dielectric lossaaaaaaaaaa
Login to View More

Abstract

The invention relates to high-performance copolymer foam, in particular to maleimide modified polymethacrylimide foam and a preparation method thereof. The maleimide modified polymethacrylimide foam is obtained by the mixed reaction of the components according to the weight proportions: 35-60 of methyl acrylic acid (MAA), 65-40 of methacrylonitrile (MAN), 0.1-50 of maleimide modifier, 0.10-2.0 of initiator, 1.0-20 of foaming agent, 0.1-8 of nucleating agent and 0.1-5 of crosslinking agent. The maleimide modified polymethacrylimide foam has high heat resistance, is not changed in color by heating under the temperature of 220 DEG C for long time, has the heat distortion temperature higher than 200 DEG C, and has the highest mechanical performance in all foams under the same intensity.

Description

technical field [0001] The invention relates to a high-performance copolymer foam, in particular to a maleimide-modified polymethacrylimide foam and a preparation method thereof. Background technique [0002] In the structural design of resin matrix composites, sandwich structural composites are a typical light-weight, high-strength, high-modulus structural material, which combines the high strength and The organic combination of high modulus and low density of the sandwich forms a lightweight, high-strength and high-rigidity structural composite material, which has extremely important applications in industries such as aircraft, rockets, radar, shipbuilding, transportation, and medical equipment. [0003] Polymethacrylimide (PMI) foam is mainly used as the core material of composite sandwich structure, which has the following properties: (1) 100% closed-cell structure, and isotropic; (2) good heat resistance, heat The deformation temperature is 180-240°C; (3) Excellent mec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/06C08F220/50C08F2/44C08J9/04C08K3/22C08K5/21C08L33/02C08L33/22C08F222/40
Inventor 赵飞明穆晗
Owner AEROSPACE RES INST OF MATERIAL & PROCESSING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com