Technique and device for producing glasses from non-plane glass

A production process, non-planar technology, applied in the field of silver mirror production process and its equipment, can solve the problems of waste of production cost, low production efficiency, increase of cost input, etc., so as to reduce production cost, increase production cost and improve utilization rate Effect

Inactive Publication Date: 2009-10-07
SHANGHAI NANLI CHEM
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] In addition, in this field, the entire glass product is vertically soaked in a tank filled with liquid medicine to solve the problem of thin coating at the edges and corners, but the product is coated with coating on the surface without coating, resulting in waste of production cost and low production efficiency; Or the surface that does not need to be coated is protected with a film in advance, and then immersion treatment is performed. The problem with this treatment is that the production cost of a single film is very high, and the production efficiency is also very low, which cannot form a large-scale production line.
Secondly, some manufacturers use physical methods, such as vacuum deposition of silver, they must use large-scale vacuum equipment to achieve quantitative production, resulting in increased production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Technique and device for producing glasses from non-plane glass
  • Technique and device for producing glasses from non-plane glass
  • Technique and device for producing glasses from non-plane glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Embodiment 1: as Figure 5 As shown, silver mirror production is performed on a diamond-like eight-sided tapered glass body with a height of 1.95mm

[0052] The first group: using the flat glass silver mirror production process, the silver nitrate solution used is 250 g / L

[0053] Group 2: Spray with 8 g / L silver nitrate (no pictogram)

[0054] The third group: use 8 grams per liter of silver nitrate to spray (adopt pictographic frame of the present invention)

[0055] First of all, the eight-sided tapered glass body is covered with 220*220mm PVC plastic, and the PVC plastic film is used as a partial protection of the non-processed surface and positioning; it is put into the tray 18, and the material is loaded;

[0056] Then, carry out cleaning, use mechanical method to add selenium oxide powder to scrub or adopt ultrasonic wave to add surfactant to clean, clean and rinse with deionized water;

[0057] Secondly, use divalent tin ions to sensitize the glass surface, a...

Embodiment 2

[0069] Embodiment 2: For example Figure 6 Concave condenser mirrors shown with a height of 22mm for silver mirror production

[0070] The first group: using the flat glass silver mirror production process, the silver nitrate solution used is 250 g / L

[0071] Group 2: Spray with 8 g / L silver nitrate (no pictogram)

[0072] The third group: use 8 grams per liter of silver nitrate to spray (adopt pictographic frame of the present invention)

[0073] Firstly, silicone rubber is used as a partial protection of the non-processing surface and positioning; it is put into the tray 18 and loaded;

[0074] Then, carry out cleaning, use mechanical method to add selenium oxide powder to scrub or adopt ultrasonic wave to add surfactant to clean, clean and rinse with deionized water;

[0075] Secondly, use divalent tin ions to sensitize the glass surface, and rinse with deionized water after sensitization;

[0076] silver plating again,

[0077] The first group: spray 1 square meter of...

Embodiment 3

[0087] Embodiment 3: for such as Figure 7 The shown three-shuttle mirror with a height of 17.23mm, two adjacent slopes are used as reflective surfaces for silver mirror production

[0088] The first group: using the flat glass silver mirror production process, the silver nitrate solution used is 250 g / L

[0089] Group 2: Spray with 8 g / L silver nitrate (no pictogram)

[0090] The third group: use 8 grams per liter of silver nitrate to spray (adopt pictographic frame of the present invention)

[0091] Firstly, silicone rubber is used as a partial protection of the non-processing surface and positioning; it is put into the tray 18 and loaded;

[0092] Then, carry out cleaning, use mechanical method to add selenium oxide powder to scrub or adopt ultrasonic wave to add surfactant to clean, clean and rinse with deionized water;

[0093] Secondly, use divalent tin ions to sensitize the glass surface, and rinse with deionized water after sensitization;

[0094] silver plating ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heightaaaaaaaaaa
Login to View More

Abstract

The invention discloses a technique and device for producing glasses from non-plane glass. The technique comprises steps of locally protecting a non-processed face of non-plane glass to be processed; rinsing; sensitizing treatment; silver plating; after positioning the non-plane glass to be processed, pressing downwards an image frame, encircling the non-plane glass to be processed in the image frame, spraying silver nitrate mixed liquid medicament onto the image frame through a spraying device until the liquid completely submerge the highest point of the non-plane glass to be processed to promote the liquid medicament to completely react with surface of the glass chemically; after reacting for a while, lifting the image frame to discharge the reacted liquid medicament; rinsing out the liquid medicament, winding to remove water, drying with hot wind; spraying protective paint, baking; cooling the glass face, taking out the glass. The technique is applied to making reflection layer of non-plane shuttle mirror. Because of the image frame used in production device, production cost is greatly saved; production efficiency is greatly improved; and massive flow line production can be realized.

Description

Technical field: [0001] The invention relates to a silver mirror production process, in particular to a silver mirror production process of non-planar glass or glass with irregular shapes and equipment thereof. Background technique: [0002] The silver mirror production process of flat glass in the prior art is generally as follows: first, the flat glass is sent to the upper end of the production line, polished, cleaned, sensitized, silver-plated, copper-plated, painted, dried, painted again, and baked again. , cleaning, off-line and other processes to complete the production of flat glass silver-plated mirrors, and the silver mirror plates coming out of the export end can be packaged and sold at the factory. [0003] The whole process can be described in detail as follows [0004] 1. The flat glass to be processed is sent to the production line; [0005] 2. Cleaning, after removing organic stains, polishing, and cleaning with pure water again, the glass is cleaned; [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/10
Inventor 张志艺
Owner SHANGHAI NANLI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com