Fiber deep dyeing promoter

A technology of deepening agent and fiber, applied in fiber processing, textile and papermaking, etc., can solve the problem of insufficient performance, and achieve the effect of increasing absorption and reducing reflected light

Inactive Publication Date: 2009-06-03
东莞市嘉宏纺织助剂有限公司
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

That is, it can be treated with fluorine-containing resin, acrylic resin, silicone resin, urethane resin or a mixture of low-refractive index resins to improve dark color, but the performance is not sufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber deep dyeing promoter
  • Fiber deep dyeing promoter
  • Fiber deep dyeing promoter

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] a. Synthesis of hydroxy-terminated amino silicone oil:

[0055] Calculated in parts by weight, 96 parts of octamethylcyclotetrasiloxane, 4 parts of -C 3 H 6 NHC 2 H 4 NH 2 The amino coupling agent was added to the reaction kettle, stirred and heated, heated to 90°C for holding at a stirring speed of 60 rpm, after holding for 2 hours, continued to heat to 130°C, and 0.2 parts of 50% NaOH aqueous solution was added as an alkaline catalyst. Increase the temperature to 140°C and keep it for 3 to 4 hours, adjust its viscosity to 1200-3000mPa.S, ammonia value 0.5, and cool to below 60°C to prepare the hydroxyl-terminated amino silicone oil of the following structural formula, and discharge it for later use.

[0056] The structural formula of the hydroxyl-terminated amino silicone oil is as follows:

[0057]

[0058] Among them, R is: -C 3 H 6 NHC 2 H 4 NH 2 , M=100, n=25.

[0059] Synthesis of partial hydrolysate of methyltrimethoxysilane:

[0060] b. Calculated in parts by wei...

Embodiment 2

[0063] a. Synthesis of hydroxy-terminated amino silicone oil:

[0064] Calculated in parts by weight, 94 parts of octamethylcyclotetrasiloxane, 6 parts of -C 3 H 6 NH 2 Add amino coupling agent into the reaction kettle, stir and heat, heat up to 90°C for holding, stirring speed 60 rpm, after holding for 2 hours, continue to heat up to 130°C, add 0.2 parts of 50% potassium hydroxide aqueous solution to make alkaline The catalyst is heated to 140°C for 3 to 4 hours, adjusted its viscosity to 800-2000mPa.S, ammonia value is 0.5, and cooled to below 60°C to prepare a hydroxyl-terminated amino silicone oil of the following structural formula, which is discharged for use.

[0065] The structural formula of the hydroxyl-terminated amino silicone oil is as follows:

[0066]

[0067] Among them, R is: -C 3 H 6 NH 2 , M=210, n=30.

[0068] b. Synthesis of partial hydrolysate of methyltrimethoxysilane:

[0069] Calculated in parts by weight, 80 parts of methyltrimethoxysilane, 17 parts of ...

Embodiment 3

[0072] a. Synthesis of hydroxy-terminated amino silicone oil:

[0073] Calculated in parts by weight, 91 parts of octamethylcyclotetrasiloxane, 9 parts of —CH 3 Add the amino coupling agent to the reaction kettle, stir and heat, heat up to 90°C for holding at a stirring speed of 60 rpm, after holding for 2 hours, continue to heat up to 130°C, add 0.2 parts of 50% BaOH aqueous solution as a basic catalyst, Increase the temperature to 140°C and keep it for 3 to 4 hours, adjust its viscosity to 600-1500mPa.S, ammonia value 0.5, and cool to below 60°C to prepare hydroxyl-terminated amino silicone oil of the following structural formula, and discharge it for later use.

[0074] The structural formula of the hydroxyl-terminated amino silicone oil is as follows:

[0075]

[0076] Among them, R is: —CH 3 , M=310, n=50.

[0077] b. Synthesis of partial hydrolysate of methyltrimethoxysilane:

[0078] Calculated in parts by weight, 80 parts of methyltrimethoxysilane, 17 parts of deionized ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of textile finishing agent, in particular to a fiber deep dyeing promoter. According to weight percentage, the fiber deep dyeing promoter comprises 10-30% of hydroxyl-terminated amino silicone oil, 1-10% of part hydrolysate of methyl trimethoxysilane, 3-20% of nonionic emulsifier, 0.5-5% of acetic acid, and 55-85% of deioned water; after textile finishing, the fiber deep dyeing promoter is attached to the surface of the fiber textile and generates moist crosslinking reaction during the heat treatment process so as to form a single-molecule organosilicon polysiloxane film layer; by virtue of the extremely low reflectivity of the rganosilicon polysiloxane film layer, the light radiating on the surface of the textile generates refraction and diffuse reflection on the fiber surface, the absorption quantity of the incident light of the textile is greatly increased and the reflective light is reduced, thus achieving the effect of deepening dyeing.

Description

Technical field: [0001] The invention relates to the technical field of textile finishing agents, in particular to a fiber dyeing deepening agent. Background technique: [0002] At present, because synthetic fibers have high strength, good wear resistance, and low cost, their output has increased year by year. In recent years, they have been widely used and accepted. Among them, polyester fiber has the largest output. As a high value-added product, textiles often require a high-end sense of deep color. For polyester fibers, it is difficult to achieve the desired color depth through dyeing methods. Polyester fiber has a special specular luster and a refractive index of 1.71. Therefore, when light is irradiated on the surface of the polyester fiber, a large amount of incident light is reflected on the surface of the fiber, and only a small part of the incident light is refracted to the inside of the fiber. The dye absorbs and becomes colored light, resulting in insufficient dyeing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643
Inventor 贺剑
Owner 东莞市嘉宏纺织助剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com