Method for manufacturing ceramic mixed product

A production method and product technology are applied in the field of preparation of ceramic mixed products, which can solve the problems of different glazing and complicated processes, and achieve the effects of increasing carbon content, ensuring stability, improving air permeability and adsorption.

Inactive Publication Date: 2009-05-27
谢锐鑫 +1
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 2. The difference in glazing
[0010] The sintering temperature of porcelain is generally 1200-1400 degrees, and the process is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The pottery clay and porcelain clay are respectively put into the ball mill according to the ratio of ball: clay: water 10:5:2. After ball milling for 22 hours, it will be aged for 3 months to make a predetermined shape of matching ceramic body and porcelain body. body, and then control the water content of the ceramic body and the porcelain body in a humidity box to be 30%, attach the porcelain body to the surface of the pottery body, dry in the shade and then fire.

[0023] Its lead content is 0, and it will not burst after a heat exchange with water at 150°C-20°C.

Embodiment 2

[0025] The pottery clay and porcelain clay are respectively put into the ball mill according to the ratio of ball: clay: water 10:5:2. After ball milling for 22 hours, it will be aged for 3 months to make a predetermined shape of matching ceramic body and porcelain body. Then control the moisture content of both the ceramic body and the porcelain body to 30% in a humidity box, attach the porcelain body to the surface of the ceramic body, dry in the shade and then biscuit at a firing temperature of 1100°C for 7 hours, and then at a high temperature of 1300 ° C, and alternately in an oxidizing atmosphere, a reducing atmosphere, and a neutral atmosphere, firing in a firing atmosphere for 10 hours, and then repeated high-temperature firing once after taking it out.

[0026] Its lead content is 0, and it will not burst after a heat exchange with water at 280°C-0°C.

Embodiment 3

[0028] Prepare pottery clay and porcelain clay respectively. The composition and mass ratio of clay clay are: Hunan feldspar 15, quartz 5, Feitianyan pottery washing mud 30, burnt talc 3, bentonite 8, Baoshan red clay 23, Yixing pottery stone 16; the composition and mass ratio of porcelain mud are: Hunan feldspar 12, Feitianyan porcelain washing mud 33, bentonite 12, Guizhou soil 5, Zhongxia white clay 20, bauxite 18.

[0029] Then put it into the ball mill according to the ratio of ball:mud:water 10:5:2, and after 22 hours of ball milling, it will be stale for 3 months to make a predetermined shape of matching ceramic body and porcelain body, and then moisturize Control the moisture content of the ceramic body and the porcelain body in the box to be 30%, attach the ceramic body to the surface of the ceramic body, dry it in the shade, and then burn it at a firing temperature of 1100°C for 7 hours. The embryo body is glazed and then fired at high temperature. Among them, the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a ceramic hybrid product, which relates to the method for preparing potteries and porcelains, in particular to the method for preparing the ceramic hybrid product. The method comprises the following steps: after performing ball milling and mustiness on a pottery pug and a porcelain pug respectively, and preparing the pottery pug and the porcelain pug into a pottery blank and a porcelain blank which are matched with each other; and adhering the porcelain blank to the surface of the pottery blank when the moisture percentage of both the pottery blank and the porcelain blank is 30 percent, and firing the blanks after drying. The method combines pottery and porcelain organically so that while the stability of a finished product at high temperature is guaranteed, the finished product not only has the characteristic of ancient pottery, but also has the characteristic of subtleness of porcelain, thus the method can be better applied to the preparation of tea pots and other supplies.

Description

【Technical field】 [0001] The invention relates to a method for preparing ceramics, in particular to a method for preparing ceramic mixed products. 【Background technique】 [0002] Pottery and porcelain are essentially two different utensils. Pottery was invented first, and porcelain was developed on the basis of self-improvement of pottery. The extensive techniques of raw material selection, washing and refining, mud processing, embryo forming, and kiln roasting are basically the same. The relationship between them seems to be close, but they are completely different from the conditions of formation and the composition of internal components. Their differences are: [0003] 1. The raw materials of fetal soil are different [0004] Pottery clay is made of clay that is easily obtained from nature through the relay of Denantu. China clay is made of a rock-like ore. , Pottery is close to soil, porcelain is close to stone. [0005] 2. The difference in glazing [0006] The su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/00C04B33/13
Inventor 谢锐鑫佘金浩
Owner 谢锐鑫
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com