Tellurium copper alloy material for electric power industry and method for producing the same

An alloy material and industrial technology, applied in the field of preparation of new alloy materials, can solve problems such as reducing production costs, and achieve the effects of reducing production costs, shortening production cycles, and reducing energy consumption

Inactive Publication Date: 2009-05-13
SICHUAN XINJU MINERAL RESOURCE DEV CO LTD
View PDF1 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

reduce manufacturing cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tellurium copper alloy material for electric power industry and method for producing the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0029] 1. Examples of the preparation of tellurium-copper alloy materials for the electrical power industry are shown in Table 1.

[0030] 2. The chemical composition test (percentage by weight) of the tellurium-copper alloy material is shown in Table 2.

[0031] 3. Test the distribution uniformity of tellurium in the tellurium-copper alloy material in the length direction of the ingot.

[0032] Take a sample at the head, middle and tail of the ingot with a diameter of 90 mm and a length of 10 meters, and measure the content of tellurium. The results (Te%) are shown in Table 3.

[0033] 4. The comparison of the main properties of tellurium-copper alloy materials produced under the old and new components and process conditions is shown in Table 4.

[0034] Table 1 Preparation of tellurium-copper alloy materials for electrical power industry *

[0035]

[0036] * The amount of R and Te added includes the amount of burning loss. Due to the smelting with a new lining, the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tellurium copper alloy material for the electric power industry and a method for preparing the same. The method is characterized by comprising the following steps: gradually adding 99.55 to 99.89 weight percent of industrial pure copper after a molten channel of a power-frequency induction furnace is melted; raising the temperature of a copper liquid to between 1,190 and 1,230 DEG C after solid state copper is melted down, and covering the copper liquid with charcoal to keep the temperature; enwrapping 0.1 to 0.4 weight percent of pure tellurium, and pressing the pure tellurium to the bottom of a power-frequency furnace close to a molten channel opening at a furnace temperature of between 1,190 and 1,230 DEG C; adding 0.01 to 0.05 weight percent of microelement into a tellurium copper alloy liquid after 50 to 80 minutes; finishing the smelting of the tellurium copper alloy liquid after 15 to 30 minutes; reducing the furnace temperature to between 1,150 and 1,180 DEG C; pouring the alloy liquid into a graphite crystallizer for crystallization; towing a cast ingot by using the prior method and sawing the cast ingot into short cast ingots with specific lengths; sampling the short cast ingots to test the content; and packaging the short cast ingots into finished products.

Description

technical field [0001] The invention relates to a tellurium-copper alloy material used in the electric power industry and a preparation method thereof, belonging to the field of preparation of new alloy materials. Background technique [0002] Because tellurium copper alloy has excellent high conductivity, arc resistance, good strength plasticity and cold and hot processing performance, it can be widely used in IT, electronics, electrical appliances, cables and other high-end industrial sectors. In the past, the process and equipment used to solve the problem of adding tellurium and additive elements that have a low density and do not form a solid solution with copper and homogenizing them in copper are relatively complicated. For example, the current process flow is: tellurium-copper master alloy melting and casting---vacuum melting and casting of low-melting element master alloy---500Kg medium frequency induction furnace melting---1000Kg power frequency induction furnace i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/00C22C1/03
Inventor 侯仁义陈家钊侯立玮叶辉成王云富
Owner SICHUAN XINJU MINERAL RESOURCE DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com