Electrical insulation compound adhesive for high voltage electrical apparatus

A technology for high-voltage electrical appliances and adhesives, used in adhesives, adhesive types, organic insulators, etc.

Active Publication Date: 2009-02-18
STATE GRID SICHUAN ELECTRIC POWER CORP ELECTRIC POWER RES INST +1
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The performance indicators of the existing phenolic adhesives still cannot meet the above requirements, and there are still problems in the bonding strength, toughness and aging resistance for the bonding between different metals and between metals and plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The composition of high voltage electrical insulation adhesive is as follows:

[0018] Phenolic resin 150, epoxy resin 35, hexamethylenetetramine 10, nitrile latex 100, 2-mercaptobenzothiazole zinc salt 6, accelerator PX 3, zinc naphthenate 3, rosin 30, benzene 200 , acetone 100, toluene diisocyanate 20, mica powder 60.

Embodiment 2

[0020] The composition of high voltage electrical insulation adhesive is as follows:

[0021] Phenolic resin 160, epoxy resin 40, hexamethylenetetramine 12, nitrile latex 110, 2-mercaptobenzothiazole zinc salt 6, accelerator PX 3, zinc naphthenate 3, rosin 30, benzene 200 , acetone 100, toluene diisocyanate 20, mica powder 60.

Embodiment 3

[0023] The composition of high voltage electrical insulation adhesive is as follows:

[0024] Phenolic resin 160, epoxy resin 30, hexamethylenetetramine 12, nitrile latex 110, 2-mercaptobenzothiazole zinc salt 8, accelerator PX 4, zinc naphthenate 4, rosin 35, benzene 220 , acetone 120, toluene diisocyanate 22, mica powder 80.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-voltage electrical apparatus insulated adhesive, which comprises the following components by weight portion: 150 to 160 portions of bakelite, 30 to 40 portions of epoxide resin, 10 to 12 portions of methenamine, 100 to 110 portions of nitrile latex, 5 to 8 portions of 2-mercaptobenzothiazole zinc salt, 2 to 4 portions of accelerant PX, 2 to 4 portions of zinc naphthenate, 30 to 35 portions of colophony, 200 to 220 portions of benzene, 100 to 120 portions of acetone, 20 to 22 portions of toluene diisocyanate, and 50 to 80 portions of mica powder. The high-voltage electrical apparatus insulated adhesive has excellent bonding properties, ageing resistance and chemical mediator resistance as well as excellent insulating properties, which is applicable for bonding metal units, and in particular applicable for manufacturing of high-voltage electrical apparatuses and equipment.

Description

technical field [0001] The invention relates to an adhesive, especially a thermosetting adhesive which is used for bonding high-voltage electrical appliances and has good heat resistance and good insulation. Background technique [0002] Phenolic adhesives are adhesives that are mainly composed of phenolic resins (made by the reaction of phenol and formaldehyde). Due to different reaction conditions (with different additives), it can form thermoplastic resin or thermosetting resin. Phenolic adhesives have the characteristics of lower cost (lower than epoxy adhesives) and better heat resistance, but have the disadvantage of brittleness. For high-voltage electrical equipment, the working environment is high in temperature, highly corrosive, and requires high insulation levels. The performance indicators of the existing phenolic adhesives still cannot meet the above requirements, and there are problems in the bonding strength, toughness and aging resistance that need to be fu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J161/06H01B3/36C09J163/00C09J109/04
Inventor 梁健徐伟何旭东王瑗
Owner STATE GRID SICHUAN ELECTRIC POWER CORP ELECTRIC POWER RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com