Method for manufacturing ceramic tile

A method of making ceramic tiles, which is applied to clay products, other household utensils, household utensils, etc. It can solve the problems of high water absorption, low surface gloss, and weak layering of tiles, etc., and achieve high gloss and super strong Effect of antifouling ability, effect improvement

Inactive Publication Date: 2008-12-10
淄博东岳实业总公司建材厂
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the ceramic tile products of the prior art still have disadvantages such as poor layering, high water absorption, and low surface gloss.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1) Ingredients, consisting of the following raw materials: 200Kg of washed mud, 200Kg of sodium ore, 200Kg of albite, 50 parts of potassium feldspar, 150 parts of feldspar, and 20 parts of talc. The supplier of washed mud is Sibi Kejiayao Xinhui Mining Company.

[0039] 2) preparation process, comprises the following steps:

[0040] a. Ingredients: pulverize and mix the above-mentioned raw materials;

[0041] b. Ball milling: Use wet ball milling to grind the above-mentioned base material to a particle size of 0.2-0.5mm.

[0042] c. Flour making: put the ball mill slurry into the slurry tank, after settling for more than 12 hours, transfer it to the transfer slurry tank, spray dry, and make powder. The particle size distribution of the obtained powder is:

[0043] 30 mesh ≤4%

[0044] 40 mesh 18~22%

[0045] 80 mesh 66~70%

[0046] 100 mesh 3~7%

[0047] Micropowder ≤3%.

[0048] d. Ingredients: The batching process is to uniformly mix the base material powder w...

Embodiment 2-3

[0053] Carry out batching according to table 1, preparation method is with embodiment 1:

[0054] Table 1 Ingredients list

[0055] raw material name

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing a ceramic tile, belonging to the clay ceramic product technical field characterized by compositions. The method for preparing the ceramic tile is characterized in that the basic formula mainly comprises the following raw materials by weight portion: 20 to 25 portions of watered mud, 20 to 30 portions of sodium ore, 20 to 30 portions of albite, 5 to 10 portions of orthoclase, 15 to 25 portions of feldspar and 2 to 5 portions of pencil stone. The product has clear layering effect on the surface and super infectant resistance and improves the surface finish by improving the formula and the powder size of the raw materials.

Description

technical field [0001] The invention belongs to the technical field of clay ceramic products characterized by ingredients, and in particular relates to a method for making ceramic tiles. Background technique [0002] The basic technological process of ordinary glazed tiles is: selection of raw materials-coarse crushing-fine crushing-batching-spray drying-milling-pressing bricks-drying-firing-plain brick selection-water spraying-glazing-decoration-glazing firing-inspection and packaging . [0003] The Chinese patent with the publication number CN1513801A discloses a processing technology for artistic ceramic tiles. The raw materials used are by weight: 35-45 parts of Laiyang soil, 25-35 parts of diopside, 5-15 parts of clay, 3-6 parts of albite Potassium feldspar 2-4 parts talc 2-4 parts bentonite 6-8 parts additive 1-2.5 parts. [0004] Publication number is that the Chinese patent of CN1709822A discloses a kind of ceramic tile and manufacture technology thereof, and it is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C04B33/24
Inventor 臧涛
Owner 淄博东岳实业总公司建材厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com