Method for producing recombination module wood from secondary processing wood

A technology for wood and lumber, applied in the field of production of reconstituted modular lumber, can solve the problems of water resistance, sun resistance, deformation, etc., and achieve the effects of not easy to crack, fine texture and simple process

Inactive Publication Date: 2008-10-15
浙江仕强竹业有限公司
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most logs still have defects such as cracking, deformation, water resistance, and light resistance.
[0004] my country's technology wood manufacturers will produce a large amount of waste scraps during the production process, most of these scraps are treated as garbage, resulting in huge waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Select the leftover wood of the rotary-cut plank with a thickness of 1.0-2.0 cm, and process the leftover material with high-temperature steam. The steam pressure is 1.5Mpa, and the temperature is 135-140° C. for 1.5 hours.

[0026] Dry the wood to reduce the moisture content of the wood to below 10%, so that the wood can better absorb the resin solution.

[0027] Dip the dried wood into the phenolic resin solution for 10 minutes, so that the wood can fully absorb the resin.

[0028] The drying temperature is controlled to be 55° C., and the impregnated wood is dried to make its moisture content 12-18%.

[0029] Bind the wood into a uniform handle with a length of 1.93 meters and a weight of 3-10Kg.

[0030] The handle is pressed into shape with a hydraulic press, and the pressure is 17-18Mpa.

[0031] The pressed semi-finished product is sent to the high-temperature curing equipment for consolidation and shaping, so that the phenolic adhesive is fully consolidated. ...

Embodiment 2

[0033] Select high-tech wood scraps with a thickness of 0.5-0.8 cm, and process them with high-temperature steam. The steam pressure is 1.5Mpa, and the temperature is 135-140°C. Treat for 3 hours, and disperse the glued scraps while they are hot.

[0034] Dry the wood to reduce the moisture content of the wood to below 10%, so that the wood can better absorb the resin solution.

[0035] Dip the dried wood into the phenolic resin solution for 7 minutes, so that the wood can fully absorb the resin.

[0036] The drying temperature is controlled to be 50°C, and the soaked wood is dried to make its moisture content 12-18%.

[0037] Bind the wood into a uniform handle with a length of 1.93 meters and a weight of 3-10Kg.

[0038] The handle is pressed into shape with a hydraulic press, and the pressure is 17-19Mpa.

[0039] Send the pressed semi-finished product to the high-temperature curing equipment for consolidation and shaping, so that the phenolic resin is fully consolidated....

Embodiment 3

[0041] With specific embodiment 1 through steam treatment, oven dry, dipping, the rotary cut plank leftover after gluing post-drying treatment, and specific embodiment 2 after steam treatment, oven dry, dipping, gluing post-drying treatment The technological wood leftovers are arranged alternately and bundled into uniform handles with a length of 1.93 meters and a weight of 3-10Kg. Use a hydraulic press to press the leftover handle into shape with a pressure of 17-18Mpa; consolidate the pressed semi-finished product at a high temperature of 150°C for 14 hours to obtain a finished recombined modular wood product. The wood pattern pattern of this module is more abundant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method of recombined module wood production by using secondary processing wood such as peeling board or reconstituted decoration lumber scrap. The method includes the steps of: vapor treating at a high temperature or digesting in oxydol and caustic soda, drying, gumming, further drying after being gummed, trimming, compression moulding, consolidating at a high temperature and obtaining the recombined module wood; the density of the obtained wood reaches 0.8-1.2kg / cm<3>, and the obtained wood has unique texture, fine texture and superior performance, and no need for treatments of insect prevention, mold prevention, corrosion resistance and cracking prevention. The obtained wood can be directly applied to fields of flooring, furnishing, building, etc., and is characterized by cracking resistance, deformation resistance and so on. The method has simple procedure, makes good use of the waste and greatly saves the forest resource by producing module wood with the waste secondary processing wood, thus, being an ideal substitute of the log.

Description

technical field [0001] The invention relates to a production process of modular wood, in particular to a method for producing recombined modular wood by using sub-processed wood such as veneer and veneer instead of logs. Background technique [0002] At present, in the world, with the rapid development of furniture, flooring, paper and other industries, a large number of log resources are consumed, and forest resources are decreasing day by day, which not only causes great damage to forest resources, but also causes soil erosion, Environmental degradation and other issues. However, the market demand for furniture and flooring is still increasing. [0003] When using logs to produce modular wood, it is necessary to carry out a long period of aging treatment, degreasing, anti-corrosion and other pretreatments on the logs, and a lot of leftovers are produced during the processing. Most logs also have shortcomings such as cracking, deformation, water resistance, and light resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27M1/02B27K5/04B27K3/34
Inventor 宋建平胡军卫
Owner 浙江仕强竹业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com