Pd/Sn colloid catalyst adsorption enhancer

A technology of adsorption promotion and catalyst, applied in liquid chemical plating, metal material coating process, coating and other directions, can solve the problems of decreased adhesion between raw materials and electroplating film, and achieve the effect of improving precipitation and good coating

Inactive Publication Date: 2008-10-08
EBARA-UDYLITE CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, methods such as improving the throwing property of copper sulfate electroplating by adding a polyol compound to the solution in the metal coating step after the catalyst is also proposed (for example, refer to Patent Docum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pd/Sn colloid catalyst adsorption enhancer
  • Pd/Sn colloid catalyst adsorption enhancer
  • Pd/Sn colloid catalyst adsorption enhancer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Using the solution of the present invention and the comparison solution described below, the following to-be-treated objects were subjected to catalyst imparting treatment, and the surface thereof was subjected to electroplating treatment.

[0039] (1) Objects to be processed

[0040] Processed object 1:

[0041] Adopt a surface area of ​​about 8dm 2 ABS rearview mirror cover (mirror cover) for automobiles. A jig made of sol-baked varnish made of vinyl chloride is used as a jig for plating to support the object to be processed at three contact points.

[0042] Processed object 2:

[0043] The surface area used is about 6dm 2 ABS molded parts for automobiles. A jig for plating is used that supports the object to be processed at two contact points, and other than the contact points are made of vinyl chloride sol-baked varnish.

[0044] (2) Catalyst treatment

[0045] First, place the object fixed on the jig in an etching solution composed of an aqueous solution con...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed are: a Pd/Sn colloid catalyst adsorption enhancer which can be used for the formation of a metal coating film on the surface of a non-conductive material (e.g., plastic) by plating with good efficiency; a catalyst-addition solution comprising the adsorption enhancer; and a method for plating a non-conductive material. The adsorption enhancer can be used for the plating onto a non-conductive material and comprises a bromine compound of any one selected from a typical metal element, a typical non-metal element and a transition metal element with bromine. The bromine compound may be lithium bromide, sodium bromide, aluminum bromide, potassium bromide, calcium bromide, strontium bromide, tin (II) bromide, cesium bromide, barium bromide, hydrobromic acid, silicon (IV) bromide, vanadium (III) bromide, manganese (II) bromide, iron (II) bromide, cobalt (II) bromide, nickel (II) bromide, palladium (II) bromide, gold (III) bromide, or the like. The non-conductive material may be an ABS resin, a PC resin-blended ABS resin, or the like.

Description

technical field [0001] The present invention relates to an adsorption promoter for a palladium-tin colloidal catalyst for promoting the adsorption of a palladium-tin colloidal catalyst on the surface of a non-conductive material when a metal coating is formed by electroplating on a non-conductive material such as plastic, and an adsorption promoter containing the adsorption promoter. Catalyst-donating solution of agent and electroplating method of non-conductive material. Background technique [0002] Conventionally, in order to form a metal coating on non-conductive materials such as plastics, the method adopted is the following so-called plastic plating method: that is, a palladium-tin colloidal catalyst (hereinafter referred to as "Pd / Sn colloidal catalyst") is deposited on The so-called catalytic treatment of depositing on the surface of the non-conductive material is followed by conductive treatment such as electroless plating or metal coating treatment as necessary, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D5/56C23C18/18
CPCC23C18/28C23C18/30
Inventor 衣幡和男横山景
Owner EBARA-UDYLITE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap