Magnesium cement fireproof board having excellent water-resistance and preparation thereof

A technology of fire-proof board and magnesium cement, which is applied in the field of magnesium cement fire-proof board, can solve the inherent problems of magnesium oxychloride cement, warping and deformation, and increase costs, etc., and achieve excellent non-combustibility and no warping and deformation , The effect of low thermal expansion coefficient

Inactive Publication Date: 2010-06-02
李锦富
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] (3) Warping deformation, thermal expansion, and bursting
The addition of additives increases the cost and solves some problems, but it cannot fundamentally solve the inherent problems of magnesium oxychloride cement, because the system of magnesium oxychloride cement has not changed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnesium cement fireproof board having excellent water-resistance and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1: taking weight as a unit, pour 80 parts of magnesium sulfate and 1 part of tartaric acid into a blender, add quantitative water, stir, adjust the Baume degree of magnesium sulfate and tartaric acid to be 26, add 85% light magnesium oxide 150 parts, 20 parts of perlite, 120 parts of heavy filler (heavy calcium carbonate), 22 parts of light filler (sawdust). Stir for 5 minutes, then discharge the material, and shape it on the fireproof board production line with double-layer 2-piece fiber mesh cloth. After it reaches a certain strength, it can be demoulded and cut.

Embodiment 2

[0025] Embodiment 2: taking weight as a unit, pour 80 parts of magnesium sulfate and 1 part of tartaric acid into a blender, add quantitative water, stir, adjust the Baume degree of magnesium sulfate and tartaric acid to be 26, add 85% light magnesium oxide 150 parts, 12 parts perlite, 120 parts heavy calcium carbonate, 22 parts sawdust. Stir for 5 minutes, then discharge the material, and shape it on the fireproof board production line with double-layer 2 pieces of fiber mesh cloth. After it reaches a certain strength, it can be demoulded and cut to produce magnesium cement fireproof board with excellent water resistance. plate. The product is detected by the test block, the flexural strength is > 10mpa, the compressive strength is > 25mpa, the softening coefficient is > 0.9, the flame resistance is Class A, and there is no phenomenon of frosting and halogen return.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention reltes to a fireproof board, belonging to the technical field of building material, decorative material, traffic facility, fireproof product, abrasive, abrasive tool and wood furniture.According to the formula of the invention, a preparation method comprises adding 80 portions of magnesium sulfate and 1 portion of tartaric acid into a mixer, adding water of suitable amount, mixing and adjusting the Baume degree of the magnesium sulfate and tartaric acid to 26, adding 150 portions of 85% light magnesium oxide, 12 portions of perlite, 120 portions of heavy calcium carbonate and 22portions of sawdust, mixing for 5min, emptying, shaping the materials on a fireproof board product line provided with two layers of dual fiber net bags, removing mould and cutting when the product reaches a suitable strength, to obtain the magnesium cement fireproof board with better water resistance. The inventive fireproof board has low thermal expansion factor, non warping deformation, softening factor higher than 0.9, non recurrent halogen, non frost mist, better freezing resistance and non combustibility.

Description

Technical field: [0001] The invention belongs to inorganic glass fiber reinforced plastics, and relates to materials used in the fields of building materials, decorative materials, traffic facilities, refractory products, abrasive abrasives, substitute wood furniture, etc., and particularly relates to a material: a magnesium cement fireproof board with excellent water resistance. technical background: [0002] Magnesium cement is a special kind of cement, which was invented by the Frenchman Sorrell in 1867, so it is also called cement by Sorrell. And because most of it is formed by the condensation of magnesium chloride and magnesium oxide, it is also called magnesium oxychloride cement. At the same time, it uses magnesium oxide as the main component, and people are used to calling them magnesium cement. Later, people used glass fiber to strengthen magnesium cement to make inorganic composite material, which is called inorganic glass fiber reinforced plastic. In the more t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B9/04C04B14/18
CPCC04B2111/29C04B28/30C04B2111/28C04B2111/27
Inventor 李锦富
Owner 李锦富
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com