High-strength high-ductility corrosion-resistant Al-Zn-Mg-(Cu) alloy

A high-strength, high-toughness, alloy technology, applied in the field of high-strength, high-toughness, corrosion-resistant Al-Zn-Mg-alloys, can solve the problems of expensive and difficult industrial aluminum alloy production, achieve cheap prices, maintain deformation recovery structure, and inhibit regeneration crystallization effect

Inactive Publication Date: 2008-06-25
CENT SOUTH UNIV
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high price of Sc, the current market price is about 40,000 RMB / kg, so it is difficult to be practically used in the production of industrial aluminum alloys.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength high-ductility corrosion-resistant Al-Zn-Mg-(Cu) alloy
  • High-strength high-ductility corrosion-resistant Al-Zn-Mg-(Cu) alloy
  • High-strength high-ductility corrosion-resistant Al-Zn-Mg-(Cu) alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1: Preparation of Al-8.6%Zn-2.5%Mg-2.2%Cu-0.08%Zr-0.1%Cr alloy. The raw materials used are high-purity aluminum (purity 99.99%), industrial pure Mg (purity 99.9%), industrial pure Zn (purity 99.9%), Al-Cu master alloy, Al-Zr master alloy, Al-Cr master alloy . First, high-purity aluminum is added to graphite clay crucible and melted in a resistance crucible furnace at a melting temperature of 780°C. After high-purity aluminum is melted, Al-Cu, Al-Cr, Al-Zr intermediate alloys are added and the temperature drops to 760°C. Add industrial pure Zn, melt and stir well, then add industrial pure Mg, remove surface slag, add 0.2% to 0.4% hexachloroethane (C 2 Cl 6 ) Refining agent deslagging and degassing, let it stand for 10 to 15 minutes, pour it into the iron mold, and demould after cooling.

Embodiment 2

[0033] Example 2: Preparation of Al-8.6%Zn-2.5%Mg-2.2%Cu-0.08%Zr-0.1%Cr-0.1Yb% (wt%) alloy. The raw materials used are high-purity aluminum (purity 99.99%), industrial pure Mg (purity 99.9%), industrial pure Zn (purity 99.9%), Al-Cu master alloy, Al-Zr master alloy, Al-Cr master alloy , Al-Yb master alloy. First, high-purity aluminum is added to the graphite clay crucible, and melted in a resistance crucible furnace at a melting temperature of 780°C. After the high-purity aluminum is melted, Al-Yb, Al-Cu, Al-Cr, and Al-Zr intermediate alloys are added to reduce the temperature. to 760°C, add industrial pure Zn, melt and stir well, then add industrial pure Mg, remove surface slag, add 0.2% to 0.4% hexachloroethane (C 2 Cl 6 ) Refining agent deslagging and degassing, let it stand for 10 to 15 minutes, pour it into the iron mold, and demould after cooling.

Embodiment 3

[0034] Example 3: Preparation of Al-8.6%Zn-2.5%Mg-2.2%Cu-0.08%Zr-0.1%Cr-0.1Er% (wt%) alloy. The raw materials used are high-purity aluminum (purity 99.99%), industrial pure Mg (purity 99.9%), industrial pure Zn (purity 99.9%), Al-Cu master alloy, Al-Zr master alloy, Al-Cr master alloy , Al-Er master alloy. First, high-purity aluminum is added to the graphite clay crucible, and melted in a resistance crucible furnace at a melting temperature of 780°C. After the high-purity aluminum is melted, Al-Er, Al-Cu, Al-Cr, and Al-Zr intermediate alloys are added to reduce the temperature. to 760°C, add industrial pure Zn, melt and stir well, then add industrial pure Mg, remove surface slag, add 0.2% to 0.4% hexachloroethane (C 2 Cl 6 ) Refining agent deslagging and degassing, let it stand for 10 to 15 minutes, pour it into the iron mold, and demould after cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength high-toughness corrosion-resistant Al-Zn-Mg-(Cu) alloy. Appropriate Cr is also added when Zr is added in the Al-Zn-Mg-(Cu) alloy; or when the Zr is added, the Cr and rare earth element Er or Yb are added. After composite addition of the elements, the invention can improve recrystallization resistance of the Al-Zn-Mg-(Cu) alloy, improve the strength, the fracture toughness and the anti-stress-corrosion performance of the alloy at the same time; micro-alloys such as Zr, Cr and so on, and the rare earth metal Er or Yb have relatively low cost and are more suitable for industrialization production.

Description

technical field [0001] The invention relates to the preparation of metal alloys, in particular to the field of high-strength, high-toughness, corrosion-resistant Al-Zn-Mg-(Cu) alloys. Background technique [0002] Forming fine coherent dispersed phases through microalloying, effectively inhibiting recrystallization and grain growth, and maintaining the deformation recovery structure is a way to simultaneously improve the strength and stress corrosion resistance of high-strength and super-strength aluminum alloys. In the early stage, the non-coherent aluminide dispersed phase was formed by adding trace amounts of Cr and Mn. Later changed to add Zr to form metastable L1 2 Type Al 3 Zr coherent dispersed phase, which improves the resistance to recrystallization and improves stress corrosion resistance, but metastable L1 2 Type Al 3 Zr transforms into incoherent stable DO during long-term homogenization and solution treatment at high temperature 23 Type Al 3 Zr dispersed p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/00C22C1/03
Inventor 陈康华方华婵张茁祝昌军黄兰萍
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com