Method of preparing protein modified polyacrylonitrile fibre

A technology of polyacrylonitrile fiber and polyacrylonitrile, which is applied in cellulose/protein conjugated rayon, spinning solution preparation, wet spinning, etc. The branch rate is difficult to control and other problems, so as to increase economic benefits, improve production efficiency, and improve mechanical properties.

Inactive Publication Date: 2008-01-23
DONGHUA UNIV
View PDF8 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patents with application numbers 02139295.1, 011331919.4 and 03148421.2 disclose methods for preparing protein and polyacrylonitrile graft copolymerized fiber spinning dope and fibers, but the problem with this method is that the grafting rate of acrylonitrile is relatively low, and the copolymerized method, the technical route is more complicated, the grafting rate is difficult to control, and the manufacturing cost is relatively increased
However, the solvents used in the above method in the spinning solution preparation process are organic reagents or inorganic salts. Organic solvents are volatile, causing serious pollution to the environment and endangering the health of operators; and inorganic reagents are highly corrosive. , extremely corrosive to the equipment
In addition, the recovery of these chemical reagents requires multi-stage decompression evaporation and multi-stage crystallization settling. The entire recovery process is not only cumbersome and requires strict control of process parameters, but also produces a large amount of waste gas and waste water, causing serious damage to the environment. Pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of preparing protein modified polyacrylonitrile fibre
  • Method of preparing protein modified polyacrylonitrile fibre
  • Method of preparing protein modified polyacrylonitrile fibre

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Raw material: silk protein, protein content 90%;

[0043] Polyacrylonitrile, viscosity average molecular weight 2.0×10 4 , is a copolymer comprising a first monomer, a second monomer and a third monomer, wherein the first monomer is 81.8% by mass of acrylonitrile, and the second monomer is 18% by mass of methyl acrylate %, the content of the third monomer itaconic acid is 0.2%;

[0044] Ionic liquid, 1-allyl-3-methylimidazolium chloride.

[0045] Mix dry silk protein with a mass percentage of 1% and dry polyacrylonitrile with a mass percentage of 99%, add it to 1-allyl-3-methylimidazolium chloride, and dissolve it at 50°C for 2 hours to obtain a stable Uniform spinning solution, the mass percentage of 1-allyl-3-methylimidazolium chloride in the solution is 95%, the spinning solution is filtered and defoamed at 50°C, extruded through a metering pump and a spinneret, and passed through 1cm layer of humid air, temperature is 5°C, humidity is 95%, enters a coagulation ba...

Embodiment 2

[0047] Raw material: wool protein, protein content 92%;

[0048] Polyacrylonitrile, viscosity average molecular weight 2.0×10 5 , is a copolymer comprising a first monomer and a second monomer, wherein the content of the first monomer is 90% of acrylonitrile, and the content of the second monomer of methyl methacrylate is 10%;

[0049] Ionic liquid, 1-butyl-3-methylimidazolium chloride.

[0050] Mix 20% wool protein with 80% polyacrylonitrile, add 1-butyl-3-methylimidazolium chloride, swell at 30°C for 2 hours, dehydrate, dissolve at 120°C for 1.5 hours, Obtain a stable and uniform spinning solution, the mass percentage of 1-butyl-3-methylimidazolium chloride in the solution is 92%, filter and defoam at 120°C, extrude through a metering pump and a spinneret, and pass through a 2cm wet The air layer, the temperature is 15°C, the humidity is 80%, enters the coagulation bath of 0°C, the mass percentage of 1-butyl-3-methylimidazolium chloride in the coagulation bath is 5%, enter...

Embodiment 3

[0052] Raw materials: soybean protein, protein content 94%;

[0053] Polyacrylonitrile, viscosity average molecular weight 5.0×10 4 , is acrylonitrile homopolymer;

[0054] Ionic liquid: 1-butyl-2-methylpyrazole bromide.

[0055] Mix 1% of dry soybean protein with 99% of 1-butyl-2-methylpyrazole bromide in mass percentage, dissolve at 70°C for 2 hours to obtain solution ①; mix 15% of Mix dry polyacrylonitrile with 85% by mass of 1-butyl-2-methylpyrazole bromide, dissolve at 80°C for 1 hour to obtain solution ②, then mix equal amounts of solution ①②, and stir at 80°C After 0.5 hours to obtain a stable and uniform spinning solution, filter and defoam at 80°C, extrude through a metering pump and a spinneret, pass through a 3cm layer of humid air at a temperature of 15°C and a humidity of 75%, and enter a coagulation bath at 20°C. The mass percent of 1-butyl-2-methylpyrazole bromide in the coagulation bath is 8%, and enters the hot water bath of 50 ℃ through the guide roller fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparing method for a protein modified polyacrylonitrile fiber, which comprises the following procedures: (1) some protein and polyacrylonitrile are solved in some ion liquid to prepare some equal-phase mixed crude liquid for spinning; (2) the spinning liquid is de-bubbled, filtered, dosed, then extruded by a spinning jet to form a fine spinning flow, which passes a wet air layer and enters into a condensing bath to condense and form; (3) fiber is spun after pre-tensioning, tensioning, water washing, drying and thermal forming, so protein modified polyacrylonitrile fiber is prepared. The method is environmental friendly, easy to recycle, of low production cost and high productivity; the clothing from the product made by the method is highly comfortable and healthy, and is of high fiber property.

Description

technical field [0001] The invention belongs to the field of preparation methods of polyacrylonitrile fibers, in particular to a preparation method of protein-modified polyacrylonitrile fibers. Background technique [0002] The main component of protein is a peptide chain composed of amino acids. It has many amino acids necessary for the human body, and has good biocompatibility and skin care and health care functions. Protein fibers including silk and wool have always been popular with consumers. However, natural The output of protein fiber is limited, it is difficult to meet the demand of the market, so the technology of using natural protein raw materials to produce regenerated protein fiber was born. However, the regenerated protein fiber prepared from pure protein is difficult to meet practical requirements due to its low strength. [0003] Polyacrylonitrile fiber has a wool-like feel and good bulkiness. It is called "synthetic wool". It is a light fiber with good drap...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/02D01F8/08D01D1/02D01D5/06
Inventor 张玉梅王华平王朝生程凌燕董炜星谢桂军
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com