Antibacterial polypropylene material and its preparation process

A technology of antibacterial polypropylene and polypropylene resin, applied in botany equipment and methods, biocides, plant growth regulators, etc., can solve the problems of poor antibacterial performance, unsustainable, high production cost, etc., and achieve improved weather resistance and reduced Production cost, fast effect of antibacterial properties

Inactive Publication Date: 2010-12-22
SHENZHEN KEJU NEW MATERIAL
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to overcome the traditional antibacterial polypropylene material with high production cost, poor antibacterial performance and non-durability, and provide a low production cost, excellent antibacterial performance, fast and durable polypropylene material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial polypropylene material and its preparation process
  • Antibacterial polypropylene material and its preparation process
  • Antibacterial polypropylene material and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0014] The present invention proposes a kind of antibacterial polypropylene material, and its component and content are:

[0015] 100 parts of polypropylene (PP) resin;

[0016] Filling agent 25-35 parts;

[0017] Toughening agent 5-15 parts;

[0018] 0.2-0.8 parts of antibacterial agent;

[0019] Dispersant 0.5~1.5 parts;

[0020] Antioxidant 0.1~0.5 parts;

[0021] UV absorber 0.1~0.5 part;

[0022] The above contents are by weight.

[0023] The polypropylene resin is homopolypropylene.

[0024] The antibacterial agent is compounded by nano-silver and organic silicon antibacterial agent in a mass ratio of 5:1.

[0025] The filler is nanometer calcium carbonate.

[0026] The toughening agent is polyolefin elastomer ethylene-1-octene copolymer (POE), which is 8150 type POE produced by DuPont Company of the United States.

[0027] The dispersant is TAS-2A, an ethylene bis fatty acid amide high-gloss lubricating dispersant.

[0028] The antioxidant is phosphite antioxi...

Embodiment 1

[0038] In parts by weight, mix 100 parts of PP resin, 25 parts of filler, 5 parts of toughening agent, 0.2 part of antibacterial agent, 0.5 part of dispersant, 0.1 part of antioxidant, and 0.1 part of ultraviolet absorber in a high-speed mixer 3 to 5 minutes, the speed of the high-speed mixer is 800 rpm; then the mixed raw materials are placed in a parallel twin-screw extruder for melt extrusion and granulation. The extrusion process is: 1 zone 170--180 ℃ , Zone 2 180--190°C, Zone 3 180--190°C, Zone 4 175--185°C, screw speed 300-350r / min, feeding frequency 15-20Hz, melt pressure 3.0-4.0MPa, vacuum degree -0.03---0.06MPa.

Embodiment 2

[0040] In parts by weight, 100 parts of PP resin, 30 parts of filler, 10 parts of toughening agent, 0.5 part of antibacterial agent, 1 part of dispersant, 0.3 part of antioxidant, 0.3 part of ultraviolet absorber, mixed in a high-speed mixer 3 to 5 minutes, the speed of the high-speed mixer is 800 rpm; then the mixed raw materials are placed in a parallel twin-screw extruder for melt extrusion and granulation. The extrusion process is: 1 zone 170--180 ℃ , Zone 2 180--190°C, Zone 3 180--190°C, Zone 4 175--185°C, screw speed 300-350r / min, feeding frequency 15-20Hz, melt pressure 3.0-4.0MPa, vacuum degree -0.03---0.06MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The antibacterial polypropylene material consists of polypropylene resin 100 weight portions, stuffing 25-35 weight portions, toughening agent 5-15 weight portions, antiseptic 0.2-0.8 weight portion, dispersant 0.5-1.5 weight portions, antioxidant 0.1-0.5 weight portion and ultraviolet absorber 0.1-0.5 weight portion. The polypropylene resin is homopolypropylene, and the antiseptic is compounded with nanometer silver and organosilicon antiseptic. The present invention also provides the preparation process of the antibacterial polypropylene material with low production cost, excellent antiseptic performance.

Description

technical field [0001] The invention relates to an antibacterial polypropylene material and a preparation method thereof, in particular to an antibacterial and durable polypropylene material and a preparation method thereof. Background technique [0002] Polypropylene (PP) is one of the five general-purpose plastics with a density of 0.90g / cm 3 , is the second lightest polymer material in existing resins (only larger than polymethylpentene, with a density of 0.85g / cm 3 ). [0003] In people's daily life, polypropylene plastic products are widely used: such as kitchen utensils, toilet facilities, trash cans, plastic shells of household appliances, wallpapers, food packaging bags, etc. Due to the appropriate temperature and humidity, it is very easy to be infected with bacteria. Therefore, it is extremely necessary to develop an antibacterial polypropylene material. [0004] At present, there are mainly two methods of making antibacterial polypropylene materials: filling t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08K5/524A01N59/16B29C47/40B29C47/92B29B9/12C08K3/26C08K5/10C08L23/08B29C48/04B29C48/92
CPCB29C48/04
Inventor 徐东贺永杨书涛
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com