Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ceramic porous membrane and ceramic filter

a ceramic filter and porous membrane technology, applied in membrane technology, membrane separation processes, membranes, etc., can solve the problems of membrane peeling, membrane formation defect, and inability to uniformly form membranes on the whole base surface, so as to reduce the number of membrane formation times and reduce the number of defects. , the effect of pressure loss

Inactive Publication Date: 2008-04-24
NGK INSULATORS LTD
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0018] In a case where a constitution in which the ceramic porous membrane is formed on the ultrafiltration membrane is employed, the membrane is formed on the ultrafiltration membrane having smoothness, and hence the thin ceramic porous membrane having less defects can be formed. In a case where a structure in which the ceramic porous membrane does not infiltrate the ultrafiltration membrane is used, a ceramic sol forming the ceramic porous membrane is not consumed for the infiltration, and can securely be formed into a membrane, so that the number of membrane formation times can be reduced. Since pressure losses in an ultrafiltration membrane portion are not increased, the ceramic porous membrane having a high flux can be prepared. When the titania membrane is employed as the ultrafiltration membrane, titania has a high durability against acid, alkali and water vapor as compared with another ceramic membrane. That is, the silica membrane having high separability, high flux and high durability can be prepared with reduced costs. Furthermore, since the titania membrane is formed on the porous base member and the silica membrane is formed on the titania membrane, the ceramic filter having high separability, high flux and high durability can be manufactured with reduced costs. When the ceramic porous membrane is the silica membrane, the membrane is suitable for an application of dehydration of alcohol such as ethanol or isopropyl alcohol or an organic acid such as acetic acid.

Problems solved by technology

However, the hot coating process has a problem that the membrane cannot uniformly be formed on the whole base surface, and the membrane can be formed on the only outer surface of the tube base member.
On the other hand, in the filtering membrane formation process, during drying of the formed membrane, a solvent present in base pores sometimes flows out on a membrane side to cause membrane peeling.
As a result, there is a problem that a defect is generated in the porous membrane formed on the fired base surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic porous membrane and ceramic filter
  • Ceramic porous membrane and ceramic filter
  • Ceramic porous membrane and ceramic filter

Examples

Experimental program
Comparison scheme
Effect test

example 1

(1) Porous Base Member

[0046] A material provided with an alumina membrane having an average pore diameter of 0.2 μm and having a monolith shape (an outer diameter of 30 mm, a cell inner diameter 3 mm×37 cells and a length of 500 mm) was used as a base member. It is to be noted that opposite end portions of the base member were sealed with glass. The average pore diameter of the base member was measured based on an air flow process described in ASTM F306.

(2) Titania Sol Liquid

[0047] Titanium isopropoxide was hydrolyzed in the presence of nitric acid to obtain a titania sol liquid. A sol particle diameter measured by a dynamic optical scattering process was 100 nm.

(3) Titania UF Membrane Formation

[0048] The titania sol liquid was diluted with water to obtain a sol liquid for membrane formation. The liquid was circulated through base cells to come in contact with the cells, whereby the membrane was formed in the cells.

(4) Drying, Firing

[0049] After a sample was dried, the sample...

example 2

[0055] During titania UF preparation of (1) to (4) of Example 1, titania was not fired unlike (4), and used as a base member, and then silica membrane formation of (6) to (9) was performed.

example 3

[0056] During titania UF preparation of (1) to (4) of Example 1, titania was fired at 300° C. in (4), and then silica membrane formation of (6) to (9) was performed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore diameteraaaaaaaaaa
pore diameteraaaaaaaaaa
weight ratioaaaaaaaaaa
Login to View More

Abstract

There are disclosed a ceramic porous membrane formed with less membrane formation times and having less defects, a small and uniform thickness and a high flux, and a ceramic filter. A silica membrane is formed on a titania UF membrane as an ultrafiltration membrane (a UF membrane) formed on a porous base member which is a microfiltration membrane (also referred to as an MF membrane) and having an average pore diameter smaller than that of the porous base member, and the silica membrane has an average pore diameter smaller than that of the titania UF membrane, and does not substantially permeates the titania UF membrane.

Description

BACKGROUND OF THE INVENTION AND RELATED ART [0001] The present invention relates to a ceramic porous membrane and a ceramic filter. More particularly, it relates to a ceramic porous membrane having less defects and having a small and uniform thickness, and a ceramic filter. [0002] Heretofore, various methods of forming a ceramic porous membrane on a porous base member have been known. For example, a hot coating process is known (see Non-Patent Document 1). This is a method of rubbing a tube base member with cloth containing a silica sol to apply the silica sol and thereby form a porous membrane on an outer surface of the heated tube base member. [0003] A method of forming a porous membrane on an inner surface of a porous base member having a tubular shape or a cylindrical lotus-root-like monolith shape by filtering membrane formation is also known (see Patent Document 1). The outer surface of the porous base member is held at a pressure lower than that of an inner surface thereof wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): B01D71/04
CPCB01D67/0048B01D69/12B01D2325/02B01D71/02B01D67/0095B01D71/024B01D2325/0283B01D69/1213B01D71/0213
Inventor ISOMURA, MANABUHISHIKI, TATSUYAWADA, ICHIRO
Owner NGK INSULATORS LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com