Nickel cobalt boron ternary alloys

a ternary alloy and cobalt technology, applied in the field of ternary alloys, can solve the problems of restricted use of chromium (vi) and its compounds in certain applications, and achieve the effects of increasing the bright plating range, and facilitating deposition of metal ions

Inactive Publication Date: 2005-08-11
TASKEM
View PDF10 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

"The present invention provides a method for electroplating a nickel cobalt boron alloy that has a mirror bright deposit and a hardness on par with chrome. The use of brighteners in the electroplating bath facilitates deposition of metal ions at relatively low current densities, resulting in a bright plating range. This allows the nickel cobalt boron alloy to replace electroplated chrome and chromium alloys, providing potential environmental benefits. The method involves providing an electroplating bath, applying a current, and allowing the alloy to form on the cathode. The invention has various applications, such as in the production of decorative and functional coatings."

Problems solved by technology

However, the use of chromium (VI) and its compounds are restricted in certain applications in some areas, primarily in the European Union.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel cobalt boron ternary alloys
  • Nickel cobalt boron ternary alloys
  • Nickel cobalt boron ternary alloys

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0071] The electroplating bath of Comparative Example 1 is prepared except that 0.05 g / L of sodium laurel sulfate as a surfactant, 2.25 g / L of sodium saccharin as a stress reliever, 0.01 g / L of 2-butyne-1,4-diol and 0.01 g / L of propargyl alcohol as brighteners, and 0.10 g / L of 1-(sulfopropyl)pyridinium hydroxide as a leveler are added.

[0072] A metal deposit is produced from the electroplating bath with a surfactant, a stress reducing agent, and brighteners using 2 amp DC current in a mechanically agitated 267 ml Hull cell to determine plate response over a wide plating current density. The electroplating bath using a standard make up requires 6.2 Volts to achieve 2 amps. Plating time is 5 minutes. The type / appearance of the metal plate is shown in FIG. 4. A mirror bright deposit is obtained over at a wide range of current densities as low as about 4 ASF and higher.

example 2

[0073] The electroplating bath of Comparative Example 1 is prepared except that 0.1 g / L of sodium 2-ethylhexyl sulfate as a surfactant, 1 g / L of bisbenzenesulfonimide as a stress reliever, 0.01 g / L of 2-butyne-1,4-diol and 0.02 g / L of propargyl alcohol as brighteners, and 0.08 g / L of (1-sulfo-2-hydroxypropyl)pyridinium hydroxide as a leveler are added.

[0074] A metal deposit is produced from the electroplating bath with a surfactant, a stress reducing agent, and brighteners using 2 amp DC current in a mechanically agitated 267 ml Hull cell to determine plate response over a wide plating current density. Plating time is 5 minutes. The type / appearance of the metal plate is shown in FIG. 4. A mirror bright deposit is obtained over at a wide range of current densities as low as about 4 ASF and higher.

example 3

[0075] The electroplating bath of Example 1 is prepared except that a 100 g / L of sodium sulfate decahydrate is added via the make up. Voltage is lowered to 5 Volts to achieve 2 amps without impacting the type / appearance of the metal plate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
temperatureaaaaaaaaaa
Login to View More

Abstract

Disclosed are methods of electroplating a nickel cobalt boron alloy involving providing an electroplating bath comprising ionic nickel, ionic cobalt, ionic boron, and at least one brightener; and applying a current to the electroplating bath whereby a nickel cobalt boron alloy forms.

Description

FIELD OF THE INVENTION [0001] The present invention generally relates to ternary alloys containing nickel, cobalt, and boron that may be employed in place of chrome and chrome alloys and methods of making the ternary alloys. BACKGROUND OF THE INVENTION [0002] Chromium is steel-gray, lustrous, hard, metallic, and takes a high polish. Chromium is a naturally occurring element present in the environment in several different forms. The most common forms are chromium (0), chromium (III), and chromium (VI). The metal chromium, which is the chromium (0) form, is used for making steel. Chromium (VI) and chromium (III) are often used for chrome plating. Chromium (VI) is used as an anti-corrosion treatment and as an electrical shielding material for certain sheet metals. There are many desirable characteristics associated with chromium plating. [0003] However, the use of chromium (VI) and its compounds are restricted in certain applications in some areas, primarily in the European Union. Broa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): C25D3/56C25D5/18
CPCC25D5/18C25D3/562C25D5/611C25D5/623C25D5/627
Inventor BOKISA, GEORGEECKLES, WILLIAM E.FRISCHAUF, ROBERT E.
Owner TASKEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com