Catalyst for preparing pentafluoroethane, manufacturing method of the catalyst

A technology of pentafluoroethane and trifluoroethane is applied in the field of preparing the catalyst and can solve the problems of low selectivity of HFC-125 and the like

Active Publication Date: 2011-05-25
FOOSUNG CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0020] That is, when the starting material is PCE, the selectivity to HFC-125 is less than 20%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for preparing pentafluoroethane, manufacturing method of the catalyst
  • Catalyst for preparing pentafluoroethane, manufacturing method of the catalyst
  • Catalyst for preparing pentafluoroethane, manufacturing method of the catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Catalysts 1 to 5 for fluorination are based on figure 1 Prepared by the method shown in the steps. exist figure 1 Among them, catalyst 1 is composed of chromium oxide and magnesium oxide, catalyst 2 is composed of chromium oxide and iron oxide, catalyst 3 is composed of chromium oxide and molybdenum oxide, catalyst 4 is composed of chromium oxide and vanadium oxide, and catalyst 5 is composed of chromium oxide and aluminum oxide. composition. Next, a catalyst composed of chromium oxide and magnesium oxide will be described.

[0036] In 1kg chromium(III) nitrate (Cr(NO 3 ) 3 9H2O) was dissolved in distilled water, and 0.391kg of ammonia (NH2O) was added dropwise 4 OH), so that blue-gray chromium hydroxide (Cr(OH) 3 )precipitation. The precipitate was washed well with hot distilled water, filtered and dried at 100°C for 24 hours to obtain solid chromium hydroxide. The chromium hydroxide thus obtained is ground into powder with a ball mill or a mortar, and then hea...

Embodiment 2

[0039] (Preparation of catalyst 2 (chromium oxide-iron oxide catalyst))

[0040] Catalyst 2 is prepared in the same manner as in Example 1, except that iron nitrate [Fe(NO 3 ) 2 ·6H 2 O] instead of magnesium nitrate.

Embodiment 3

[0042] (Preparation of catalyst 3 (chromium oxide-molybdenum oxide catalyst))

[0043] Catalyst 3 is prepared in the same manner as in Example 1, except that ammonium molybdate [(NH 4 ) 6 Mo 7 o 24 ] instead of magnesium nitrate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a chromium oxide catalyst for preparing pentafluoroethane using chloroethane, which comprises heating chromium hydroxide powder at greater than 300 DEG C. to give chromium oxide powder; heating a metal hydroxide selected from magnesium hydroxide, iron hydroxide, molybdenum hydroxide, vanadium hydroxide or aluminum hydroxide at 300 DEG C. or less to give a metal oxide powder e.g. magnesium oxide, iron oxide, molybdenum oxide, vanadium oxide or aluminum oxide; mixing the chromium oxide powder (85-99.5 wt.%) with the metallic oxide powder (0.5-15 wt.%); granulating the obtained mixture; calcining the granules at 200-300 DEG C. under nitrogen gas medium; and calcining the obtained granules at 300-320 DEG C. under a gas mixture comprising nitrogen and hydrogen fluoride (HF) and then at 320-380 DEG C. using HF gas. According to the invention, the fluorinating catalyst can be efficiently to prepare HFC-125 using chloroethane as a material and high yield is achieved.

Description

technical field [0001] The present invention generally relates to a catalyst for the preparation of pentafluoroethane and a method for its preparation. Specifically, the present invention relates to a kind of catalyst, it is applicable to by perchloroethane (C 2 Cl 4 , hereinafter referred to as "PCE") or 1,1-dichloro-2,2,2-trifluoroethane (CHCl 2 CF 3 , hereinafter referred to as "HCFC-123") reacts with HF to produce pentafluoroethane (CF 3 CHF 2 , hereinafter referred to as "HFC-125"), and relates to a method for preparing the catalyst. Background technique [0002] Typically, HFC-125 does not contain chlorine in its molecules, so it has little impact on global warming and ozone depletion. HFC-125 is an alternative raw material for chlorofluorocarbons or hydrochlorofluorocarbons used as traditional refrigerants, blowing agents or propellants, and it is combined with difluoromethane (CH 2 f 2 , hereinafter referred to as "HFC-32") can be used as a raw material for m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/26B01J37/04B01J37/08C07C19/08C07C17/00
CPCB01J37/04B01J23/26B01J37/26B01J23/28B01J37/031B01J23/862C07C17/206B01J37/0009C07C19/08B01J23/24B01J23/86B01J23/88
Inventor 张香子金大铉金哲虎赵荣救李定殷金荣守饭久保祐一
Owner FOOSUNG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap