Method for producing copper alloy contact wire with excellent comprehensive performance

A comprehensive performance, copper alloy technology, used in cable/conductor manufacturing, electrical components, circuits, etc., can solve problems such as brittleness of contact wires, and achieve the effects of good plasticity, improved grain size and less impurities

Active Publication Date: 2007-03-21
邢台鑫晖铜业特种线材有限公司
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cuprous oxide formed by oxygen and copper forms a brittle structure between copper grain boundaries, which in turn causes brittle fracture of the contact wire during processing or use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing copper alloy contact wire with excellent comprehensive performance
  • Method for producing copper alloy contact wire with excellent comprehensive performance
  • Method for producing copper alloy contact wire with excellent comprehensive performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The contact wire raw material of the method of the present invention is a ternary copper alloy in which a small amount of magnesium and tin are added to a copper matrix or a quaternary copper alloy in which a small amount of magnesium, tin and rare earth elements are added. Among them, melting magnesium and tin into copper can form a solid solution with copper, aggravate lattice distortion, and play a composite strengthening role. Adding rare earth elements can not only refine grains, increase strength, eliminate or reduce composition segregation, but also improve the electrical conductivity of the alloy. By strictly controlling the addition amount and ratio of magnesium, tin, and rare earth elements, it is possible to improve the strength and electrical conductivity of the material, and at the same time make the alloy material have a high toughness index. Tests have shown that the strength of the above-mentioned ternary or quaternary alloys after upward continuous cast...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is concerned with the copper alloy touching line and the preparation method with choiceness integrative performance that uses to improve the using performance of the touching line of the cable technology field. It is: the copper alloy is as the material that the material melts with the following percentage weight, magnesium 0.05~ 0.35%, stannum 0.35~0.05%, total quantity of impurity is smaller than 0.10%, remainder is copper; the above material makes to be the touching line by the steps of smelting, heat preservation, casting pole, pressing, cold rolling, molding rolling. The index of the touching line achieves and overruns the international similar product level, such as the intensity, the conductivity, the elongation ratio, the reverse, repeating bending, convolution.

Description

technical field [0001] The invention relates to a method for preparing catenary conductors used in electrified railways, belonging to the technical field of electric cables. Background technique [0002] In recent years, the operating mileage of electrified railways has developed rapidly. Taking my country as an example, the electrification rate of railways is close to 30%. The general development trend of electrified railways has shifted from mountain fortresses to plain trunk lines, from light loads to heavy loads, and from low speeds to high speeds. From passenger and cargo collinear to passenger and cargo diversion. With the rapid development of electrified railway, the performance requirements of catenary wire, the key component required, are constantly increasing, that is, high strength, high electrical conductivity, weather resistance, wear resistance, good toughness and current-taking effect are required. For this reason, experts in the industry have done a lot of re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01B13/00C22C9/00C22C1/02B22D11/00B21C23/00B21C1/00
Inventor 张进东韩士恩王振兴王汉裴
Owner 邢台鑫晖铜业特种线材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com