Environment protection colour polyurethane paint and preparation process thereof

A preparation process, polyurethane technology, applied in polyurea/polyurethane coatings, antifouling/underwater coatings, coatings, etc., can solve the problems of cumbersome operation, high toxicity, poor performance, etc., and achieve strong adhesion and adhesion. The effect of relay, strong deformation adaptability and excellent low temperature performance

Inactive Publication Date: 2006-06-28
何霖
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polyurethane waterproof coatings that are still on the market use asphalt instead of coal tar as the raw material, but they need to be melted at high temperature in the production process, and then mixed with organic solvents such as benzene after a period of cooling. The process is backward and the operation is very cumbersome. , and the performance is poor, the service life is short, and the leakage phenomenon of the building is quite common.
In addition, asphalt is recognized as poisonous in the world, and the benzene used in processing is a strong carcinogen, which is very toxic, causing great harm to the human body and polluting the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: a kind of environment-friendly type colored polyurethane waterproof coating, it comprises A component and B component, by A component: the ratio of B component=1: 2 is blended and made, and wherein, A component is made of The raw material composition of following weight ratio:

[0031] Polyether 3010 220

[0032] Polyether 204 55

[0033] Polyether 210 100

[0034] Isocyanate (TDI) 100;

[0035] Component B consists of raw materials in the following weight ratios:

[0036] Dibutyl fat 110

[0037] film card 20

[0038] Heavy calcium 280

[0039] Organic bentonite 12

[0040] Color pigment 0.8.

[0041] Preparation process: The preparation process of component A:

[0042] (1) Empty still operation, feed steam 15 minutes simultaneously, steam pressure is 0.2Mpa;

[0043] (2) Turn off the steam, add polyether 210, polyether 3010, and polyether 204 in order according to the above weight ratio, and stir for 3 minutes;

[0044] (3) drop in isocyanate ...

Embodiment 2

[0053] Embodiment 2: a kind of environment-friendly type colored polyurethane waterproof paint, it comprises A component and B component, by A component: the ratio of B component=1: 1 is blended and made, and wherein, A component is made of The raw material composition of following weight ratio:

[0054] Polyether 3010 245

[0055] Polyether 204 65

[0056] Polyether 210 120

[0057] Isocyanate (TDI) 130;

[0058] Component B consists of raw materials in the following weight ratios:

[0059] Dibutyl fat 150

[0060] Film card 40

[0061] heavy calcium 400

[0062] Organic Bentonite 20

[0063] color pigment 1

[0064] Preparation process: The preparation process of component A:

[0065] (1) Empty still operation, feed steam 15 minutes simultaneously, steam pressure is 0.5Mpa;

[0066] (2) Turn off the steam, add polyether 210, polyether 3010, polyether 204 in order according to the above weight ratio, and stir for 8 minutes;

[0067] (3) drop in isocyanate (TDI), an...

Embodiment 3

[0076] Embodiment 3: a kind of environment-friendly color polyurethane waterproof paint, it comprises A component and B component, by A component: the ratio of B component=1: 2 is blended and made, and wherein, A component is made of The raw material composition of following weight ratio:

[0077] Polyether 3010 240.5

[0078] Polyether 204 50.1

[0079] Polyether 210 104

[0080] Isocyanate (TDI) 100.7;

[0081] Component B consists of raw materials in the following weight ratios:

[0082] Dibutyl fat 140

[0083] film card 20

[0084] Heavy calcium 280

[0085] Organic bentonite 12

[0086] Color pigment 0.8.

[0087] Preparation Process:

[0088] Preparation process of component A:

[0089] (1) Empty still operation, feed steam 10 minutes simultaneously, steam pressure is 0.4Mpa;

[0090] (2) Turn off the steam, add polyether 210, polyether 3010, and polyether 204 in the order of the above parts by weight, and stir for 5 minutes;

[0091] (3) drop in isocyanate (T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses environmental protection color polyurethane water proofing paint. It includes A and B components. Their rate is 1:1-2.5. The A component includes polyether 3010, 204, 210, TDI. The B component includes DOP, film card, coarse whiting, organic alta mud, and color pigment. Its manufacturing technology includes A and B component manufacturing technologies. It has the advantages of environmental protection, strong adhesive force, asepsis, no pollution, water proof, big tensile strength, heat and clod resistance, strong caking power with many materials; and it can be achieved by cold working.

Description

technical field [0001] The invention relates to a waterproof coating and its preparation process, in particular to an environment-friendly colored polyurethane waterproof coating and its preparation process. technical background [0002] Polyurethane waterproof coatings are widely used waterproof materials at present. The first generation of polyurethane waterproof coatings is made of polyurethane and coal tar as raw materials, but because coal tar will cause poison to the human body, in It was banned in my country in 2000. The polyurethane waterproof coatings that are still on the market use asphalt instead of coal tar as the raw material. However, during the production process, it needs to be melted at high temperature, and then mixed with organic solvents such as benzene after a period of cooling. The process is backward and the operation is very cumbersome. , and poor performance, short service life, resulting in building leakage is quite common. In addition, asphalt is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08C09D5/16
Inventor 何霖
Owner 何霖
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com