Metallocene polyolefin tenacity-increased profax resin composition

A metallocene polyolefin and polypropylene resin technology, which is applied in the field of metallocene polyolefin toughened polypropylene resin composition, can solve the problems of complex process, poor material fluidity, high cost, etc., and achieve good toughness, low cost, Good processing performance

Inactive Publication Date: 2006-05-03
SHANGHAI SUNNY
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has high cost, complex process and poor fluidity of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 and 2

[0031] Homopolypropylene and copolymerized polypropylene resin imported from South Korea are used for polypropylene, MPE imported from Japan and POE from the United States are used for metallocene polyolefin, CMG9801 from Shanghai Rizhisheng Company is used as a compatibilizer, and 168 from CIBA Company is used as an antioxidant and 1010, the lubricant uses calcium stearate.

[0032] raw material name

Proportion 1 (wt%)

Proportion 2 (wt%)

Copolymer polypropylene

69

50

Homopolypropylene

--

24

MPE

25

--

POE

--

20

CMG9801

5

5

1010 / 168(1∶1)

0.5

0.5

Calcium stearate

0.5

0.5

[0033] Put all the raw material components in proportion into a high mixer and mix for 4 minutes, discharge, and then extrude and granulate with a screw extruder, the processing temperature is 200°C, and the screw speed is 250 rpm.

[0034] Sample 1, sample 2 prepar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a metallocene polyolefin tenacity-increased profax resin composition comprising raw materials of the following constituents (by weight proportion): polypropylene 60-85%, metallocene polyolefine 5-30%, compatibilzer 5-10%, anti-oxidant 0.1-1% and lubricating agent 0.1-0.5%.

Description

technical field [0001] The invention relates to a metallocene polyolefin toughened polypropylene resin composition, which can be used to manufacture auto parts and electrical and electronic components, and belongs to the technical field of polypropylene modification. Background technique [0002] Polypropylene (PP) is cheap, light, corrosion-resistant, has good processability, good mechanical balance, wide application range, and has the best heat resistance among general-purpose resins. Polypropylene is widely used in the automotive industry, and its engineering tendency is very obvious. However, the toughness of polypropylene, especially the low-temperature impact toughness, is very poor, which limits its use. [0003] There are many ways to improve the toughness of polypropylene. The most researched is ethylene-propylene rubber toughened polypropylene, and HDPE and ethylene-propylene rubber synergistically toughened polypropylene. The dynamic vulcanization technology devel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12B29C47/36C08K5/11
Inventor 辛敏琦陈晓东杨涛唐倬吴小龙
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com