Internal lining casting material of industrial reaction furnace and lining-up method

A pouring material and working lining technology, applied in the direction of lining repair, etc., can solve the problems of poor air erosion resistance, increased demolition workload, complex brick shape, etc., to achieve strong air erosion resistance, simple construction method, and convenient construction Effect

Inactive Publication Date: 2005-12-28
西安秦翔科技股份有限公司
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The innermost working lining of the carbon black reaction furnace lining directly contacts the high-temperature airflow. The existing technology mainly uses chrome corundum bricks as the innermost working lining. 4 months, and when dismantling, the middle layer with good thermal insulation performance and the outer thermal insulation layer with light heat insulation should also be removed at the same time, which will increase the workload of dismantling and increase the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]Including the lightweight heat-insulating outer insulation layer material of aluminum oxide hollow balls, the high-strength and high-aluminum middle layer material with good heat insulation performance, and the inner layer working lining casting material also includes 75% of fused dense corundum according to the mass ratio. Fused zirconia mullite 4%, chromium oxide 4%, zircon superfine powder 4%, aluminum oxide fine powder 9%, calcium aluminate cement 4%. The particle size gradation mass ratio of the working lining pouring material is as follows: the dense corundum with a particle size of 5-8mm should account for 12% of the total mass ratio, and the dense corundum with a particle size of 3-5mm should account for 12% of the total mass ratio. Dense corundum with a particle size of ~3mm should account for 19% of the total mass ratio, dense corundum with a particle size of 0~1mm should account for 25% of the total mass ratio, and dense corundum with a particle size of 50 ≤3μm...

Embodiment 2

[0045] Including the lightweight heat-insulating outer insulation layer material of alumina hollow spheres, the high-strength and high-aluminum middle layer material with good heat insulation performance, and the inner layer working lining casting material also includes 77% of fused dense corundum according to the mass ratio. Fused zirconia mullite 3%, chromium oxide 4%, zircon superfine powder 3%, aluminum oxide micropowder 7%, calcium aluminate cement 6%; The ratio is: dense corundum with a particle size of 5-8mm should account for 12% of the total mass ratio, dense corundum with a particle size of 3-5mm should account for 12% of the total mass ratio, and dense corundum with a particle size of 1-3mm should account for 20% of the total mass ratio. %, 0-1mm particle size dense corundum should account for 26% of the total mass ratio, and 50 ≤3μm particle size is 3%, aluminum oxide powder D 50 ≤5μm particle size is 7%, calcium aluminate cement is 6%.

[0046] A furnace lining m...

Embodiment 3

[0053] Including the lightweight heat-insulating outer insulation layer material of alumina hollow spheres, the high-strength and high-aluminum middle layer material with good heat insulation performance, and the inner layer working lining casting material also includes 77% of fused dense corundum according to the mass ratio. Fused zirconia mullite 5%, chromium oxide 3%, zircon superfine powder 4%, aluminum oxide micropowder 6%, calcium aluminate cement 5%; The ratio is: dense corundum with a particle size of 5-8mm should account for 14% of the total mass ratio, dense corundum with a particle size of 3-5mm should account for 14% of the total mass ratio, and dense corundum with a particle size of 1-3mm should account for 17% of the total mass ratio. %, 0-1mm particle size dense corundum should account for 25% of the total mass ratio, 50 ≤3μm particle size is 4%, aluminum oxide powder D 50 ≤5μm particle size is 6%, calcium aluminate cement is 5%.

[0054] A furnace lining metho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A casting material for the internal working liner of industrial reduction furnace is prepared from aluminium oxide for insulating layer, high-Al material for intermediate layer and the compact corundum, zirconium mullite, chromium oxide, superfine zircon powder, Al2O3 powder and calcium aluminate cement through weighing raw materials except calcium aluminate cement, stirring, loading in bag for future use, casting external insulating layer, casting mediate layer and casting working liner, which includes proportionally mixing said mixture with calcium aluminate cement, adding water, stirring, moulding, vibrating, demoulding, natural curing and baking.

Description

technical field [0001] The invention relates to an industrial reaction furnace lining refractory material, which is especially suitable for the inner layer working lining pouring material of an oil furnace method carbon black furnace and the furnace lining method. Background technique [0002] Carbon black is one of the indispensable important chemical raw materials in the modern national economy. Among them, 90% are used in the rubber industry, and the rest are used in ink, paint, plastic, synthetic leather and other fields. Carbon black is of great significance to the development of national transportation, the realization of agricultural mechanization, and the improvement of people's material and spiritual civilization. [0003] Oil furnace carbon black is the most important production method in the contemporary carbon black industry. The lining of carbon black reaction furnaces in my country generally adopts a three-layer structure: the innermost layer with good high te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F27D1/16
Inventor 王臻高云琴刘振平
Owner 西安秦翔科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com