Stainless steel slagging and degassing refining agent

A stainless steel and refining agent technology, which is applied in the field of stainless steel slagging and degassing refining agents, can solve the problems of not being able to reduce the subcutaneous black spots of workpieces, unsatisfactory heat preservation and degassing effects, and inconspicuous use effects, etc., to achieve the reduction of subcutaneous black spots, heat preservation Good degassing effect and avoid heat loss

Inactive Publication Date: 2005-09-07
张华静
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reasons are: 1. The use effect is not obvious, and the subcutaneous black spots of the workpiece, black spots and pitting on the surface of the polished piece cannot be reduced, thereby greatly reducing the yield of the product; 2. The effect of heat preservation and degassing is not ideal, and the slag removal Trouble, there are still a lot of slag inclusions; 3. The furnace wall is severely eroded. Since the furnace lining is made of magnesia (MgO), the molten steel rolls in the furnace lining, which will wash the furnace lining, and a small amount of magnesia will fall into the molten steel, causing the furnace lining Under normal circumstances, a furnace lining can be used for 150-180 times, but after using slagging agent, it can only be used within 100 times

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] In the embodiment of the present invention, take dolomite (CaMg(CO3) as: 70, aluminum powder (Al2O3) as: 15, fluorite (CaF2) as: 15, and make slagging and degassing refining agent by mixing uniformly at room temperature , weigh bags as required, and pack the finished product into storage. Dolomite and fluorite are in powder form.

[0014] The method of using the slagging and degassing refining agent prepared from the formula in this example is as follows: it is used in a large steel factory. Put 0.3-0.5 slagging and degassing refining agent of molten steel weight on the bottom of the furnace. When the temperature measurement of the molten steel reaches the temperature required by the smelting process, adjust it upwards by 20-30°C, then turn off the power and let it stand for a period of time. Slightly shake the molten steel to make the slag float up as soon as possible. At this time, do not do any slag removal action (that is, do not sprinkle slag remover), if the temp...

Embodiment 2

[0017] In the embodiment of the present invention, take dolomite (CaMg(CO3) as: 75, aluminum powder (Al2O3) as: 12.5, fluorite (CaF2) as: 10.5, mix and stir at room temperature to make slagging and degassing refining agent , carry out weighing bag as required, and finished product packs storage.Adopt the slagging and degassing refining agent that formula is made in the present embodiment, and adopt the method of use in the embodiment one, use in large-scale steel mill and can reach and embodiment The same use effect as the first one, the pure molten steel improves the overall performance of the product.

Embodiment 3

[0019] In the embodiment of the present invention, take dolomite (CaMg(CO3) as: 80, aluminum powder (Al2O3) as: 10, fluorite (CaF2) as: 6, and make slagging and degassing refining agent by mixing uniformly at room temperature , carry out weighing and bagging as required, and the finished product is packaged and stored in the warehouse. The slagging and degassing refining agent made by the formula in this embodiment can also make the molten steel cleaner and have better performance after being used in foundries.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention relates to a rustless steel slag-forming and degassing agent, which is specifically a casting accessory material to clean up rustless steel molten steel surface and improve rustless steel quality, and belong to metal surface treatment technique area in foundry industry. This agent mainly comprises 70-80 wt% of dolomite, 10-15 wt% of aluminum dust and 6-15 wt% of fluor. The components are mixed completely in normal temperature and packed to completed product. This invention possesses the properties of increasing life of brasque to more than 200 times; improving slag-forming ability to decrease endermic points, decrease surface points and pocks of buffing surface and increase rate of finished products and improving thermal insulation and degasification by floating constantly on the surface of molten steel, in which molten steel is prevented to contact with air and oxygenized, suck in hydrogen and nitrogen and interfused with foreign substance, so as to ensure cleaner molten steel higher property.

Description

technical field [0001] The invention relates to a stainless steel slagging and degassing refining agent, in particular to a casting auxiliary material used for purifying molten stainless steel and improving the quality of stainless steel, belonging to the technical field of foundry metallurgy. Background technique [0002] Before the present invention was made, in the prior art, the following three schemes were usually adopted for the slagging and degassing refining agent for molten steel surface treatment in the stainless steel foundry industry: 1, adopt lime (CaO), fluorite (CaF ) to mix and 2. It is made by mixing lime (CaO), magnesium oxide (MgO) and fluorite (CaF2); 3. It is made by mixing lime (CaO), fluorite (CaF2) and aluminum powder (Al2O3). These slag-forming and degassing refining agents are mainly used in large steel mills, and less used in foundries. The main reasons are: 1. The use effect is not obvious, and the subcutaneous black spots of the workpiece, black...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D1/00C21C7/04
Inventor 张华静
Owner 张华静
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap