Environmental protection type nano material modified latex paint for internal wall

A latex paint and nano-material technology, applied in latex paint, coating, etc., can solve the problems of no decomposition of harmful organic matter, high VOC content, etc., achieve low film forming temperature, reduce harmful substances, and good photocatalytic effect

Inactive Publication Date: 2005-06-29
CNOOC CHANGZHOU PAINT & COATINGS IND RES INST
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coatings involved in the above-mentioned patents have relatively high VOC content, about 100g / l, and the coating films formed by these coatings do not have the function of decomposing common harmful organic substances in the room.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] First, add 18.0 parts (parts by mass, the same below) of deionized water, 0.6 parts of wetting and dispersing agent, 2.0 parts of nano-silica powder, 20.0 parts of titanium dioxide, 20.0 parts of precipitated barium sulfate, and 10.0 parts of ultrafine talc in the container Powder and 0.1 part of defoamer, mixed evenly at high speed, then grinded in a sand mill until the fineness is less than 50 microns, then added 35.0 parts of modified acrylic emulsion, 0.1 part of defoamer, 0.3 parts of thickener, 0.2 parts of leveling agent part, 0.3 part of the composite slurry, and adjust the pH value to 8-9, and the finished product can be obtained after stirring evenly. The product quality is excellent, and the performance test results are shown in Table 2.

Embodiment 2

[0024] The preparation method is the same as in Example 1, and its components (parts by mass) are: 24.0 deionized water, 0.8 wetting and dispersing agent, 1.0 nanometer silicon dioxide powder, 10.0 titanium dioxide, 30.0 precipitated barium sulfate, 15.0 ultrafine talcum powder , defoamer 0.2, modified acrylic emulsion 25.0, thickener 0.2, leveling agent 0.2, composite slurry 0.1. The cost of the coating is relatively low, and the properties of the coating are good after testing, and the properties of the coating are shown in Table 2.

[0025] Test items

[0026] As can be seen from table 2 test results, interior wall latex paint of the present invention (embodiment 1 and 2), its film performance (water resistance, scrub resistance) is better than the standard of national excellent product and has good antibacterial property, Anti-mildew, anti-corrosion and the function of removing formaldehyde and toluene. The VOC content of the paint is lower than 5g / l, which is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
minimum film forming temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relate to a nm material modified latex coating for inside wall with environmental protection,comprises of the following components:water 18-24,dispersant 0.4-1.0;nm silicon dioxide powder 1.0-3.0;deposit barium sulfate 20-30;talcum powder 10-15;titanium dioxide 10-20;antifoaming agent 0.1-0.2;modified crylic acid 25-35;zinc oxide and titanium oxide compound finishing mixture 0.1-0.3;thickener 0.3-0.4; 0.15-0.30;and pH regulator. The modified crylic acid has the lowest temperature to form film being 0-5deg.C and glassifying temperature being 10-15deg.C, the coating contains 6 organic compound lower than 5g / l,is suitable for decoration and protection for inside wall.

Description

technical field [0001] The invention relates to an environment-friendly nano-material modified interior wall latex paint. Background technique [0002] Traditional interior wall latex paints need to add a large amount of organic solvents such as antifreeze and film-forming aids when preparing the paint, resulting in a high content of volatile organic compounds (VOC) in the paint; in addition, in order to prevent corrosion of the paint during storage Deterioration and mildew of the coating film, a large amount of organic anti-mold fungicides harmful to the human body need to be added to the coating, which not only directly affects the physical and mental health of the occupants, but also has timeliness. After a period of time, it loses the anti-mold Mildew effect. In interior decoration, since wooden furniture, plywood and other woods and solvent-based wood paints will release a large amount of organic volatiles such as formaldehyde and / or benzene that are highly toxic to th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/02C09D133/02
Inventor 殷武孔志元张保利朱柯史立平何庆迪
Owner CNOOC CHANGZHOU PAINT & COATINGS IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com