Multi constituent niobate lead-free piezoelectric ceramics

A lead-free piezoelectric, multi-component technology, applied in ceramics, piezoelectric/electrostrictive/magnetostrictive devices, circuits, etc., to achieve excellent piezoelectric ferroelectric performance and good process stability

Inactive Publication Date: 2004-07-14
SICHUAN UNIV
View PDF8 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the work in this area is still in the research and exploration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi constituent niobate lead-free piezoelectric ceramics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0012] The following are the formulations of several piezoelectric ceramic embodiments and the measured piezoelectric performance parameters:

[0013] One, (Li 0.04 Na 0.4 K 0.56 )NbO 3 (98wt%); add ErMnO 3 (1wt%), YMnO 3 (1wt%) form lead-free piezoelectric ceramics, the performance of the prepared piezoelectric ceramics is:

[0014] d 33 (pC / N)ε 33 / ε 0 k p (%) Poisson's ratio

[0015] 150 360 27.3 0.266

[0016] Two, (Li 0.07 Na 0.6 K 0.33 )Nb 0.7 Sb 0.1 Ta 0.2 o 3 (98%); add YbMnO 3 (2wt%) form lead-free piezoelectric ceramics, the performance of prepared piezoelectric ceramics is:

[0017] d 33 (pC / N)ε 33 / ε 0 k p (%) Poisson's ratio

[0018] 120 450 23.2 0.286

[0019] Three, (Li 0.1 Na 0.55 K 0.35 )Nb 0.9 Sb 0.1 o 3 (96%); add ErMnO 3 (2wt%), DyMnO 3 (2wt%) form lead-free piezoelectric ceramics, the performance of prepared piezoelectric ceramics is:

[0020] d 33 (pC / N)ε 33 / ε 0 k p (%) Poisson's ratio

[0021]135 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to environment concordant piezoelectric ceramic. The lead-free piezoelectric ceramic of the present invention may be expressed in the general expression of (LixNayK1-x-y)(Nb1-zRz)O3+aLMnO3, where, x is 0-0.3, y 0-1, (x+y) is 0-1, z 0-0.4, a is the weight percentage of LMnO3, 0-15 wt%, R is Ta and / or Sb, L is RE element, such as Y, Er, Ho, Dy , Tm, etc. The piezoelectric ceramic has d33 up to 150 pC / N and kp up to 27.0 %, and may be prepared with industrial material and through traditional piezoelectric ceramic process.

Description

1. Technical field [0001] The invention relates to a class of multi-component niobate-based lead-free piezoelectric ceramics, which belongs to the field of environment-harmonic piezoelectric ceramic materials. 2. Background technology [0002] Since the discovery of the piezoelectricity of barium titanate ceramics in the mid-1940s, the research and development of piezoelectric ceramics has been very active. Piezoelectric ceramics and components made of piezoelectric ceramics have been widely used in industries, especially in the information industry. field. Lead zirconate titanate (Pb(Ti, Zr)O 3 ) as the representative lead-based binary system and lead zirconate titanate (Pb(Ti, Zr)O 3 ) as the base material, adding the third component, such as lead magnesium niobate (Pb(Mg 1 / 3 Nb 2 / 3 )O 3 ) represented by lead-based ternary piezoelectric ceramic materials have excellent piezoelectric ferroelectric properties and high Curie temperature. At present, the vast majority of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/495H01B3/12H01L41/187
Inventor 肖定全赁敦敏朱建国余萍鄢洪建张文
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com