Leadless easy cutted brass ally material and its manufacturing method

A technology of brass alloy and manufacturing method, applied in the field of brass alloy, can solve problems such as dezincification corrosion, achieve the effects of improving corrosion resistance, improving cutting performance and plating resistance, and compensating for embrittlement effect

Inactive Publication Date: 2003-12-17
SAN ETSU METALS
View PDF0 Cites 73 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, when used as a part in contact with water, there is a problem of dezincification corrosion, so dezincification-resistant brass alloys have been increasingly used in recent years.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The embodiment is to hot extrude (750° C.) the ingot (cylindrical shape with an outer diameter of 60 mm and a length of 200 mm) of the composition in Table 1 into a round bar with an outer diameter of 16 mm, carry out heat treatment at 580° C. for 4 hours, and use 50° C. / hour Cooling rate Furnace cold. Then carry out cold drawing to make a 15mm round bar. The comparative alloy material (Table 2) was also processed and formed in the same way.

[0033] Sample No.

Cu

Zn

Bi

Al

sn

P

Pb

Remark

1

61.14

Bal

1.86

0.02

0.75

0.05

0.05

2

61.48

Bal

1.82

0.01

0.97

0.08

0.09

3

61.20

Bal

2.05

0.03

0.55

0.09

0.05

4

60.21

Bal

1.80

0.04

0.89

0.04

0.06

5

61.26

Bal

1.86

0.02

0.82

0.06

0.05

6

61....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An easily cutted lead-free brass alloy is prepared from Cu (60-62 wt.%), Bi (0.5-2.2), Al (0.01-0.1), Sn (0.5-1.6), P (0.04-0.15) and Zn (rest) through heat treating at 460-600 deg.C for 30 min-4 hr, and slow cooling at speed lower than 70 deg.C / hr.

Description

technical field [0001] The invention relates to a lead-free brass alloy, and relates to a lead-free free-cutting brass alloy material with excellent cutting performance, corrosion resistance, thermal processing performance and mechanical performance and its manufacturing method. Background technique [0002] Examples of brass alloys excellent in machinability include "JIS H3250 C3601", "JIS H3250 C3604", and "JIS H3250 C3771". These brass alloys ensure cutting performance by containing 1.0 to 3.7% by weight of lead. [0003] Lead-containing brass alloy materials are currently used as structural materials for many products (such as faucet fittings for general piping, valve stems, etc.) due to their excellent cutting performance. In addition, when used as a part in contact with water, there is a problem of dezincification corrosion, and for this reason, dezincification-resistant brass alloys have been increasingly used in recent years. [0004] As a conventional dezincificat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C9/00
Inventor 钓谷宏行
Owner SAN ETSU METALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com