Method for mfg. hot rolled steel plate possessing superfine crystal grains and hot rolled steel plate produced

A technology of a hot-rolled steel sheet and a production method, which is applied in the field of hot-rolled steel sheet to achieve the effects of easy control, simple chemical composition and high elongation

Inactive Publication Date: 2003-07-23
攀枝花钢铁有限责任公司钢铁研究院 +1
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the deficiency that existing production technology cannot use carbon steel with low carbon and low manganese content to obtain ultra-fine-grained ferrite and pearlitic hot-rolled steel plates on traditional hot continuous rolling mills, the present invention provides a Production method of low-carbon low-manganese content carbon steel hot-rolled steel plate with ultra-fine-grained ferrite and pearlite structure and low-carbon low-manganese content carbon steel hot-rolled steel plate on traditional hot rolling mill

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for mfg. hot rolled steel plate possessing superfine crystal grains and hot rolled steel plate produced
  • Method for mfg. hot rolled steel plate possessing superfine crystal grains and hot rolled steel plate produced

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] Embodiment: the production method of the hot-rolled steel plate with ultra-fine crystal grain is that carbon steel, especially the carbon steel with low carbon and low manganese content, is poured into 200 * (800~1200) * 5500mm continuous casting method with conventional continuous casting method Casting slabs, the continuous casting slabs are heated to 1200-1230°C in the heating furnace, and the heated continuous casting slabs are sent to Roll on the 1450mm hot rolling mill. Rough rolling adopts eight-pass rolling, and the rolling temperature is 950-1100°C. After the rough rolling, the intermediate slab enters the finish rolling mill for finish rolling, and the temperature at the entrance of the finish rolling mill is controlled to be 870-900°C. Finish rolling adopts six rolling passes, the reduction of the first pass of finish rolling is 13-16mm, the reduction of the second pass of finish rolling is 8-10mm, and the reduction of the third pass is 5-7mm , through the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

A technology for manufacturing hot-rolled steel plate with superfine grains is disclosed. The said steel plate contains C (0.1-0.16 wt.%), Si (0.12-0.3 wt.%), Mn (0.45-0.65 wt.%), P (0-0.020 wt.%) and S (0-0.015 wt.%). Its technological steps include casing, heating to 1200-1230 deg.c, coarse rolling, and three-pass fine rolling. Its advantages are superfine crystal grain (3-6 microns), excellentproperties and simple chemical components.

Description

technical field [0001] The invention relates to a hot-rolled steel plate and a production method thereof, in particular to a production method of a hot-rolled steel plate with ultra-fine grains and the produced hot-rolled steel plate. Background technique [0002] Grain refinement of steel is the only method that can simultaneously improve strength and toughness. In recent years, countries around the world are constantly exploring methods of grain refinement. At present, the minimum ferrite grain size of carbon steel produced industrially on traditional hot rolling mills is 20 μm, and its tensile strength is 400 MPa. Countries such as South Korea and Japan have studied the method of refining the ferrite grain size of low-carbon manganese steel to 1 μm under laboratory conditions. Domestic steel mills have industrially produced ferrite and high-manganese steel components. Hot rolled steel plate with bainite structure. However, under the conditions of large-scale industrial ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/26C21D8/00C22C38/00
Inventor 宋立秋侯豁然左军王义成张开华程兴德刘清友张开坚董瀚
Owner 攀枝花钢铁有限责任公司钢铁研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More