Non-corrosive solder for soldering stainless iron and aluminium

A technology of aluminum brazing and stainless iron, applied in the direction of welding medium, welding equipment, welding/cutting medium/material, etc., can solve the problem of low qualified rate of brazing

Inactive Publication Date: 2002-02-27
GUANGZHOU RES INST OF NON FERROUS METALS
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The qualified rate of brazing is very low, only about 60%, it is impossible to be used for industrial production in this industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] According to weight percentage, take 95.0% of potassium fluoroaluminate eutectic, 3.00% of zinc fluoride, 0.5% of copper fluoride, and 1.5% of tin fluoride, and then ball mill to 200 mesh in a ball mill after mixing. The measured ultimate tensile strength is 29N / mm 2 .

Embodiment 2

[0012] The same as in Example 1. Take 95.0% of potassium fluoroaluminate eutectic, 4.0% of zinc fluoride, 0.2% of copper fluoride, and 0.8% of tin fluoride. The measured ultimate tensile strength is 32N / mm 2 .

Embodiment 3

[0014] The same as in Example 1. Take 97.5% of potassium fluoroaluminate eutectic, 1.2% of zinc fluoride, 0.4% of copper fluoride, 0.6% of tin fluoride, and 0.3% of cadmium fluoride. The measured ultimate tensile strength is 48N / mm 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Ultimate tensile strengthaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a brazing flux for brazing metal, its composition includes (wt%) KAlF4+K3AlF6 cocrystal body 95.0-97.5, zinc fluoride 1.5-4.0, copper fluoride 0.2-0.5, tin fluoride 0.6-1.5 and cadmium fluoride 0.1-0.5. Said brazing flux is used for brazing stainless iron-aluminium.

Description

Technical field [0001] The invention relates to a flux for brazing of metals, in particular to a non-corrosive flux for brazing of different metals. Background technique [0002] The fluxes for stainless steel-aluminum brazing currently available on the market are potassium tetrafluoroaluminate + potassium hexafluoroaluminate (KAlF) 4+ K 3 AlF 6 ) Eutectic, successfully used for stainless steel-aluminum composite brazing, and the brazing qualification rate is greater than 99.9%. However, this flux is not suitable for stainless iron-aluminum welding. Taking potassium fluoroaluminate eutectic solder and silicon-aluminum eutectic solder as examples, the tensile strength of the stainless iron-aluminum welded is relatively low. The qualified rate of brazing is very low, only about 60%, and it is impossible to be used in industrial production in this industry. Summary of the invention [0003] The object of the present invention is to provide a non-corrosive flux for stainless iron-al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/362
Inventor 陈志祥曾燕蔡志红蔡沛沛黄齐博
Owner GUANGZHOU RES INST OF NON FERROUS METALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com