Polyurethane microporous elastic body production method

A microcellular elastomer and polyurethane technology, applied in the field of polyurethane microcellular elastomer preparation, can solve the problems of high production and equipment costs, long in-mold time, poor product technology and material performance, and achieve fast curing and fluidity Good, optimize the effect of physical and mechanical properties

Inactive Publication Date: 2007-05-09
上海凯众聚氨酯有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the above-mentioned deficiencies in the prior art, and propose a preparation method of polyurethane microporous elastomer to solve the problems of long time in the mold, poor product technology and material performance, and high production and equipment costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Polycaprolactone with a molecular weight of 2000 and diphenylmethane diisocyanate (MDI) were reacted at 80° C. for 2 hours to obtain an isocyanate-terminated prepolymer with an -NCO content of 20 wt %. The above-mentioned polyester polyol is mixed with diethylene glycol, water, retardation catalyst, and surfactant to form a resin mixture, wherein the amount of diethylene glycol is controlled to be 15 wt% of the polyester polyol amount. The catalyst uses a mixture of delayed tertiary amine SPF-2 and organotin DBTDL, wherein SPF-2 / DBTDL=1 / 0.1, and the total amount is 0.8wt% of the resin mixture.

[0016] Using a low-pressure foaming machine, mix the prepolymer and the resin mixture according to the ratio of the isocyanate index to 100%, inject the reaction liquid into the mold at 65°C, mature, and release the mold after 5 minutes. A high-strength damping microporous elastomer shock-absorbing block is obtained. The relevant process parameters and the physical properties o...

Embodiment 2

[0018] This example is the same as Example 1, except that: the catalyst uses a mixture of delayed tertiary amine SPF-2 and organotin DBTDL, SPF-2 / DBTDL=1 / 0.05, and the total amount is 1.2wt% of the resin mixture. The relevant process parameters and the physical parameters of the obtained microcellular elastomer are shown in the attached table.

Embodiment 3

[0020] The rest of this example is the same as Example 1, except that: the retarded tertiary amine SPF-2 is used as a catalyst, and the total amount is 1.6wt% of the resin mixture.

[0021] The process parameters of this embodiment and the physical parameters of the obtained microcellular elastomer are shown in the attached table.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A process for preparing the millipore polyurethane elastomer used for high-strength damping elements includes proportionally mixing prepolymer at 35-60 deg.C with polyol resin, adding delay alamine as catalyst, reaction, pouring in mould at 50-70 deg.C and ageing.

Description

technical field [0001] The invention relates to a preparation method of a polyurethane microcellular elastomer, in particular to a preparation method of a polyurethane microcellular elastomer used as a damping element. Background technique [0002] Polyurethane microcellular elastomer is a chemical system formed by pouring a liquid reaction mixture into a mold cavity. The chemical raw materials used mainly include polyols, isocyanates, expansion agents, foaming agents, catalysts, additives, etc.; the preparation process mainly includes The following chemical reactions: polyol reacts with isocyanate to form urethane chain-gel reaction, isocyanate reacts with water to form urea and CO 2 - Foaming reaction. [0003] The technical improvement of polyurethane microcellular elastomers mainly focuses on two aspects: process performance improvement and material performance improvement. The improvement of process performance mainly includes: improving the fluidity of materials to f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/10C08G18/72C08G18/32C08G18/24
Inventor 杨颖韬侯瑞宏李建星聂世波
Owner 上海凯众聚氨酯有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap