Preparation method for reinforced aluminum base composite material composed by in situ ª‡-Al2O3 crystal whisker and TiC grain

An aluminum-based composite material and particle composite technology, which is applied in the field of in-situ α-Al2O3 whisker and TiC particle composite-reinforced aluminum-based composite material preparation, can solve the problems of backward development speed, complex process technology, high cost, etc. Low cost, simple process, small size effect

Inactive Publication Date: 2007-01-31
UNIV OF SCI & TECH BEIJING
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the complex technology and high cost of metal matrix composite materials, the development speed has been lagging behind that of resin matrix composite materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for reinforced aluminum base composite material composed by in situ ª‡-Al2O3 crystal whisker and TiC grain
  • Preparation method for reinforced aluminum base composite material composed by in situ ª‡-Al2O3 crystal whisker and TiC grain
  • Preparation method for reinforced aluminum base composite material composed by in situ ª‡-Al2O3 crystal whisker and TiC grain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Preparation of 0.3% α-Al 2 o 3 Whiskers (calculated. % by weight) and 3% by weight TiC / technically pure aluminum composite. Weigh Al powder, Ti powder and C powder with purity of 98%, 99.8% and 99.5% and particle size of 75 μm, 45 μm and 10 μm according to the ratio of Al:Ti:C=2:70:28, and mix them evenly . A cylindrical prefabricated block of Φ20×30mm is pressed on a 50-ton press. Put 2 kg of industrial pure aluminum into an intermediate frequency induction furnace to melt and heat to 850°C. Press 0.06 kg of prefabricated blocks into molten aluminum with a graphite bell jar and keep warm for 10 minutes. When the temperature drops to 750° C., add 0.4 wt % hexachloroethane for refining. When the melt temperature is 720°C, it is poured into a metal mold to obtain 0.3 wt% α-Al 2 o 3 Whiskers and 3 wt% TiC / commercially pure aluminum composites. Composite material σ b is 147MPa, and δ is 14%.

Embodiment 2

[0030] Preparation of 0.45% α-Al 2 o 3 Whiskers (calculated. % by weight) and 5% by weight TiC / Al-21Si-2.5Cu composite. By Al:TiO 2 : C = 1: 2.22: 0.33 ratio to take appropriate amounts of Al powder, TiO with a purity of 98%, 99.8% and 99.5% and a particle size of 75 μm, 75 μm and 10 μm respectively 2 powder and C powder, mix them well. A cylindrical prefabricated block of Φ20×30mm is pressed on a 50-ton press. Put 4 kg of Al-21Si-2.5Cu alloy into a medium-frequency induction furnace to melt and heat to 950 °C. Press a 0.20 kg prefabricated block into molten aluminum with a graphite bell jar and keep it warm for 15 minutes. Refining is added by adding 0.3% by weight of hexachloroethane to the melt. When the temperature drops to 740°C, add 0.4% hexachloroethane to the weight of the melt for refining. When the melt temperature is 730°C, it is poured into a metal mold to obtain 0.45 wt% α-Al 2 o 3 Whiskers and 5 wt% TiC / Al-21Si-2.5Cu composites. Composite material σ b ...

Embodiment 3

[0032] Preparation of 0.5% α-Al 2 o 3 Whiskers (calculated. wt%) and 5 wt% TiC / 7075 composite. By Al:TiO 2 : Ti: C=1: 2.6: 0.44: 0.44 The ratio of weighing appropriate amount of purity is respectively 98%, 99.8% and 99.5%, the particle size is respectively 75 μm, 75 μm, 45 μm and 10 μm of Al powder, TiO 2 Powder, Ti powder and C powder, mix them evenly. A cylindrical prefabricated block of Φ20×30mm is pressed on a 50-ton press. Put 4 kg of 7075 alloy into an intermediate frequency induction furnace to melt and heat to 900°C. Press a 0.20 kg prefabricated block into molten aluminum with a graphite bell jar and keep it warm for 10 minutes. Refining by adding 0.3% hexachloroethane by weight of the melt. When the melt temperature is 730°C, it is poured into a metal mold to obtain 0.5 wt% α-Al 2 o 3 Whiskers and 5 wt% TiC / 7075 composite. Composite material σ after extrusion b It is 675MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The preparation process of in-situ alpha-Al2O3 whisker and TiC grain composite reinforcing aluminum-base material features that the technological process includes two stages of preparing prefabricated block and smelting aluminum-base composite material. Three kinds of reactant may be selected, including the first kind of Al+Ti+C+O2, the second kind of Al+ C+O2+TiO2, and the third kind of Al+Ti+C+TiO2. The raw materials in the stoichiometric proportion are mixed homogeneously, pressed to form in the pressure of 25-100 MPa and smelted into the composite material. The present invention has the advantages of simultaneous alloy smelting and reinforced phase formation, shortened composite material preparing process and lowered production cost, and the composite material may be used widely in various fields.

Description

technical field [0001] The invention belongs to the field of metal matrix composite materials, and in particular provides an in-situ α-Al 2 o 3 The preparation method of whisker and TiC particle composite strengthened aluminum matrix composite material can make the smelting of matrix alloy and the generation of reinforcing phase proceed simultaneously, significantly shorten the process flow of composite material preparation, reduce the manufacturing cost of metal matrix composite material, and can be widely used in Where lightweight and high-strength composite materials are required. Background technique [0002] With the development of modern science and technology, the requirements for materials are increasing day by day. It is hoped that materials have certain special properties and excellent comprehensive properties at the same time, which makes it more and more difficult for ordinary single materials to meet the needs. Composite materials have the characteristics of b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C47/00C22C49/06C22C29/00
Inventor 杨滨王玉庆张济山
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com