Weld anti-spatter compound and its preparation method

An anti-splash agent and reagent technology, applied in the field of chemical coatings, can solve the problems of reduced sensitivity of ultrasonic detection, consumption of ultrasonic energy, damage to price probes, etc., to avoid dust damage, reduce labor intensity, and ensure reliability.

Inactive Publication Date: 2005-07-27
HUDONG ZHONGHUA SHIPBUILDINGGROUP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ultrasonic testing on such a surface will not only damage the expensive probe, but also consume a large amount of ultrasonic energy on the rough surface, which will greatly reduce the sensitivity of ultrasonic testing. These dangerous defects cannot be found, and the consequences are unimaginable
[0007] The method of not using grinding has not yet been proposed, even in some authoritative specifications such as the International Institute of Welding (IIW) and the American ASME 1998 BOILER AND PRESSURE VESSEL CODESection IX-Welding. is not possible

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] Unit: % by weight

[0025] raw material

Example 1

Example 2

Example 3

① Rutile powder

10

20

14

② Iron vanadium aluminum powder

5

10

8

③ Iron manganese phosphate

2

8

5

④Light calcium carbonate

2

8

5

⑤ Calcium nitrate

1

6

4

⑥ Zinc oxide

2

8

5

⑦Butyl cellulose

8

20

15

⑧Modified ethanol

70

20

44

[0026] The preparation method of this reagent is:

[0027] (1), weigh each raw material by above-mentioned proportioning, and each composition is mixed successively;

[0028] (2) Pour the mixture into a sand mill for grinding. The grinding particle size is required to pass through a 320-hole sieve to be considered qualified, and the finished product is obtained after siev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to chemical paint and is especially one kind reagent painted to the metal surface to prevent splash. The splash preventing agent consists of rutile powder 10-20 wt%, calcium nitrate 1-6 wt%, iron-vanadium-aluminum powder 5-10 wt%, zinc oxide 2-8 wt%, ferric manganese phosphate 2-8 wt%, butyl cellulose 8-20 wt%, light calcium carbonate 2-8 wt% and modified ethanol 20-70 wt%. Applying the splash preventing agent makes the welded plane maintain smooth and no damage, and this can omit the polishing with grinding wheel after welding and ensure the reliability of ultraviolet detection.

Description

Technical field: [0001] The invention relates to a chemical coating, and the anti-splash agent refers to a reagent used to prevent spatter on the surface of metal after welding. Background technique: [0002] Welding construction is a process widely used in modern industry. For example: marine ships, aerospace, railway transportation, petrochemical industry, boiler containers, hardware construction, etc., there are welding occasions everywhere. [0003] The metal that is partially melted during welding is generally the welding rod and the two pieces of metal that are expected to be connected, also known as the base metal. The three are melted locally, and the mixture often has external gas or non-metallic inclusions mixed in. The released gas, due to the high temperature of the arc generated by the high current, explodes due to the rapid temperature rise, and throws some liquid metal into the air with a crackling sound. They shine because of the high temperature and fly aro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K31/00B23K35/22B23K35/36
Inventor 王建喜陈时宗
Owner HUDONG ZHONGHUA SHIPBUILDINGGROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products