Corrosionproof alloy material

A corrosion-resistant alloy and component technology, applied in the field of metallurgy, can solve the problems of high production cost, complex production process, poor welding performance, etc., and achieve the effects of reducing production processes, excellent seawater resistance, and reducing production costs.

Inactive Publication Date: 2005-02-16
JIGANG INT ENG & TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing corrosion-resistant alloy materials used on ships have been proved by many aspects such as use experiments to obtain satisfactory results in terms of mechanical properties, but they still have deficiencies: due to the high content of precious elements Ni, V, Mo, etc. need to be normalized or dispatched after rolling, which makes the production process complicated, high production cost, and poor welding performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention can be implemented by following various components:

[0012] 1. 0.12% C, 0.8% Mn, 1.2% Si, 0.06% Al, 0.03% P, 0.06% Nb, 0.03% Cu, 0.06% Re, 0.02% S, and the balance iron.

[0013] 2. 0.06% C, 1.2% Mn, 0.8% Si, 0.03% Al, 0.04% P, 0.05% Nb, 0.08% Cu, 0.01% Re, 0.03% S, and the balance is iron.

[0014] 3. 0.2% C, 0.5% Mn, 0.2% Si, 0.03% Al, 0.05% P, 0.08% Nb, 0.4% Cu, 0.01% Re, 0.01% S, the balance is iron.

[0015] 4. 0.18% C, 1.3% Mn, 1.5% Si, 0.08% Al, 0.02% P, 0.04% Nb, 0.15% Cu, 0.06% Re, 0.03% S, and the balance iron.

[0016] 5. 0.1% C, 1.1% Mn, 0.9% Si, 0.05% Al, 0.03% P, 0.045% Nb, 0.25% Cu, 0.05% Re, 0.02% S, and the balance iron.

[0017] 6. 0.2% C, 1.6% Mn, 0.1% Si, 0.01% Al, 0.01% P, 0.09% Nb, 0.5% Cu, 0.06% Re, 0.01% S, the balance iron.

[0018] 7. 0.09% C, 1.6% Mn, 1.6% Si, 0.08% Al, 0.05% P, 0.04% Nb, 0.4% Cu, 0.01% Re, 0.02% S, and the balance iron.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An anticorrosion alloy material contains C (0.01-0.2%), Mn (0.3-1.6), Si (0.1-1.6), Al (0.01-0.08), P (0.01-0.06), Nb (0.01-0.09), Cu (0.01-0.5), Re (0.01-0.06), S (0.01-0.03) and Fe (rest), and is prepared from molten iron of blast furnace through pretreating, loading to another furnace, adding waste steel, fluorite and ore, deoxidizing for alloying, refining, conticasting, rolling and cooling. Its advantage are high anticorrosion performance and weldability and low cost.

Description

technical field [0001] The invention relates to the technical field of metallurgy, and relates to a corrosion-resistant alloy material. Background technique [0002] The existing corrosion-resistant alloy materials used on ships have been proved by many aspects such as use experiments to obtain satisfactory results in terms of mechanical properties, but they still have deficiencies: due to the high content of precious elements Ni, V, Mo, etc. need to be normalized or dispatched after rolling, which makes the production process complicated, high production cost, and poor welding performance. Contents of the invention [0003] The object of the present invention is to provide a corrosion-resistant alloy material, which has the advantages of good corrosion resistance, good welding performance and low production cost. [0004] In order to achieve the above object, the present invention is achieved through the following technical solutions: a corrosion-resistant alloy material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/12
Inventor 孙传水
Owner JIGANG INT ENG & TECH CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com