Oiling agent for semi-continuous spinning of viscose filament yarn as well as preparation method and application of oiling agent

A semi-continuous, spunbond technology, used in textiles and papermaking, chemical post-processing of cellulose/protein rayon, fiber processing, etc. It is not conducive to the application of high-end textiles and the use of downstream customers, so as to achieve the effect of clear and transparent appearance, prevention of adhesion and less sagging.

Pending Publication Date: 2022-04-15
SHENYANG HAOBO IND CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the silk cakes produced by domestic semi-continuous spunbond filament production enterprises with oil agents have always had the following problems, such as poor shape retention of the silk cakes, easy edge collapse when winding into a tube, and high end-break rate , the quality of the finished silk is low, which is not conducive to the use of downstream customers; the dry breaking strength and elongation of the dry breaking elongation of the inner and outer layers of the silk cake have large deviations, which is not conducive to the application in high-end textiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oiling agent for semi-continuous spinning of viscose filament yarn as well as preparation method and application of oiling agent
  • Oiling agent for semi-continuous spinning of viscose filament yarn as well as preparation method and application of oiling agent
  • Oiling agent for semi-continuous spinning of viscose filament yarn as well as preparation method and application of oiling agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Raw materials

[0022] According to the number of parts by mass, it is composed of:

[0023]

[0024] The fatty alcohol polyether is, the structural formula is C 12 h 25 O(CH 2 CH 2 O) 3 H lauryl ether.

[0025] The fatty acid polyester is, the structural formula is C 12 h 25 COO(CH 2 CH 2 O) 10 H is 5 parts of lauric acid polyester and the structural formula is C 18 h 37 COO(CH 2 CH 2 O) 9 A combination of 5 parts of polyester stearate.

[0026] The fatty amine polyether is, the structural formula is C 12 h 25 N[(CH 2 CH 2 O) 10 H] 2 dodecylamine polyether.

[0027] The oleic acid is vegetable oleic acid with an oleic acid content of 85%.

[0028] (2) Preparation method

[0029] Prepare materials according to the above-mentioned parts by mass, add No. 10 white oil, No. 15 white oil, oleic acid, fatty alcohol polyether, fatty acid polyester, and fatty amine polyether into the compounding kettle A in sequence, and after each addition, the ...

Embodiment 2

[0031] (1) Raw materials

[0032] According to the number of parts by mass, it is composed of:

[0033]

[0034]

[0035] The fatty alcohol polyether is, the structural formula is C 12 h 25 O(CH 2 CH 2 O) 5 H lauryl ether.

[0036] The fatty acid polyester is, the structural formula is C 12 h 25 COO(CH 2 CH 2 O) 10 H is 5 parts of lauric acid polyester and the structural formula is C 18 h 37 COO(CH 2 CH 2 O) 6 A combination of 7 parts of polyester stearate.

[0037] The fatty amine polyether is, the structural formula is C 12 h 25 N[(CH 2 CH 2 O) 10 H] 2 dodecylamine polyether.

[0038] The oleic acid is vegetable oleic acid with an oleic acid content of 85%.

[0039] (2) Preparation method

[0040] Prepare materials according to the above-mentioned mass parts, add No. 10 white oil, No. 15 white oil, oleic acid, fatty alcohol polyether, fatty acid polyester, and fatty amine polyether into the compounding kettle A in sequence, and after each feedin...

Embodiment 3

[0042] (1) Raw materials

[0043]

[0044] The fatty alcohol polyether is, the structural formula is C 18 h 37 O(CH 2 CH 2 O) 10 H's stearyl ether.

[0045] The fatty acid polyester is, the structural formula is C 12 h 25 COO(CH 2 CH 2 O) 15H is 4 parts of lauric polyester and the structural formula is C 18 h 37 COO(CH 2 CH 2 O) 10 A combination of 5 parts of oleic acid polyester.

[0046] The fatty amine polyether is, the structural formula is C 18 h 37 N[(CH 2 CH 2 O) 12 H] 2 octadecylamine polyether.

[0047] The oleic acid is vegetable oleic acid with an oleic acid content of 85%.

[0048] (2) Preparation method

[0049] Prepare materials according to the above-mentioned parts by mass, add No. 10 white oil, No. 15 white oil, glyceryl monostearate, oleic acid, fatty alcohol polyether, fatty acid polyester, and fatty amine polyether into the compounding kettle in sequence In A, stir at room temperature for 10 minutes after each addition; add deioni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an oiling agent for semi-continuous spinning of viscose filaments as well as a preparation method and application of the oiling agent. The oiling agent is prepared from the following components in parts by mass: 60-90 parts of a lubricant, 10-20 parts of an emulsifier, 1-5 parts of an antistatic agent, 1-10 parts of a shape retention agent, 1-5 parts of oleic acid and 5-10 parts of deionized water. The oil agent prepared by the invention can form a stable emulsion with water, so that a spinning cake can be stiff and elastic and has proper shape retention, the dry strength and dry stretching deviation of inner and outer layer fibers of the spinning cake is smaller, and the edge collapse is less when the spinning cake is wound into a barrel, thereby reducing the end breakage rate of the spinning cake and improving the quality of the fibers.

Description

technical field [0001] The invention relates to the field of chemical oil agents, in particular to an oil agent for semi-continuous spun viscose filaments. Background technique [0002] Semi-continuous spun viscose filaments use cotton pulp or wood pulp as raw materials. After a series of chemical reactions and physical processes, viscose liquid is first prepared, and then silk cakes are made from viscose liquid on a semi-continuous spinning machine. Then it is made through a series of post-processing procedures. [0003] The oil agent is used in the oiling process in the post-processing process, and it mainly plays the role of lubrication, antistatic, cluster cohesion and so on. At present, the silk cakes produced by domestic semi-continuous spunbond filament production enterprises with oil agents have always had the following problems, such as poor shape retention of the silk cakes, easy edge collapse when winding into a tube, and high end-break rate , The quality of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/02D06M15/53D06M15/333D06M13/17D06M13/224D06M13/203D06M15/285D01F11/02D06M101/06
Inventor 梁聪徐莫临刘洋黄韬
Owner SHENYANG HAOBO IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com