1*19 structure steel wire rope and preparation method thereof

A steel wire rope and steel wire technology, which is applied in the field of steel wire rope, can solve problems such as deep reduction and failure to meet customer needs, and achieve the effect of improving ellipticity

Pending Publication Date: 2022-03-29
泰州兴达特种钢丝绳有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, customers in the market have higher and higher requirements for the ellipticity of the 1×19 structural steel wire rope. However, the 1×19 structural steel wire rope is a “cc” type steel wire rope. In order to control its looseness, a straightener is simply used as a debugging method in conventional production. , the reduction is very deep, and the ellipticity of the finished steel wire rope reaches more than 4.4% of the thickness of the steel wire rope, which cannot meet customer needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 1*19 structure steel wire rope and preparation method thereof
  • 1*19 structure steel wire rope and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a method for preparing a 1×19 structural steel wire rope, and the specific steps are as follows:

[0025] Step 1: select a smooth steel wire with a diameter of 1.60mm, and draw the 1.60mm smooth steel wire through a hot-dip galvanizing process to preferred monofilaments with a diameter of 0.35mm and 0.325mm.

[0026] Among them, the composition and weight percentage of the steel monofilament are: the content of carbon is 0.3% to 1.15%, the content of manganese is 0.1% to 1.1%, the content of silicon is 0.1% to 0.9%, and the content of sulfur and phosphorus does not exceed 0.15%, the chromium content is 0.2% to 0.4%, the copper content is 0.2%, and the others are iron.

[0027] Step 2, select a monofilament with a diameter of 0.35mm as the first steel wire monofilament 1, select a monofilament with a diameter of 0.325mm as the second steel monofilament 2; combine 1 first steel monofilament 1 with 6 second steel wires The monofilament 2 is placed...

Embodiment 2

[0037] This implementation discloses a 1×19 structural steel wire rope, such as figure 1 As shown, it is prepared by using the preparation method of the 1×19 structural steel wire rope in Example 1.

[0038] Specifically, the 1×19 structural steel wire rope includes 1 first steel monofilament 1 , 6 second steel monofilaments 2 and 12 third steel monofilaments 3 .

[0039] Among them, 6 second steel monofilaments 2 are evenly distributed on the peripheral side of the first steel monofilament 1 to form a core strand structural strand; 12 third steel monofilaments 3 are evenly distributed on the periphery of the core structural strand side.

[0040] The experimental data shows that the 1×19-Φ1.59mm galvanized steel wire rope prepared in Example 1 has an ellipticity of 0.04 when the thickness of the steel wire rope is 1.58-1.62, and the ellipticity of the steel wire rope can be effectively controlled at 2.5% of the thickness of the steel wire rope within.

[0041] In the descri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a 1 * 19 structure steel wire rope and a preparation method thereof, and the preparation method comprises the following steps: twisting and stranding one first steel wire monofilament and six second steel wire monofilaments into a core strand structure plied yarn; using a stranding machine to twist and strand the core strand structure plied yarns and 12 third steel wire monofilaments into a 1 * 19 structure steel wire rope; wherein the ratio of the over-twisting rotating speed of the stranding machine to the rotating speed of the machine tool is not lower than 0.2 and not higher than 0.3; a steel wire rope of a 1 * 19 structure penetrates through a plurality of straighteners, and the adjacent straighteners are vertically placed. By strictly controlling the ratio of the over-twisting rotating speed of the stranding machine to the rotating speed of the machine tool and reasonably using the straightener in a matched mode, the ovality of the galvanized steel wire rope of the 1 * 19 structure is improved, and the ovality of the steel wire rope can be effectively controlled within 2.5% of the thickness of the steel wire rope.

Description

technical field [0001] The invention relates to a 1×19 structural steel wire rope and a preparation method thereof, belonging to the technical field of steel wire ropes. Background technique [0002] At present, customers in the market have higher and higher requirements for the ellipticity of the 1×19 structural steel wire rope. However, the 1×19 structural steel wire rope is a “cc” type steel wire rope. In order to control its looseness, a straightener is simply used as a debugging method in conventional production. , The reduction is very deep, and the ellipticity of the finished steel wire rope reaches more than 4.4% of the thickness of the steel wire rope, which cannot meet customer needs. [0003] The information disclosed in this Background section is only for enhancement of understanding of the general background of the present invention and should not be taken as an acknowledgment or any form of suggestion that the information constitutes the prior art that is alrea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D07B1/06D07B3/00D07B7/02
CPCD07B1/0693D07B3/00D07B7/02D07B2205/3025D07B2201/102D07B2201/2006D07B2201/2009
Inventor 兴成尧王彪陈彬陈金彬崔万生夏广宇
Owner 泰州兴达特种钢丝绳有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com