Method for making optical fiber preform having ultimately low PMD through improvement of ovality

An optical fiber preform, preform technology, applied in manufacturing tools, glass manufacturing equipment, optics, etc., can solve problems such as volatilization limitation, and achieve the effect of improving ellipticity and improving PMD

Inactive Publication Date: 2006-10-25
LG CABLE INC
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] Although the inner diameter of the hollow preform is minimized after the shrinkage process, the inner diameter increases during the etching process due to internal water pressure, so minimizing or preventing the GeO 2 volatility is still limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making optical fiber preform having ultimately low PMD through improvement of ovality
  • Method for making optical fiber preform having ultimately low PMD through improvement of ovality
  • Method for making optical fiber preform having ultimately low PMD through improvement of ovality

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

[0036] first, figure 2 It is a bottom sectional view for explaining a process of forming a flame hydrolysis gas-generated deposit on the inner wall of a hollow preform as a pretreatment for shrinkage according to the present invention. refer to figure 2 , when a tube 10 made of, for example, quartz glass is rotated in the circumferential direction at a constant speed, the flame hydrolysis produces a gas 11 such as SiCl 4 、GeCl 4 and POCl 3Injected into the tubing 10 together with oxygen. Then, by moving the torch 13 having a semi-cylindrical shape in the longitudinal direction of the tube 10 , the tube 10 is heated so that a transparent glass layer is deposited on the inner wall of the tube 10 . At this point, the concentration of the flame hydrolysis gas 11 is controlled to adjust the refractive index of the deposited layer while...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface temperatureaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a method of manufacturing an optical fiber preform finally having low PMD (Polarization Mode Dispersion) through improvement of ellipticity. The method has several shrinking steps for shrinking an optical fiber preform having a cladding / core deposition layer formed in a preform tube, wherein the shrinking rate in each shrinking step is 0.01- 0.06mm / min. By using this method, the ovality and PMD of the optical fiber preform can be improved.

Description

technical field [0001] The present invention relates to a kind of method that finally has the optical fiber preform rod (perform) of low PMD (polarization mode dispersion) by the improvement of optical fiber ellipticity, and particularly relates to a kind of shrinking rod (collapse) rate that is relevant to temperature by optimizing, blowtorch The method of improving the ellipticity and PMD of the optical fiber by the moving speed of the moving speed and the difference between the internal pressure and the external pressure of the hollow preform during the shrinkage process. [0002] Furthermore, the present invention relates to a method for improving PMD by keeping the inner diameter of the hollow preform at a fixed value in the range of 2 mm to 4 mm before closing the hollow preform through several shrinkage treatments, and then sealing together using etching Hollow preforms to minimize dips. Background technique [0003] In general, an optical fiber widely used as a wave...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B6/00C03B37/018
CPCC03B37/01861C03B37/01869Y02P40/57
Inventor 姜秉润文俊皓李奉勋朴耿巡金正珉
Owner LG CABLE INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com