Application of cu/au/pt-mofs and their visual test strips in the detection of h2o2, cys or glucose

A technology of H2O2 and test paper, which is applied in the field of nanomaterials and its analysis applications, can solve the problems of complex detection process, long detection time and low detection sensitivity, and achieve the effect of high sensitivity determination, simple operation and strong peroxidase activity

Active Publication Date: 2022-05-27
CENT SOUTH UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these traditional analytical techniques have disadvantages such as low detection sensitivity, complex detection process and long detection time. At present, a convenient, sensitive and efficient new detection technology is urgently needed.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of cu/au/pt-mofs and their visual test strips in the detection of h2o2, cys or glucose
  • Application of cu/au/pt-mofs and their visual test strips in the detection of h2o2, cys or glucose
  • Application of cu/au/pt-mofs and their visual test strips in the detection of h2o2, cys or glucose

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Detection of H based on Cu / Au / Pt-MOFs composites 2 O 2 The method, the Cu / Au / Pt-MOFs composite materials are composed of Cu-TCPP (Fe) and Cu / Au / Pt NPs grown in situ on their surfaces, the mass ratio of Cu-TCPP (Fe) and Cu / Au / Pt polymetallic nanoparticles is 1:1.57, and the mass ratio of Cu / Au / Pt polymetallic nanoparticles is 1:5.78:4.52.

[0044] First, the preparation method of Cu / Au / Pt NPs-MOFs, the specific steps are as follows:

[0045] Divide 0.012 g Cu(NO 3 ) 2 ·3H 2O (0.01 mmol), 50 μL trifluoroacetic acid (1.0 M), and 50.0 mg polyvinylpyrrolidone dissolved in a mixture of 60 mL DMF and ethanol (V:V=3:1). Dissolve 0.022 g TCPP(Fe) (0.005 mmol) in a 20 mL DMF and ethanol (V:V=3:1) mixed solution dropwise into the above mixed solution under stirring. Then, the solution was sonicated for 10 min, placed in a reactor and heated to 80 °C and maintained for 15 h. The resulting dark brown product was washed twice with ethanol and collected by centrifugation at 8000 rpm, 25 °...

Embodiment 2

[0054] A method based on Cu / Au / Pt-MOFs composite material detection Cys, Cu / Au / Pt-MOFs composite material is prepared by the method of Example 1, the operating steps are as follows:

[0055] Add 20 μL of TMB (6 mmol / L), 10 μL of 10 μL of NOAc buffered solution (0.01 M, pH 5.5) to 135 μL of NaOAc buffered solution 2 O 2 (20 mmol / L), 25 μL Cu / Au / Pt NPs-MOFs, and 10 μL of Cys solutions of different concentrations were measured using an UV-Visible spectrophotometer after 15 min of the reaction at room temperature.

[0056] as Figure 6 The UV-Vis absorption spectrum shown shows that the absorbance decreases with the increase of Cys concentration in the range of 0-700 μM, and in the range of 0 μM to 300 μM, the absorbance at 652 nm is linearly related to the Cys concentration, and the regression equation is Δ = -0.00592 C + 1.6884（R 2 = 0.9068）（ Figure 7 ）。 Based on the results of 11 blank samples, a detection limit of 0.51 μM was calculated using the formula LOD = 3S / K (S is th...

Embodiment 3

[0058] A method for detecting glucose based on Cu / Au / Pt-MOFs composite material, Cu / Au / Pt-MOFs composite material is prepared by the method of Example 1, the operating steps are as follows:

[0059] First, 10 μL of 8 mg / mL of glucose oxidase solution was added to 290 μL of glucose solution of different concentrations and mixed well, incubated in a metal bath for 15 min. Then, take 10 μL of the above incubation solution and add 135 μL to NaOAc buffer solution containing 20 μLTMB (6 mmol / L), 25 μL Cu / Au / Pt NPs-MOFs (0.01 M, pH 5.5), after letting the reaction sit for 15 min at room temperature, measure the absorbance of the reaction system at 652 nm using an ultraviolet-visible spectrophotometer.

[0060] from Figure 8 It can be seen that the absorbance at 652 nm increases with the increase of glucose concentration, and in the range of 0 μM to 800 μ M, the absorbance at 652 nm is linearly related to the glucose concentration, and the regression equation is ΔA = 0.00396 C + 0.1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Cu / Au / Pt-MOFs composite material in the detection of H 2 O 2 , Cys or glucose, the Cu / Au / Pt-MOFs composite mainly consists of metal-organic framework composites and Cu / Au / Pt multi-metal nanoparticles grown in situ on its surface. The present invention detects H 2 O 2 , Cys or glucose method, the H 2 O 2 Quantitative detection of , Cys and glucose, simple operation, fast, low cost and high sensitivity. The invention also discloses a visual test paper based on Cu / Au / Pt-MOFs composite material. The sample to be tested can be directly dropped on the test paper to react, and then the color information (RGB) of the test paper can be read by intelligent software. Only a small amount of sample is needed. It can quickly, conveniently and accurately quantify the target substance in the sample to be tested.

Description

Technical field [0001] The present invention belongs to the field of nanomaterials and analytical applications thereof, specifically relates to a cu / Au / Pt NPs - metal-organic framework (Cu / Au / Pt- MOFs) composite material detection H 2 O 2 , Cys or glucose methods and visualization test strips. Background [0002] Hydrogen peroxide (H 2 O 2 ), also known as hydrogen peroxide, is a strong oxidant, with oxidation, antiseptic, bleaching, disinfection and other effects, often as preservatives, bleaching agents and fungicides are widely used in food processing, industrial bleaching, surgical disinfection and other fields. Exposure to excess H 2 O 2 It will cause irritation and corrosion to the human body, damage the muscle cells; H 2 O 2 Heavy entry into the bloodstream can also lead to arterial or venous gas embolism. China's food safety related standards clearly prohibit the detection of hydrogen peroxide residues in food. In addition, H 2 O 2 It is also an important part of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/78G01N21/31
CPCG01N21/78G01N21/314G01N2021/7759G01N2021/3148
Inventor 丁萍龚芳洁伍翩开天瀚陈翠梅王丹琪黄瑞雪张竞文
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap