Printing ink, and preparation method and application thereof

A technology of ink and mass, applied in the field of ink to achieve the effect of reducing damage, good working performance, and improving viscosity on the high side

Inactive Publication Date: 2021-12-31
SUZHOU ZHONGYA INK
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the development of modern society, the requirements for environmental protection are getting higher and higher; therefore, in the process of realizing the present application, the inventors found that the environmental protection of inks in related technologies still needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0043] This preparation example discloses a preparation method of a microcapsule phase change material (MCPCM), including:

[0044] S01, get n-tetradecane 200kg and methyl methacrylate 100kg and mix both; Add styrene maleic anhydride copolymer 12.5kg to the mixture of n-tetradecane and methyl methacrylate and mix evenly; Under ultrasonic vibration (frequency 60kHz), add 600 kg of water to the mixture of the above three (n-tetradecane, methyl methacrylate and styrene maleic anhydride copolymer), and control the addition time for 30 minutes; after that, ultrasonic vibration 2h, water is mixed with n-tetradecane, methyl methacrylate and styrene maleic anhydride copolymer to obtain an emulsion;

[0045] Among them, n-tetradecane is a low-temperature solid-liquid phase change material, and is used as a core material of the microcapsule; methyl methacrylate is a wall material monomer of the microcapsule; and styrene-maleic anhydride copolymer is used as an emulsifier.

[0046] It s...

preparation example 2

[0051] This preparation example discloses a preparation method of a microcapsule phase change material (MCPCM), including:

[0052] S01, get n-tetradecane 250kg and methyl methacrylate 100kg and both mix homogeneously; Add styrene maleic anhydride copolymer 15kg and mix homogeneously in the mixture of n-tetradecane and methyl methacrylate; Under ultrasonic vibration (frequency 60kHz), add 700kg of water to the mixture of the above three, and control the addition time to 40min; then ultrasonically vibrate for 2.5h to make water and n-tetradecane, methyl methacrylate and styrene maleic acid The anhydride copolymers are mixed to obtain an emulsion.

[0053] S02. Add 30kg of allyl methacrylate (AMA) and 8kg of azobisisobutyronitrile (ABIN) to the emulsion; under nitrogen protection, stir the above emulsion at 55°C for 30min, and control the stirring speed to 1000rpm; then the temperature was raised to 87°C, and stirred at a stirring speed of 400rpm for 2h.

[0054] S03. Vacuum s...

preparation example 3

[0056] This preparation example discloses a preparation method of a microcapsule phase change material (MCPCM), including:

[0057] S01, get n-tetradecane 150kg and methyl methacrylate 100kg and both mix homogeneously; Add styrene maleic anhydride copolymer 10kg and mix homogeneously in the mixture of n-tetradecane and methyl methacrylate; Under ultrasonic vibration (frequency 60kHz), add 500 kg of water to the mixture of the above three, and control the addition time to 25 minutes; after that, ultrasonic vibration for 2 hours to make water and n-tetradecane, methyl methacrylate and styrene maleic anhydride The copolymers are mixed to obtain an emulsion.

[0058] S02. Add 20kg of allyl methacrylate (AMA) and 7kg of azobisisobutyronitrile (ABIN) to the emulsion; under nitrogen protection, stir the above emulsion at 60°C for 20min, and control the stirring speed to 1200rpm; then the temperature was raised to 90°C, and stirred at a stirring speed of 300rpm for 4h.

[0059] S03....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of printing ink, and particularly discloses a printing ink, and a preparation method and application thereof. The printing ink is prepared from, by weight, 100 parts of polyurethane resin, 106 to 120 parts of pigment, 75 to 85 parts of methyl 3-methoxypropionate, 135 to 145 parts of ethyl 3-ethoxypropionate, 25 to 35 parts of n-propyl acetate, 85 to 95 parts of ethanol, 6 to 12 parts of n-propyl alcohol and 7 to 10 parts of a first dispersing agent. The preparation method of the printing ink comprises the following steps: weighing the above raw materials, dissolving the resin, mixing for the first time, grinding, mixing for the second time and the like. The printing ink is printed on the surface of a packaging bag. By using the organic solvent with good environmental protection property, the damage of the organic solvent in the ink to a human body can be reduced, and the pollution of the organic solvent to the environment is also reduced, so that the environmental protection property of the ink is improved. Meanwhile, the printing ink disclosed by the invention has good adhesive force, surface dryness, normal-temperature viscosity and color, so that the ink has good working performance.

Description

technical field [0001] The application relates to the field of ink, more specifically, it relates to an ink and its preparation method and application. Background technique [0002] Ink is an important material for printing, which is a viscous colloidal fluid mainly composed of binders, pigments, solvents and additives. Among them, the binder acts as a medium for dispersing the pigment, and after ink printing, the binder can form a film layer with a certain strength to protect the pigment; the binder is usually a resin, such as polyurethane resin, polyacrylic resin, epoxy resin, etc. . Pigments are color-developing components that can impart various colors to inks. The solvent is the carrier of each component of the ink, including organic solvents and water; according to different solvents, inks can be divided into oil-based inks and water-based inks. Auxiliaries include leveling agents, matting agents, wear-resistant agents, etc., which can give ink more performance. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/033C09D11/03C09D11/102
CPCC09D11/033C09D11/03C09D11/102
Inventor 张东明周忠伟胡春玲汪思兵
Owner SUZHOU ZHONGYA INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com