High-strength and high-toughness automobile suspension spring steel and production method thereof

An automobile suspension, high strength and toughness technology, applied in the field of automobile suspension spring steel, can solve the problems of steel wire strength reduction, failure to meet the technical standard requirements of 2000MPa steel wire, sacrifice strength, etc., and achieve low decarburization, excellent fatigue performance, low cost effect

Active Publication Date: 2021-12-07
ANGANG STEEL CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above method will sacrifice the strength, which will eventually lead to a decrease in the strength of the steel wire, so that it cannot meet the technical standard requirements of 2000MPa steel wire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and high-toughness automobile suspension spring steel and production method thereof
  • High-strength and high-toughness automobile suspension spring steel and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The invention discloses a high-strength and toughness automobile suspension spring steel and a production method thereof. Those skilled in the art can refer to the content of this article to appropriately improve the process parameters to achieve. In particular, it should be pointed out that all similar replacements and modifications are obvious to those skilled in the art, and they are all considered to be included in the present invention. The method and application of the present invention have been described through preferred embodiments, and the relevant personnel can obviously make changes or appropriate changes and combinations to the method and application described herein without departing from the content, spirit and scope of the present invention to realize and Apply the technology of the present invention.

[0030] A kind of production method of high-strength toughness automobile suspension spring steel specifically comprises the following steps:

[0031] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of automobile suspension spring steel, in particular to high-strength and high-toughness automobile suspension spring steel and a production method thereof. The steel comprises the following chemical components in percentage by weight: 0.5%-0.6% of C, 1.2%-1.6% of Si, 0.60%-0.9% of Mn, 0.6%-0.9% of Cr, 0.01%-0.3% of V, less than or equal to 0.015% of P, less than or equal to 0.015% of S, less than or equal to 0.0015% of Ti, 0.0005%-0.0050% of total aluminum, less than or equal to 0.0025% of total oxygen, less than or equal to 0.0050% of N, less than 0.1% of inevitable impurities and the balance of iron. Through brand new low-alloy-content and low-cost chemical component design and in cooperation with appropriate converter smelting, refining, continuous casting, continuous rolling, wire rod rolling, drawing, heat treatment and other processes, the technical problems that the 2000MPa-grade automobile suspension spring steel wire is excessive in strength and insufficient in plasticity and toughness are solved. The tensile strength of the steel can reach 2000 MPa level and 2100 MPa level respectively, and the area reduction rate is larger than or equal to 45%. The spring steel not only has the excellent mechanical properties of high toughness, but also has the advantages of low cost, low decarburization, high surface quality, high purity and excellent fatigue property.

Description

technical field [0001] The invention relates to the technical field of automobile suspension spring steel, in particular to a high-strength and toughness automobile suspension spring steel and a production method thereof. Background technique [0002] 55SiCr spring steel is a Si-Cr series spring steel, mainly used to make automobile suspension springs. It is currently the most widely used steel type for making automobile suspension springs. This steel has excellent fatigue performance and anti-elasticity loss performance . [0003] At present, in the industrial production process, the tensile strength of the oil-quenched and tempered steel wire made of the steel wire rod after drawing and heat treatment can reach 1800MPa (1750MPa~1850MPa), 1900MPa (1850MPa) depending on the production process. ~1950MPa) and 2000MPa grade (1950MPa~2050MPa). [0004] However, in the actual production process of 2000MPa oil-quenched and tempered suspension spring steel wire, if there is a cer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/34C22C38/24C22C38/06C22C33/06C21D8/06C21D1/18B21C37/04
CPCC22C38/02C22C38/04C22C38/34C22C38/24C22C38/06C22C33/06C21D8/065C21D1/18B21C37/047Y02P10/20
Inventor 张博安绘竹郭大勇高航王秉喜马立国潘阳
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products