Contrast enhancer

A technology of contrast enhancer and volatile solvent, applied in the direction of coating, material magnetic variable, etc., can solve the problems of reducing flaw detection sensitivity, difficulty in cleaning, pollution, etc., and achieve the effect of improving flaw detection sensitivity, easy cleaning, and uniform leveling

Pending Publication Date: 2021-11-23
WUJIANG HYPERD NDT MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, existing contrast enhancers
The formed film is thicker, and it is easy to form processing at tiny defects, thereby reducing the sensitivity of flaw detection, and it is difficult to remove, which has certain pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A contrast enhancer comprising the following components by weight percentage:

[0030] The mixture of titanium dioxide, magnesium oxide and zinc oxide powder, 15 parts, the weight ratio of titanium dioxide, magnesium oxide and zinc oxide powder is 1:1:1.

[0031] 3 parts fluorescent whitening agent

[0032] Volatile solvent ethanol, dioctyl phthalate and n-pentane 75 parts

[0033] 1 part of the mixture of ethyl cellulose ether and rosin resin, the weight ratio of ethyl cellulose ether and rosin resin is 1:1.

[0034] 30 parts of T-306 environmental solvent.

Embodiment 2

[0036] A contrast enhancer comprising the following components by weight percentage:

[0037] The mixture of titanium dioxide, magnesium oxide and zinc oxide powder, 20 parts, the weight ratio of titanium dioxide, magnesium oxide and zinc oxide powder is 1:1:1.

[0038] Fluorescent whitening agent 5 parts

[0039] Volatile solvent ethanol, dioctyl phthalate and n-pentane 78 parts

[0040] The mixture of ethyl cellulose ether and rosin resin is 2 parts, and the weight ratio of ethyl cellulose ether and rosin resin is 1:1.

[0041] 40 parts of T-306 environmental solvent.

[0042] The preparation method of above-mentioned contrast enhancing agent, comprises the steps:

[0043] Step 1. Mix titanium dioxide, magnesium oxide, zinc oxide powder, fluorescent whitening agent, volatile solvent, ethyl cellulose ether, rosin resin, and T-306 environment-friendly solvent in proportion to obtain mixture A;

[0044] Step 2. Put the mixture A obtained in step 1 into a grinder for grindin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a contrast enhancer which comprises the following components in percentage by weight: 15-20 parts of a mixture of titanium dioxide, magnesium oxide and zinc oxide powder, 3-5 parts of a fluorescent whitening agent, 75-80 parts of a volatile solvent, 0.5-2 parts of a mixture of ethyl cellulose ether and rosin resin, and 30-50 parts of a T-306 environment-friendly solvent. The contrast enhancer provided by the invention is used for magnetic powder inspection, can be used for enhancing the contrast ratio when a workpiece cannot obtain a good background due to corrosion, is thin and uniform in spraying, is dry after being sprayed, can effectively provide a good background contrast ratio, is pure white in color and luster and thin in formed film, has the thickness of less than 1 micron, does not affect the adsorption force of a leakage magnetic field, is uniform in leveling and strong in seepage adhesion force, cannot form overhead so as to improve flaw detection sensitivity, is easy to clear, and cannot pollute the environment.

Description

technical field [0001] The invention relates to a contrast enhancing agent used for magnetic particle flaw detection. Background technique [0002] Magnetic particle testing is one of the five conventional non-destructive testing (penetrant testing, magnetic particle testing, radiographic testing, ultrasonic testing, eddy current testing) methods. The principle of magnetic particle testing is that after the ferromagnetic material and the workpiece are magnetized, due to the existence of discontinuity, the magnetic field lines on the surface and near the surface of the workpiece will be locally distorted to generate a leakage magnetic field, which will absorb the magnetic powder applied on the surface of the workpiece and form it under suitable light. A visual indication showing the location, shape and size of a discontinuity. It has the following advantages: intuitively display the position, shape, size, and severity of defects; high detection sensitivity, the width can rea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N27/84C09D1/00C09D7/65C09D7/40
CPCG01N27/84C09D1/00C09D7/65C09D7/40
Inventor 沈明奎沈耀程
Owner WUJIANG HYPERD NDT MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com